Aqueous polymer mixture, process for its preparation and its use as substrate anchoring, blocking resistant one-coat sealing lacquer on sheet products

Claim 2

An aqueous polymer mixture of at least two components containing a vinylidene halide copolymer for the preparation of heat-sealing one layer coatings comprising I component A which containins the vinylidene halide compolymer and is present in the form of an acid aqueous dispersion and consists of micronuclear shell structures comprising a copolymer which forms the nuclear portion which copolymer consists of recurrent structural units derived from a monomer mixture of 10 to 57% by weight of methyl acrylate and/or 5 to 30% by weight of ethyl acrylate and/or 1 to 5% by weight of acrylic acid and/or 15 to 30% by weight of methacrylic acid-n-butyl ester and/or 15 to 30% by weight of methyl methacrylate and the amount of vinylidene halide necessary to make up the percentage by weight to 100, and a copolymer forming the shell portion, consisting of recurrent structural units derived from a monomer mixture of 1 to 14% by weight of methyl acrylate and/or 1 to 14% by weight of methyl methacrylate and/or 1 to 14% by weight of ethyl methacrylate and/or 1 to 14% by weight of ethyl hexyl acrylate and/or 1 to 14% by weight of acrylic acid-n-butyl ester and/or 1 to 14% by weight of methacrylic acid-n-butyl ester and 0.1 to 5% by weight of itaconic acid and the quantity of vinylidene halide required to make up this monomer mixture to 100% by weight but not amounting to more than 95% by weight thereof based on 100% of the total monomer mixture and II of a component B, which is a polymeric anchoring substance containing functional groups and which is added in form of an alkaline aqueous solution and consists of homopolymers and/or copolymers derived from unsaturated carboxylic acid amid-N-methylol derivatives corresponding to the general formula ##STR5## in which R represents --H or --CH 3 and Y represents ##STR6##

Claim 3

An aqueous polymer mixture as claimed in claim 1 wherein component B contains in addition units derived from unsaturated water-soluble carboxylic acids and/or the amide of these unsaturated carboxylic acids and/or methacrylic acid amide.

Claim 4

An aqueous polymer mixture as claimed in claim 1 which also contains components C in the form of plasticizers and/or components D in the form of lubricants and/or components E in the form of pigments.

Claim 5

An aqueous polymer mixture as claimed in claim 1 in which the vinylidene halide is vinylidene chloride.

Claim 6

An aqueous polymer mixture as claimed in claim 1 in which the carboxylic acid amide-N-methylol derivative is methacrylic acid amido-N-methylol methyl ether.

Claim 7

An aqueous polymer mixture as claimed in claim 1 in which in addition to methacrylic acid amido-N-methylolmethyl ether, component B contains recurrent structural unit derived from an acrylic acid amide and optionally acrylic acid.

Claim 8

An aqueous polymer mixture as claimed in claim 6 in which the recurrent structural unit, acrylic acid amide, in component B is replaced by the recurrent structural unit, N-methylolacrylamide.

Claim 9

An aqueous polymer mixture as claimed in claim 6 in which in component B, the recurrent structural units derived from methacrylic acid amido-N-methylomethyl ether, are present in a quantity of 20 to 80% by weight from acrylic acid amide in a quantity of 20 to 80% by weight and optionally from N-methylolacrylamide, in a quantity of 20 to 30% by weight and from acrylic acid in a quantity of 3 to 8% by weight.

Claim 10

A process for the preparation of a polymer mixture as claimed in claim 1 in which in order to produce component A, a nuclear dispersion (substance I) is first produced by known aqueous emulsion polymerisation techniques, by the copolymerisation of 10 to 57% by weight methyl acrylate and/or 5 to 30% by weight of ethyl acrylate and/or 1 to 5% by weight of acrylic acid and/or 15 to 30% by weight of methacrylic acid-n-butyl-ester and/or 15 to 30% by weight of methyl methacrylate and the quantity of vinylidene halide required to make the percentage by weight up to 100, using soidum vinyl sulphonate and a conventional emulsifier in the presence of a redox catalyst, and on this resulting nuclear polymer substance (substance I) which is in the form of an aqueous dispersion there is then polymerised an aqueous dispersion of a shell building substance which has been formed from three separately prepared substances (II, III, and IV), this latter polymerisation being carried out by adding, to the the already polymerised, dispersed nuclear substances I to which has previously been added an aqueous solution of itaconic acid and a similar solution of a conventional redox catalyst, the aforesaid substance II in the form of a monomeric mixture of vinylidene halide, butyl acrylate and ethyl hexyl acrylate, and, separately therefrom, the aforesaid substance III in the form of a mixture of a commercial emulsifier and the reducing part of a conventional redox catalyst and, separately therefrom, the aforesaid substance IV in the form of the oxidizing part of a conventional redox catalyst, which oxidizing part has been taken up in water, and then producing the shell structure polymer on this nuclear substance by a conventional emulsion polymerisation technique to form the aqueous dispersion of component A, to which is added the water-soluble component B which has been prepared separately by (co)polymerisation from an unsaturated carboxylic acid amide-N-methylol derivative corresponding to the general formula ##STR7## in which R represents --H or --CH 3 and Y represents ##STR8## and optionally an unsaturated water soluble carboxylic acid and/or the amide of this carboxylic acid and/or methacrylic acid amide, using conventional techniques with the addition of a redox initiator, and the finished, aqueous polymer mixture is thus formed, optionally with the addition of further components in the form of known plasticizers C and/or lubricants D and/for pigments F.

Claim 11

A process as claimed in claim 9 in which components A is prepared in an aqueous acidic medium and is stable when stored in such a medium.

Claim 12

A process as claimed in claim 9 in which component B is prepared in an aqueous alkaline medium and is stable when stored in such a medium.

Claim 13

A process as claimed in claim 9 in which the mixture of components A and B is prepared in a weakly acid to neutral medium and is stable when stored in such a medium.

Claim 14

A process as claimed in claim 9 in which the stabilizer used for the polymer mixture of A+B is a weakly acid to neutral medium adjusted to a pH of 5.5 to 7.

Claim 15

A polymer mixture when prepared by a process as claimed in claim 9.