Self supporting electrical resistor composed of glass, refractory materials and noble metal oxide
Assignee: CTS Corp
•
Filing: 1977-10-05
•
Granted: 1981-05-12
•
Expires: 1997-10-05
Abstract
Abstract Disclosed is a glass bonded electrical resistor element and composition composed of glass binder, refractory material to provide form stability during firing and electric conductivity imparting materials of noble metal and noble metal oxides. Manganese may also be present. Oxides of Ru and Ir are disclosed as being significant.
Inventors
- 👤 Curtis L. Holmes
- 👤 William M. Faber, Sr.
- 👤 Gaylord L. Francis
- 👤 Otis F. Boykin
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 15:54
CPC Classifications
H; H01; H01C; H01C17/00; H01C17/06; H01C17/065; H01C17/06506; H01C17/06513; H01C17/06533; H01C17/0654; Y; Y10; Y10T; Y10T29/00; Y10T29/49; Y10T29/49002; Y10T29/49117; Y10T29/49204; Y10T29/49206
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
110 words
An electrical resistor comprising a composition having a glass, at least 0.2 percent by weight of the total composition being a noble metal selected from the group consisting of iridium and ruthenium, said noble metal provided as a pyrolytically decomposable organo-metallic composition calcined to effect iridium oxide or ruthenium oxide and dispersed through the composition, and 30 percent to 70 percent by weight of the total composition of a finely divided refractory filler oxide selected from the group consisting of alumina and silica, the glass bonding the finely divided refractory filler oxide together, the refractory filler oxide being uniformly dispersed in the composition, said composition attaining consistent electrical resistor properties.
Claim 2
Dependent Claim
110 words
An electrical resistor comprising a composition having a glass, at least 0.2 percent by weight of the total composition being a noble metal selected from the group consisting of iridium and ruthenium, said noble metal provided as a pyrolytically decomposable organo-metallic composition calcined to effect iridium oxide or ruthenium oxide and dispersed through the composition, and 30 percent to 70 percent by weight of the total composition of a finely divided refractory filler oxide selected from the group consisting of alumina and silica, the glass bonding the finely divided refractory filler oxide together, the refractory filler oxide being uniformly dispersed in the composition, said composition attaining consistent electrical resistor properties.
Claim 3
Dependent Claim
127 words
An electrical resistor comprising a finely divided refractory filler oxide in the range of 30 percent to 70 percent by weight of the total composition and selected from the group consisting of alumina and silica, a glass bonding the refractory filler oxide together, the refractory filler oxide being uniformly dispersed in the composition, and at least 0.2 percent by weight of the total composition being a noble metal selected from the group consisting of iridium and ruthenium, said noble metal provided as a pyrolytically decomposable organo-metallic composition calcined to effect iridium oxide or ruthenium oxide and dispersed through the composition, the ruthenium oxide comprising from 1 percent to 99 percent by weight of the total mixture of metal oxides present, said composition attaining consistent electrical resistor properties.
Claim 4
Dependent Claim
127 words
An electrical resistor comprising a finely divided refractory filler oxide in the range of 30 percent to 70 percent by weight of the total composition and selected from the group consisting of alumina and silica, a glass bonding the refractory filler oxide together, the refractory filler oxide being uniformly dispersed in the composition, and at least 0.2 percent by weight of the total composition being a noble metal selected from the group consisting of iridium and ruthenium, said noble metal provided as a pyrolytically decomposable organo-metallic composition calcined to effect iridium oxide or ruthenium oxide and dispersed through the composition, the ruthenium oxide comprising from 1 percent to 99 percent by weight of the total mixture of metal oxides present, said composition attaining consistent electrical resistor properties.
Claim 5
Dependent Claim
129 words
An electrical resistor comprising a finely divided refractory filler oxide in the range to 30 percent to 70 percent by weight of the total composition and selected from the group consisting of alumina and silica, a glass bonding the refractory filler oxide together, the refractory filler oxide being uniformly dispersed in the composition, and at least 0.2 percent by weight of the total composition being the combination of a metal and the noble metal ruthenium, said noble metal provided as a pyrolytically decomposable organo-metallic composition calcined to effect ruthenium oxide and dispersed through the composition the metal and the metal oxide comprising at least fifty percent by weight ruthenium oxide and from about ten percent to about fifty percent by weight platinum, said composition attaining consistent electrical resistor properties.
Claim 6
Dependent Claim
129 words
An electrical resistor comprising a finely divided refractory filler oxide in the range to 30 percent to 70 percent by weight of the total composition and selected from the group consisting of alumina and silica, a glass bonding the refractory filler oxide together, the refractory filler oxide being uniformly dispersed in the composition, and at least 0.2 percent by weight of the total composition being the combination of a metal and the noble metal ruthenium, said noble metal provided as a pyrolytically decomposable organo-metallic composition calcined to effect ruthenium oxide and dispersed through the composition the metal and the metal oxide comprising at least fifty percent by weight ruthenium oxide and from about ten percent to about fifty percent by weight platinum, said composition attaining consistent electrical resistor properties.
Claim 7
Dependent Claim
133 words
An electrical resistor comprising a finely divided refractory filler oxide in the range of 30 percent to 70 percent by weight of the total composition and selected from the group consisting of alumina and silica, a glass bonding the refractory filler oxide together, the refractory filler oxide being uniformly dispersed in the composition, and at least 0.2 percent by weight of the total composition being the combination of a metal and the noble metal ruthenium, said noble metal provided as a pyrolytically decomposable organo-metallic composition calcined to effect ruthenium oxide and dispersed through the composition, the metal and the metal oxide comprising from about 20 percent to about 90 percent by weight ruthenium oxide and from about 10 percent to about 80 percent by weight manganese, said composition attaining consistent electrical resistor properties.
Claim 8
Dependent Claim
133 words
An electrical resistor comprising a finely divided refractory filler oxide in the range of 30 percent to 70 percent by weight of the total composition and selected from the group consisting of alumina and silica, a glass bonding the refractory filler oxide together, the refractory filler oxide being uniformly dispersed in the composition, and at least 0.2 percent by weight of the total composition being the combination of a metal and the noble metal ruthenium, said noble metal provided as a pyrolytically decomposable organo-metallic composition calcined to effect ruthenium oxide and dispersed through the composition, the metal and the metal oxide comprising from about 20 percent to about 90 percent by weight ruthenium oxide and from about 10 percent to about 80 percent by weight manganese, said composition attaining consistent electrical resistor properties.
Claim 9
Dependent Claim
139 words
An electrical resistor comprising a finely divided refractory filler oxide in the range of 30 percent to 70 percent by weight of the total composition and selected from the group consisting of alumina and silica, a glass bonding the refractory filler oxide together, the refractory filler oxide being uniformly dispersed in the composition, and at least 0.2 percent of the total composition being the combination of a metal and the noble metal iridium, said noble metal provided as a pyrolytically decomposable organo-metallic composition calcined to effect iridium oxide and dispersed through the composition, the metal oxide comprising from about 50 percent to about 90 percent iridium oxide by weight and the metal comprising from about 10 percent to about 50 percent platinum by weight of the combination of metal and metal oxide, said composition attaining consistent electrical resistor properties.
Claim 10
Dependent Claim
139 words
An electrical resistor comprising a finely divided refractory filler oxide in the range of 30 percent to 70 percent by weight of the total composition and selected from the group consisting of alumina and silica, a glass bonding the refractory filler oxide together, the refractory filler oxide being uniformly dispersed in the composition, and at least 0.2 percent of the total composition being the combination of a metal and the noble metal iridium, said noble metal provided as a pyrolytically decomposable organo-metallic composition calcined to effect iridium oxide and dispersed through the composition, the metal oxide comprising from about 50 percent to about 90 percent iridium oxide by weight and the metal comprising from about 10 percent to about 50 percent platinum by weight of the combination of metal and metal oxide, said composition attaining consistent electrical resistor properties.
Claim 11
Dependent Claim
114 words
An electrical resistor comprising finely divided refractory filler oxide particles in the range of 30 percent to 70 percent by weight of the total composition and selected from the group consisting of alumina and silica, at least 0.2 percent by weight of the total composition being a noble metal selected from the group consisting of iridium and ruthenium, said noble metal provided as a pyrolytically decomposable organo-metallic composition calcined to effect iridium oxide or ruthenium oxide deposited on the surface of the refractory filler oxide particles, and a glass bonding the refractory filler oxide particles togther, the refractory filler oxide particles being uniformly dispersed in the composition, said composition attaining consistent electrical resistor properties.
Claim 12
Dependent Claim
114 words
An electrical resistor comprising finely divided refractory filler oxide particles in the range of 30 percent to 70 percent by weight of the total composition and selected from the group consisting of alumina and silica, at least 0.2 percent by weight of the total composition being a noble metal selected from the group consisting of iridium and ruthenium, said noble metal provided as a pyrolytically decomposable organo-metallic composition calcined to effect iridium oxide or ruthenium oxide deposited on the surface of the refractory filler oxide particles, and a glass bonding the refractory filler oxide particles togther, the refractory filler oxide particles being uniformly dispersed in the composition, said composition attaining consistent electrical resistor properties.
References Cited (Backward Citations)
US1764311A
Cited
US2739901A
Cited
US2718577A
Cited
US2786819A
Cited
US2950995A
Cited
US3149002A
Cited
US2950996A
Cited
US2924540A
Cited
US3154503A
Cited
US3304199A
Cited
US3329526A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-05-11 | 1984-11-10 | 1985-05-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-05-11 | 1988-11-10 | 1989-05-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-05-11 | 1992-11-10 | 1993-05-12 | $7700.00 | Window Closed / Lapsed |