US4266979A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Oxygen sensor ceramic and process for preparing the same
Assignee: Hitachi Ltd
•
Filing: 1979-10-01
•
Granted: 1981-05-12
•
Expires: 1999-10-01
Abstract
Abstract Oxygen sensor ceramic of solid electrolyte of zirconia-yttria system comprises aggregates of cubic zirconia grains having an average grain size of 2-10 mu m and monoclinic zirconia grains having an average grain size of 0.2-1 mu m, the appregates of the cubic zirconia grains being in contact with one another, and the monoclinic zirconia grains being distributed as aggregates in clearances among the aggregates of the cubic zirconia grains, and has a high thermal shock resistance, a high mechanical strength and a resistivity equal to that of the ceramic consisting only of cubic zirconia grains. The oxygen sensor ceramic is prepared by mixing zirconia powder having a grain size of 0.1-0.5 mu m with 4-8% by mole of yttria powder having an average grain size of 0.5-5 mu m, on the basis of total mixture, and molding and firing the mixture at 1,400 DEG -1,550 DEG C.
Inventors
- 👤 Tadahiko Miyoshi
- 👤 Takeo Yamazaki
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 17:02
CPC Classifications
G; G01; G01N; G01N27/00; G01N27/26; G01N27/403; G01N27/406; G01N27/407; G01N27/4073; C; C04; C04B; C04B35/00; C04B35/01; C04B35/48; C04B35/486; H; H01; H01M; H01M8/00; H01M8/10; H01M8/12; H01M8/124; H01M8/1246; H01M8/1253; Y; Y02; Y02E; Y02E60/00; Y02E60/30; Y02E60/50; Y02P; Y02P70/00; Y02P70/50
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
71 words
An oxygen sensor ceramic of a solid electolyte of a zirconia-yttria system, which comprises aggregates of cubic zirconia grains having an average grain size of 2-10 μm and monoclinic zirconia grains having an average grain size of 0.2-1 μm, the aggregates of said cubic zirconia grains being in contact with one another, and said monoclinic zirconia grains being distributed as aggregates in clearances among the aggregates of the cubic zirconia grains.
Claim 2
Dependent Claim
71 words
An oxygen sensor ceramic of a solid electolyte of a zirconia-yttria system, which comprises aggregates of cubic zirconia grains having an average grain size of 2-10 μm and monoclinic zirconia grains having an average grain size of 0.2-1 μm, the aggregates of said cubic zirconia grains being in contact with one another, and said monoclinic zirconia grains being distributed as aggregates in clearances among the aggregates of the cubic zirconia grains.
Claim 3
Dependent Claim
31 words
An oxygen sensor ceramic according to claim 1, wherein the cubic zirconia grains have an average grain size at least 5 times as large as that of the monoclinic zirconia grains.
Claim 4
Dependent Claim
27 words
An oxygen sensor ceramic according to claim 1 or 2, wherein an average yttria concentration in the monoclinic zirconia is in a range of 0.01-1% by mole.
Claim 5
Dependent Claim
27 words
An oxygen sensor ceramic according to claim 1 or 2, wherein an average yttria concentration in the cubic zirconia is in a range of 7-10% by mole.
Claim 6
Dependent Claim
30 words
An oxygen sensor ceramic according to claim 1 or 2, wherein an amount of the monoclinic zirconia in the ceramic is 10-50% by mole on the basis of total mixture.
Claim 7
Dependent Claim
57 words
A process for preparing an oxygen sensor ceramic, which comprises mixing monoclinic zirconia powder having a grain size of 0.1-0.5 μm with 4-8% by mole of yttria powder on the basis of the total mixture, said yttria powder having an average grain size of 0.5-5 μm, molding and firing the mixture at a temperature of 1,400°-1,550° C.
Claim 8
Dependent Claim
57 words
A process for preparing an oxygen sensor ceramic, which comprises mixing monoclinic zirconia powder having a grain size of 0.1-0.5 μm with 4-8% by mole of yttria powder on the basis of the total mixture, said yttria powder having an average grain size of 0.5-5 μm, molding and firing the mixture at a temperature of 1,400°-1,550° C.
Claim 9
Dependent Claim
48 words
A process for preparing an oxygen sensor ceramic as set forth in claim 6, wherein the mixture of zirconia powder and yttrium powder is calcinated at a temperature of about 1100° to about 1300° C., and then pulverized to grain size of about 0.5 μm prior to molding.
Claim 10
Dependent Claim
33 words
A process for preparing an oxygen sensor ceramic as set forth in claim 6 or 7, wherein the mixture of zirconia powder and yttrium powder is mixed with a binder prior to molding.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-05-11 | 1984-11-10 | 1985-05-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-05-11 | 1988-11-10 | 1989-05-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-05-11 | 1992-11-10 | 1993-05-12 | $7700.00 | Window Closed / Lapsed |