Assignee: Kolene Corp
•
Filing: 1980-07-01
•
Granted: 1981-05-19
•
Expires: 2000-07-01
Abstract
Abstract A process for case hardening steel is described. A fused bath of inert salt is maintained which bath is comprised of alkali or alkali earth halides, and alkali, or alkaline earth oxides or carbonates. To this fused bath is added urea, dicyanodiamide or pyrolysis/condensation products of urea or dicyanodiamide. This will form active ions containing carbon and/or nitrogen, and either the nitrogen and/or carbon will diffuse into the surface of a steel piece suspended in the bath to form either a nitride, carbonitride or carburized case depending upon the temperature of the bath, which is maintained between above 540° C. and about 950° C.
Inventors
- 👤 Thomas M. Jakubowski
- 👤 William G. Wood
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 15:49
CPC Classifications
C; C23; C23C; C23C8/00; C23C8/40; C23C8/42; C23C8/48; C23C8/50; C23C8/44; C23C8/46; C23C8/52; C23C8/54; C23C8/56
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
183 words
A process for forming a hardened case on a ferrous metal comprising the steps of maintaining, at a temperature from about 540° C. (1000° F.) to about 950° C. (1750° ), a fused chemical salt bath consisting essentially of a first material selected from the group consisting of alkali halides, or alkaline earth halides, or mixtures thereof; and a second material selected from the group consisting of alkali oxides, alkaline earth oxides, alkali carbonates, alkaline earth carbonates, or mixtures thereof; said bath being maintained free of cyanide and cyanate salts, suspending the metal workpiece to be case hardened in said bath; thereafter adding to said bath a third material or combination of materials selected from the group consisting of urea, dicyanodiamide, and any of the pyrolysis/condensation products of urea or dicyanodiamide; or combinations thereof at a rate which will not produce cyanide or cyanate salts whereby to form in situ active case producing ingredients to thereby produce a case on said workpiece, removing said workpiece, and thereafter maintaining said bath free of cyanide and cyanate salts, with the original first and second material.
Claim 2
Dependent Claim
183 words
A process for forming a hardened case on a ferrous metal comprising the steps of maintaining, at a temperature from about 540° C. (1000° F.) to about 950° C. (1750° ), a fused chemical salt bath consisting essentially of a first material selected from the group consisting of alkali halides, or alkaline earth halides, or mixtures thereof; and a second material selected from the group consisting of alkali oxides, alkaline earth oxides, alkali carbonates, alkaline earth carbonates, or mixtures thereof; said bath being maintained free of cyanide and cyanate salts, suspending the metal workpiece to be case hardened in said bath; thereafter adding to said bath a third material or combination of materials selected from the group consisting of urea, dicyanodiamide, and any of the pyrolysis/condensation products of urea or dicyanodiamide; or combinations thereof at a rate which will not produce cyanide or cyanate salts whereby to form in situ active case producing ingredients to thereby produce a case on said workpiece, removing said workpiece, and thereafter maintaining said bath free of cyanide and cyanate salts, with the original first and second material.
Claim 3
Dependent Claim
30 words
The invention as defined in claim 1 wherein the temperature of the bath is maintained between about 540° C. and about 590° C., whereby to form an essentially nitride case.
Claim 4
Dependent Claim
29 words
The invention as defined in claim 1 wherein the temperature of the bath is maintained between about 590° C. and about 815° C., whereby to form a carbonitride case.
Claim 5
Dependent Claim
30 words
The invention as defined in claim 1 wherein the temperature of the bath is maintained between about 815° C. and about 950° C., whereby to form an essentially carburized case.
Claim 6
Dependent Claim
28 words
The invention as defined in claim 1 wherein the first material is a mixture of CaCl 2 and NaCl, and wherein said second material is CaCO 3 .
Claim 7
Dependent Claim
40 words
The invention as defined in claim 5 wherein said first material includes about 64-68 percent by weight CaCl 2 , about 30-32 percent by weight NaCl, and wherein said second material includes about 1-5 percent by weight CaCO 3 .
Claim 8
Dependent Claim
13 words
The invention as defined in claim 1 wherein the third material is urea.
Claim 9
Dependent Claim
13 words
The invention as defined in claim 1 wherein the third material is dicyanodiamide.
Claim 10
Dependent Claim
17 words
The invention as defined in claim 1 wherein the third material is a pyrolysis/condensation product of dicyanodiamide.
Claim 11
Dependent Claim
32 words
The invention as defined in claim 7 wherein the rate of addition of urea is from about 0.1 to about 4 percent by weight of the bath per hour of addition time.
Claim 12
Dependent Claim
32 words
The invention as defined in claim 7 wherein the rate of addition of urea is controlled as a function of temperature and load size as depicted in the graph of FIG. 1.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-05-18 | 1984-11-17 | 1985-05-19 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-05-18 | 1988-11-17 | 1989-05-19 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-05-18 | 1992-11-17 | 1993-05-19 | $7700.00 | Window Closed / Lapsed |