Process for preparing vinyl acetate-ethylene copolymer latices
Assignee: Equistar Chemicals LP
•
Filing: 1979-01-22
•
Granted: 1981-05-12
•
Expires: 1999-01-22
Abstract
Abstract Vinyl acetate-ethylene copolymer latices having an inherent viscosity of not less than about 1.90 and demonstrating superior performance in the Time of Set Test and Vinyl Wetting Test are prepared by the process which comprises copolymerizing from about 60% to about 95% by weight of vinyl acetate monomer with from about 40% to about 5% by weight of ethylene monomer in an emulsified reaction medium containing: (a) at least one surface active agent in an amount of not less than about 1.0% by weight, and not more than about 2.0% by weight, of the total monomer, (b) a catalyst, and (c) a protective colloid, the total weight of the surface active agent and vinyl acetate monomer being introduced into the reaction medium in delayed increments prior to and after the commencement of copolymerization.
Inventors
- 👤 Manfred Heimberg
- 👤 Louis J. Rekers
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 23:55
CPC Classifications
C; C08; C08F; C08F218/00; C08F218/02; C08F218/04; C08F218/08
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
151 words
A process for preparing vinyl acetate-ethylene copolymer latices having an inherent viscosity of not less than about 1.90 measured upon solution of 0.250 gm of latex in 50-75 ml of 80% weight aqueous acetic acid heated to 50°-60° C., and demonstrating superior performance in the Time of Set Test and Vinyl Wetting Test which comprises copolymerizing from about 60% to about 95% by weight of vinyl acetate monomer with from about 40% to about 5% by weight of ethylene monomer is an emulsified reaction medium containing: (a) at least one surface active agent in an amount of not less than 1.0% by weight, and not more than 2.0% by weight, of the total monomer, (b) a catalyst, and (c) a protective colloid, the total weight of the surface active agent and vinyl acetate monomer being introduced into the reaction medium in delayed increments prior to and after the commencement of copolymerization.
Claim 2
Dependent Claim
151 words
A process for preparing vinyl acetate-ethylene copolymer latices having an inherent viscosity of not less than about 1.90 measured upon solution of 0.250 gm of latex in 50-75 ml of 80% weight aqueous acetic acid heated to 50°-60° C., and demonstrating superior performance in the Time of Set Test and Vinyl Wetting Test which comprises copolymerizing from about 60% to about 95% by weight of vinyl acetate monomer with from about 40% to about 5% by weight of ethylene monomer is an emulsified reaction medium containing: (a) at least one surface active agent in an amount of not less than 1.0% by weight, and not more than 2.0% by weight, of the total monomer, (b) a catalyst, and (c) a protective colloid, the total weight of the surface active agent and vinyl acetate monomer being introduced into the reaction medium in delayed increments prior to and after the commencement of copolymerization.
Claim 3
Dependent Claim
23 words
The process of claim 1 wherein in addition to ethylene, at least one other ethylenically unsaturated comonomer is copolymerized with the vinyl acetate.
Claim 4
Dependent Claim
55 words
The process of claim 1 wherein the surface active agent is a nonionic surface active agent selected from the group consisting of (i) the alkylphenoxypoly(ethyleneoxy)ethanols, (ii) the polyoxalkylene derivatives of hexitol or partial long-chain fatty acid esters, (iii) condensates of ethylene oxide with a hydrophobic base, and (iv) ethylene oxide derivatives of long-chain fatty alcohols.
Claim 5
Dependent Claim
18 words
The process of claim 1 wherein from about 1.2% to about 1.5% total surface active agent is employed.
Claim 6
Dependent Claim
26 words
The process of claim 1 wherein the protective colloid is employed in the emulsified reaction medium at from about 0.1% to about 2.0% by weight thereof.
Claim 7
Dependent Claim
15 words
The process of claim 1 wherein the protective colloid is a partially hydrolyzed polyvinyl alcohol.
Claim 8
Dependent Claim
34 words
The process of claim 1 wherein from about 25% to about 90% by weight of the total surface active agent is present in the emulsified reaction medium at the beginning of the copolymerization reaction.
Claim 9
Dependent Claim
34 words
The process of claim 1 wherein from about 5% to about 90% by weight of the total vinyl acetate monomer is present in the emulsified reaction medium at the beginning of the copolymerization reaction.
References Cited (Backward Citations)
GB994380A
Cited
GB1112863A
Cited
US3844990A
Cited
GB1133867A
Cited
US3423352A
Cited
GB1133556A
Cited
GB1229989A
Cited
US3578618A
Cited
GB1233837A
Cited
US3644262A
Cited
US4128518A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-05-11 | 1984-11-10 | 1985-05-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-05-11 | 1988-11-10 | 1989-05-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-05-11 | 1992-11-10 | 1993-05-12 | $7700.00 | Window Closed / Lapsed |