Process for non-ferrous metals production from complex sulphide ores containing copper, lead, zinc, silver and/or gold
Assignee: Individual
•
Filing: 1979-12-14
•
Granted: 1981-05-12
•
Expires: 1999-12-14
Abstract
Abstract Metal sulphide ore is leached by water under a low pressure and oxidizing atmosphere to dissolve zinc and copper, hydrolyze iron to hematite, and leave lead and precious metals as insoluble sulphates. The residue is leached by sodium chloride and calcium chloride to dissolve lead and the precious metals.
Inventors
- 👤 Angel L. Redondo-Abad
- 👤 Eduardo Diaz-Nogueira
- 👤 Martin Gerez-Pascual
- 👤 Jose M. Regife-Vega
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 21:07
CPC Classifications
C; C22; C22B; C22B3/00; C22B3/04; C22B3/06; C22B3/08; Y; Y02; Y02P; Y02P10/00; Y02P10/20
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
293 words
A process for non-ferrous metals production from complex sulphide ores containing copper, lead, of zinc, silver and/or gold which comprises: grinding said ore and subjecting it to a flotation operation for obtaining a bulk concentrate of the non-ferrous metals minerals and for separating most of the pyrite as a flotation tail, slurrying said concentrate in water in such a way as to obtain a predetermined solid-liquid ratio and subjecting said slurry to an oxidation leach in a stirred pressure reactor, at an oxygen partial pressure in the range of from about 5 to 15 Kg/cm 2 g and a temperature in the range of from about 150° to 250° C. for complete oxidation of metal sulphides to sulphates, separating the reaction mixture into a solid residue containing ferric oxide, lead sulphate and precious metals, and a leaching liquor containing sulphuric acid, copper sulphate and zinc sulphate, neutralizing the free sulphuric acid contained in said leaching liquor with grounded limestone to a final pH in the range of from about 1.5 to 2.5. removing precipitated gypsum from solution, recovering copper by cementation or solvent extraction and electrowinning, leaching lead, silver and gold from the said solid residue by a strong chloride solution containing calcium chloride at a temperature in the range of about 60° to 90° C. at a pH in the range of from about 7.0 to 1.0 and in the presence of about 1 gram per liter of ferric chloride, recovering lead, silver and gold from the brine solution after solid removal by cementation with scrap zinc, mixing the lead free brine solution containing the zinc used in lead cementation with the zinc bearing solution from the copper recovery operation, and recovery zinc from the resulting solution by solvent extraction and electrowinning.
Claim 2
Dependent Claim
293 words
A process for non-ferrous metals production from complex sulphide ores containing copper, lead, of zinc, silver and/or gold which comprises: grinding said ore and subjecting it to a flotation operation for obtaining a bulk concentrate of the non-ferrous metals minerals and for separating most of the pyrite as a flotation tail, slurrying said concentrate in water in such a way as to obtain a predetermined solid-liquid ratio and subjecting said slurry to an oxidation leach in a stirred pressure reactor, at an oxygen partial pressure in the range of from about 5 to 15 Kg/cm 2 g and a temperature in the range of from about 150° to 250° C. for complete oxidation of metal sulphides to sulphates, separating the reaction mixture into a solid residue containing ferric oxide, lead sulphate and precious metals, and a leaching liquor containing sulphuric acid, copper sulphate and zinc sulphate, neutralizing the free sulphuric acid contained in said leaching liquor with grounded limestone to a final pH in the range of from about 1.5 to 2.5. removing precipitated gypsum from solution, recovering copper by cementation or solvent extraction and electrowinning, leaching lead, silver and gold from the said solid residue by a strong chloride solution containing calcium chloride at a temperature in the range of about 60° to 90° C. at a pH in the range of from about 7.0 to 1.0 and in the presence of about 1 gram per liter of ferric chloride, recovering lead, silver and gold from the brine solution after solid removal by cementation with scrap zinc, mixing the lead free brine solution containing the zinc used in lead cementation with the zinc bearing solution from the copper recovery operation, and recovery zinc from the resulting solution by solvent extraction and electrowinning.
Claim 3
Dependent Claim
34 words
A process according to claim 1 wherein the ore grinding degree and the flotation scheme must be suitable to obtain a bulk flotation concentrate of the non-ferrous metals with a pyrite content below 30%.
Claim 4
Dependent Claim
38 words
A process according to claim 1 wherein the bulk flotation concentrate is slurried in water at a solid-liquid ratio such that the total iron in the solid to water ratio be lower than 20 Kg. per cubic meter.
Claim 5
Dependent Claim
27 words
A process according to claim 1 wherein the oxidation leach reaction of the bulk concentrate slurry in water is carried out at a temperature of 200°±10° C.
Claim 6
Dependent Claim
39 words
A process according to claim 1 wherein the oxidation leach reaction of the bulk concentrate slurry in water is carried out at constant pressure with an oxygen partial pressure in the oxidizing gas higher than 5 Kg/cm 2 .
Claim 7
Dependent Claim
61 words
A process according to claim 1 wherein the oxidation leach reaction of the bulk concentrate slurry in water is carried out under intense stirring conditions with dispersion of the oxidizing gas into the reacting slurry, in such a way as to create a gas-liquid interphase surface large enough to avoid oxygen disolution rate becoming controlling mechanism, in the overall oxidation kinetics.
Claim 8
Dependent Claim
72 words
A process according to claim 1 where in the conditions of the oxidation leach reaction of the bulk concentrate slurry in water are maintained constant not only until all the metal sulphides are oxidizes to sulphates but also until all the ferric sulphate in solution is hydrolyzed to ferric oxide, which is achieved in a residence time equivalent to a reaction time in the range of from about 45 to 60 minutes.
Claim 9
Dependent Claim
73 words
A process according to claim 1 wherein the pregnant leaching solution containing copper and zinc, after solid-residue removal is neutralized with ground limestone, raising the pH to 2.0±0.2, whereby gypsum is precipitated, washing and removing said gypsum by vacuum filtration, constituting a final solid residue of the process, and producing a clean liquor a pH 2.0 quite suitable to copper recovery either by cementation with scrap iron or by solvent extraction and electrowinning.
Claim 10
Dependent Claim
60 words
A process according to claim 1 wherein the strong chloride solution for leaching lead, silver and gold from the pressure leaching solid residue, is an aqueous solution containing NaCl at a concentration in the range of from about 200 to 300 grams per liter and CaCl 2 at a concentration corresponding to the stoichiometry of the lead to be leached.
Claim 11
Dependent Claim
38 words
A process according to claim 1 wherein the strong chloride solution for lead, silver and gold leaching is initially adjusted to a pH of 1.0 and 1 gram per liter of FeCl 3 is added to said solution.
Claim 12
Dependent Claim
33 words
A process according to claim 1 wherein leaching of lead, silver and gold from the pressure leaching solid residue with the strong chloride solution is carried out at a temperature of 85°±5° C.
Claim 13
Dependent Claim
53 words
A process according to claim 1 wherein the conditions of the leaching of lead, silver and gold from the pressure leaching solid residue with the strong chloride solution, are maintained under mild stirring conditions for a residence time equivalent to a reaction time in the range of from about 15 to 40 minutes.
Claim 14
Dependent Claim
46 words
A process according to claim 1 wherein leaching of lead, silver and gold from the pressure leaching solid residue with the strong chloride solution is carried out at a solid-liquid ratio lower than the equivalent one to the maximum solubility of lead into said chloride solution.
Claim 15
Dependent Claim
50 words
A process according to claim 1 wherein the leaching chloride solution containing lead, silver and gold is separated from the ferric oxide solid residue by thickening and filtration at a temperature higher than 60° C., becoming a suitable solution for lead, silver and gold recovery by cementation with metallic zinc.
Claim 16
Dependent Claim
35 words
A process according to claim 1 wherein at least a portion of the strong chloride solution from lead, silver and gold cementation containing zinc is mixed with the zinc sulphate solution coming from copper recovery.
Claim 17
Dependent Claim
46 words
A process according to claim 15 wherein the chloride concentration in the resulting mixture must be adjusted to a value in the range of from about 30 to 70 grams per liter, reaching suitable conditions of feed material for zinc recovery by solvent extraction and electrowinning.
References Cited (Backward Citations)
US3923976A
Cited
US3957602A
Cited
US4011146A
Cited
US3961941A
Cited
US4063933A
Cited
US4113471A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-05-11 | 1984-11-10 | 1985-05-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-05-11 | 1988-11-10 | 1989-05-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-05-11 | 1992-11-10 | 1993-05-12 | $7700.00 | Window Closed / Lapsed |