Process for producing grain oriented electrical silicon steel sheet
Assignee: Nippon Steel Corp
•
Filing: 1979-06-11
•
Granted: 1981-05-19
•
Expires: 1999-06-11
Abstract
Abstract An electrical silicon steel sheet composed of secondary or tertiary recrystallized grains oriented in one or two directions, is produced by a process comprising a decarburization annealing operation in an oxidation atmosphere in which a ratio of PH2O/PH2 wherein PH2O represents a partial pressure of water vapor in said oxidation atmosphere and PH2 represents a partial pressure of hydrogen in said oxidation atmosphere, is adjusted to a value of 0.15 or more in an initial stage of said decarburization annealing operation and, then, to a value smaller than that in said initial stage in a final stage of said decarburization annealing operation.
Inventors
- 👤 Kenzo Iwayama
- 👤 Osamu Tanaka
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 20:24
CPC Classifications
C; C21; C21D; C21D3/00; C21D3/02; C21D3/04; C21D8/00; C21D8/12; C21D8/1244; C21D8/1255; C21D9/00; C21D9/46; C21D8/1272
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
158 words
A process for producing a grain oriented electrical silicon steel sheet comprising: subjecting a cold-rolled silicon steel sheet, after it has been cold-rolled, to a continuous two-stage decarburization annealing procedure in an oxidation atmosphere, in an initial stage of which procedure a ratio of PH 2 O/PH 2 , wherein PH 2 O represents the partial pressure of water vapor in said oxidation atmosphere and PH 2 represents the partial pressure of hydrogen in said oxidation atmosphere, is adjusted to a value of 0.15 or more, and a decarburization annealing temperature is adjusted to a value of from 750° through 880° C. and; in a final stage of said procedure the ratio of PH 2 O/PH 2 is adjusted to a value smaller than that in said initial stage, and said decarburization annealing temperature is adjusted to a value of from 750° through 1200° C., the total decarburization annealing time for both stages being 200 seconds or less.
Claim 2
Dependent Claim
158 words
A process for producing a grain oriented electrical silicon steel sheet comprising: subjecting a cold-rolled silicon steel sheet, after it has been cold-rolled, to a continuous two-stage decarburization annealing procedure in an oxidation atmosphere, in an initial stage of which procedure a ratio of PH 2 O/PH 2 , wherein PH 2 O represents the partial pressure of water vapor in said oxidation atmosphere and PH 2 represents the partial pressure of hydrogen in said oxidation atmosphere, is adjusted to a value of 0.15 or more, and a decarburization annealing temperature is adjusted to a value of from 750° through 880° C. and; in a final stage of said procedure the ratio of PH 2 O/PH 2 is adjusted to a value smaller than that in said initial stage, and said decarburization annealing temperature is adjusted to a value of from 750° through 1200° C., the total decarburization annealing time for both stages being 200 seconds or less.
Claim 3
Dependent Claim
31 words
A process as claimed in claim 1, wherein said ratio of PH 2 O/PH 2 in said final stage of said decarburization annealing operation has a value of 0.75 or less.
Claim 4
Dependent Claim
40 words
A process as claimed in claim 1, wherein the proportion of the period of said final stage of said decarburization annealing operation to the entire period of said decarburization annealing operation is in a range of from 1/10 to 9/10.
Claim 5
Dependent Claim
34 words
A process as claimed in claim 1 or 2, wherein said ratio PH 2 O/PH 2 in said final stage of said decarburization annealing operation is in a range of from 0.15 to 0.75.
Claim 6
Dependent Claim
22 words
A process as in claim 1 wherein the total decarburization annealing time for the two stages ranges from 120 to 200 seconds.
Claim 7
Dependent Claim
36 words
A process as claimed in claim 1, wherein said ratio of PH 2 O/PH 2 is in a range of from 0.15 through 0.75 in the initial stage and less than 0.15 in the final stage.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-05-18 | 1984-11-17 | 1985-05-19 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-05-18 | 1988-11-17 | 1989-05-19 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-05-18 | 1992-11-17 | 1993-05-19 | $7700.00 | Window Closed / Lapsed |