US4267224A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Plastic material for simulating engraved metal plates
Assignee: Contemporary Inc
•
Filing: 1979-07-18
•
Granted: 1981-05-12
•
Expires: 1999-07-18
Abstract
Abstract A plastic material which is suitable for simulating engraving on metal has a substrate which is not deformed by the heat or pressure of a hot stamping process. A sheet or layer of thermoplastic material of limited thickness is laminated to the upper surface of the substrate. The opposite side of the thermoplastic material is covered by a containment film. Thus, within the limits of manufacturing tolerances, the layer of thermoplastic material may be subjected to any amount of pressure to produce a debossment which is no deeper than the depth of the limited thickness when a hot stamping die bottoms on the non-deformable substrate. Therefore, there is a much more predictable end product.
Inventors
- 👤 James C. Kanzelberger
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 20:45
CPC Classifications
B; B32; B32B; B32B27/00; B32B27/06; B32B27/08; B32B15/00; B32B15/04; B32B15/08; B44; B44C; B44C3/00; B44C3/08; B44C3/085; B44F; B44F11/00; B44F9/00; B44F9/10; B32B2439/00; B32B2439/40; B32B2439/66; Y; Y10; Y10S; Y10S428/00; Y10S428/913; Y10T; Y10T156/00; Y10T156/10; Y10T156/1002; Y10T156/1039; Y10T428/00; Y10T428/24; Y10T428/24942; Y10T428/2495; Y10T428/24967; Y10T428/24975; Y10T428/31504; Y10T428/31678; Y10T428/31681; Y10T428/31692; Y10T428/31699; Y10T428/31786; Y10T428/31797
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
113 words
A plastic material comprising a laminated structure forming a plate having a metal-like appearance, said structure having a substrate layer of material which does not distort under hot stamping pressures and temperatures, a second layer of thermoplastic material having a predetermined thickness superimposed over said substrate, said thermoplastic material flowing under the heat and pressure of a hot stamping die, whereby the depth of the hot stamping debossment is limited to the predetermined thickness of said thermoplastic layer, and a film of non-heat-spreading material covering the surface of said thermoplastic material which is opposite said substrate, said film following and containing the flow of said thermoplastic material under hot stamping heat and pressure.
Claim 2
Dependent Claim
113 words
A plastic material comprising a laminated structure forming a plate having a metal-like appearance, said structure having a substrate layer of material which does not distort under hot stamping pressures and temperatures, a second layer of thermoplastic material having a predetermined thickness superimposed over said substrate, said thermoplastic material flowing under the heat and pressure of a hot stamping die, whereby the depth of the hot stamping debossment is limited to the predetermined thickness of said thermoplastic layer, and a film of non-heat-spreading material covering the surface of said thermoplastic material which is opposite said substrate, said film following and containing the flow of said thermoplastic material under hot stamping heat and pressure.
Claim 3
Dependent Claim
21 words
The material of claim 1 wherein said substrate is a polyester material having a thickness of at least approximately 0.005 inches.
Claim 4
Dependent Claim
16 words
The material of claim 2 wherein said thermoplastic layer has a thickness of approximately 0.004 inches.
Claim 5
Dependent Claim
19 words
The material of claim 3, wherein said film is a polyester material having a thickness of approximately 0.001 inches.
Claim 6
Dependent Claim
13 words
The material of claim 4 and a colored coating layer over said film.
Claim 7
Dependent Claim
16 words
The material of claim 1 wherein said thermoplastic layer has a thickness of approximately 0.004 inches.
Claim 8
Dependent Claim
19 words
The material of claim 6, wherein said film is a polyester material having a thickness of approximately 0.001 inches.
Claim 9
Dependent Claim
13 words
The material of claim 1 wherein said substrate is a sheet of metal.
Claim 10
Dependent Claim
14 words
The material of claim 1 wherein said substrate is a sheet of metal stock.
Claim 11
Dependent Claim
25 words
The material of claim 1 wherein said substrate is a sheet of metal stock of the type used for making the walls of beverage cans.
Claim 12
Dependent Claim
96 words
A process for making a debossable plastic material, said process comprising the steps of: a. forming a substrate from a material which does not deboss under heat and pressure; b. forming a layer of thermoplastic material of limited thickness integrally with and over the surface of said substrate, whereby debossment under heat and pressure is only possible in said layer of limited thickness; and c. forming integrally with and over the surface of said thermoplastic material a heat-resisting film which does not spread said heat, said film having a thickness which follows and confines said debossment.
Claim 13
Dependent Claim
96 words
A process for making a debossable plastic material, said process comprising the steps of: a. forming a substrate from a material which does not deboss under heat and pressure; b. forming a layer of thermoplastic material of limited thickness integrally with and over the surface of said substrate, whereby debossment under heat and pressure is only possible in said layer of limited thickness; and c. forming integrally with and over the surface of said thermoplastic material a heat-resisting film which does not spread said heat, said film having a thickness which follows and confines said debossment.
Claim 14
Dependent Claim
23 words
The process of claim 11 wherein said limited thickness causes a rim of thermoplastic material to rise around the perimeter of said debossment.
Claim 15
Dependent Claim
28 words
The process of claim 12 wherein said heat-resisting film is a polyester film having a metallized surface, whereby the surface of said debossable material has a metallic appearance.
References Cited (Backward Citations)
US3014828A
Cited
US3480500A
Cited
US3510388A
Cited
US3567571A
Cited
US3681180A
Cited
US3666516A
Cited
US3953635A
Cited
US3940864A
Cited
US4084032A
Cited
US4125655A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-05-11 | 1984-11-10 | 1985-05-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-05-11 | 1988-11-10 | 1989-05-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-05-11 | 1992-11-10 | 1993-05-12 | $7700.00 | Window Closed / Lapsed |