Lightweight frothed gypsum structural units
Assignee: Lyondell Chemical Technology LP
•
Filing: 1979-12-26
•
Granted: 1981-05-05
•
Expires: 1999-12-26
Abstract
Abstract Compositions useful for lightweight structural units such as wallboard panels and the like are provided in which low density expandable thermoplastic granules or particles that have been expanded are used in conjunction with a cementitious base material, such as, gypsum (generally calcined to hemihydrate form, i.e. CaSO4.1/2 H2O); a surfactant; an additive which acts as a frothing agent to incorporate an appropriate amount of air into the mixture to aid in obtaining a light density without decreasing strength or causing undue brittleness of the finished product; a film forming component to provide better flow and consistence of the mixture, as well as greater strength, flexibility, water resistance and adherence of the final product when the mixture is cured; and a starch which may be added as a binding agent and to increase the adhesive properties of the mixture. The appropriate combination of the above ingredients can provide a mixture which can be readily mixed, have the proper consistency to be disposed in a board or panel configuration for curing, and will require a decreased excess of water over that required for hydration. Thus, the energy, time, equipment and space necessary to effect curing may be reduced. This will result in significant savings, especially in high speed, high production of product.
Inventors
- 👤 Gerald W. Burkhart
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 21:56
CPC Classifications
C; C04; C04B; C04B28/00; C04B28/14; Y; Y10; Y10T; Y10T428/00; Y10T428/249921; Y10T428/249953; Y10T428/249971; Y10T428/249972; Y10T428/31504; Y10T428/31971; Y10T428/31993; Y10T428/31996
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
139 words
In a lightweight structural unit, the improvement which comprises a heat-cured frothed core containing: (a) a gypsum composition acting as a matrix, (b) a rubbery polymeric latex, in an amount of from about 0.1 to 5% by weight of gypsum, (c) expandable thermoplastic granules in expanded form, in an amount up to about 3% by weight of gypsum, (d) a surfactant, (e) a latex frothing agent, said surfactant and said frothing agent being present in a total amount of from about 0.075 to about 0.3% by weight of gypsum, (f) starch, in an amount of from about 0.5 to 3% by weight of gypsum, and (g) water, but only in an amount sufficient to react with said gypsum composition plus sufficient excess to provide a flowable mixture capable of being disposed in form for curing as a structural element.
Claim 2
Dependent Claim
139 words
In a lightweight structural unit, the improvement which comprises a heat-cured frothed core containing: (a) a gypsum composition acting as a matrix, (b) a rubbery polymeric latex, in an amount of from about 0.1 to 5% by weight of gypsum, (c) expandable thermoplastic granules in expanded form, in an amount up to about 3% by weight of gypsum, (d) a surfactant, (e) a latex frothing agent, said surfactant and said frothing agent being present in a total amount of from about 0.075 to about 0.3% by weight of gypsum, (f) starch, in an amount of from about 0.5 to 3% by weight of gypsum, and (g) water, but only in an amount sufficient to react with said gypsum composition plus sufficient excess to provide a flowable mixture capable of being disposed in form for curing as a structural element.
Claim 3
Dependent Claim
20 words
A lightweight structural unit as claimed in claim 1 wherein the surfactant and the frothing agent comprise a single compound.
Claim 4
Dependent Claim
16 words
A lightweight structural unit as claimed in claim 1 wherein the latex is a styrene-butadiene copolymer.
Claim 5
Dependent Claim
146 words
A heat-cured frothed core composition suitable for a lightweight wallboard which comprises: (a) calcined gypsum in an amount of from about 89 to about 99 parts by weight, (b) up to about 3% by weight of said gypsum of expandable thermoplastic granules in expanded condition, (c) from about 0.1% to about 5% by weight of said gypsum of an emulsion polymeric latex, (d) a surfactant, (e) a latex frothing agent, said agent and said surfactant being present in a total amount of from about 0.075% to about 0.3% by weight of said gypsum, (f) from about 0.5% to about 3% by weight of said gypsum of starch, and (g) water in an amount sufficient to react with said gypsum plus an excess amount only sufficient to provide a smooth plastic flowable mixture to enable disposition of said mixture in a mold means to form said core.
Claim 6
Dependent Claim
146 words
A heat-cured frothed core composition suitable for a lightweight wallboard which comprises: (a) calcined gypsum in an amount of from about 89 to about 99 parts by weight, (b) up to about 3% by weight of said gypsum of expandable thermoplastic granules in expanded condition, (c) from about 0.1% to about 5% by weight of said gypsum of an emulsion polymeric latex, (d) a surfactant, (e) a latex frothing agent, said agent and said surfactant being present in a total amount of from about 0.075% to about 0.3% by weight of said gypsum, (f) from about 0.5% to about 3% by weight of said gypsum of starch, and (g) water in an amount sufficient to react with said gypsum plus an excess amount only sufficient to provide a smooth plastic flowable mixture to enable disposition of said mixture in a mold means to form said core.
Claim 7
Dependent Claim
130 words
In a lightweight gypsum wallboard having a core and at least two facing skin members adhered thereto, an improved core which has been frothed and heat-cured and which comprises: (a) a hemihydrate gypsum composition, (b) up to about 3% by weight of said gypsum composition of expandable thermoplastic particles which have been expanded to a density below about 3 pounds per cubic foot, (c) from about 0.1% to about 5.0% by weight of said gypsum composition of a rubbery polymeric latex, (d) a surfactant, (e) a latex frothing agent, and (f) water in an amount sufficient for hydration of said gypsum composition plus a minimum excess of water sufficient permit mixing of said ingredients into a flowable mixture and disposing said mixture in a mold means to form said core.
Claim 8
Dependent Claim
130 words
In a lightweight gypsum wallboard having a core and at least two facing skin members adhered thereto, an improved core which has been frothed and heat-cured and which comprises: (a) a hemihydrate gypsum composition, (b) up to about 3% by weight of said gypsum composition of expandable thermoplastic particles which have been expanded to a density below about 3 pounds per cubic foot, (c) from about 0.1% to about 5.0% by weight of said gypsum composition of a rubbery polymeric latex, (d) a surfactant, (e) a latex frothing agent, and (f) water in an amount sufficient for hydration of said gypsum composition plus a minimum excess of water sufficient permit mixing of said ingredients into a flowable mixture and disposing said mixture in a mold means to form said core.
Claim 9
Dependent Claim
13 words
The product claimed in claim 5 wherein the surfactant is a non-ionic surfactant.
Claim 10
Dependent Claim
17 words
The product claimed in claim 5 wherein the surfactant and the frothing agent comprise sodium lauryl sulfate.
Claim 11
Dependent Claim
28 words
The product claimed in claim 5 wherein the rubbery polymeric latex comprises a styrene-butadiene latex having a styrene to butadiene ratio of between about 20:80 to about 80:20.
Claim 12
Dependent Claim
62 words
The product as claimed in claim 5 in which the expanded thermoplastic particles are present in an amount of about 2.8% by weight of gypsum, the latex is present in an amount of about 2% by weight of the gypsum, and the surfactant and frothing agent are present in a total amount of about 0.1 to 0.2% by weight of the gypsum.
Claim 13
Dependent Claim
130 words
The process of making a core for a lightweight structural unit which comprises mixing together a gypsum composition, a rubbery polymeric latex in an amount of about 0.1 to 5% by weight of the gypsum, expandable thermoplastic granules in expanded form in an amount of up to about 3% by weight of the gypsum, a surfactant, a frothing agent, said surfactant and frothing agent being present in a total amount of from about 0.075 to about 0.3% by weight of the gypsum, and water, said water being added only in an amount to react with said gypsum composition plus sufficient excess to provide a flowable mixture, mixing said ingredients to entrain air and form a froth, disposing the same in a form means, and heating said mixture to cured form.
Claim 14
Dependent Claim
130 words
The process of making a core for a lightweight structural unit which comprises mixing together a gypsum composition, a rubbery polymeric latex in an amount of about 0.1 to 5% by weight of the gypsum, expandable thermoplastic granules in expanded form in an amount of up to about 3% by weight of the gypsum, a surfactant, a frothing agent, said surfactant and frothing agent being present in a total amount of from about 0.075 to about 0.3% by weight of the gypsum, and water, said water being added only in an amount to react with said gypsum composition plus sufficient excess to provide a flowable mixture, mixing said ingredients to entrain air and form a froth, disposing the same in a form means, and heating said mixture to cured form.
Claim 15
Dependent Claim
38 words
The process as claimed in claim 10 in which the surfactant, frothing agent and a portion of the water are initially mixed and agitated to make a froth prior to the addition of the balance of the ingredients.
Claim 16
Dependent Claim
14 words
The process claimed in claim 10 in which the surfactant comprises a non-ionic surfactant.
Claim 17
Dependent Claim
180 words
The process of making a lightweight gypsum composition wallboard having a core and two facing members adhered thereto, the improvement in the making of a core which comprises: (a) mixing water, latex in an amount of from about 0.1 to 5% by weight of the gypsum, a surfactant, and a latex frothing agent, said surfactant and frothing agent being used in a total amount of from about 0.075 to 0.3% by weight of gypsum, (b) agitating the same to entrain air and form a froth, (c) adding calcined gypsum and partially expanded thermoplastic particles at a density of less than 3 pounds per cubic foot in a finite amount of up to 3% by weight of gypsum in a controlled manner to obtain a smooth flowable mixture. (d) adding the balance of a predetermined amount of the water, whereby said mixture contains a minimum of water in excess of that required for reaction with said gypsum and only sufficient to obtain a usable flowable mixture required to be able to place said mixture in a means for molding said core.
Claim 18
Dependent Claim
180 words
The process of making a lightweight gypsum composition wallboard having a core and two facing members adhered thereto, the improvement in the making of a core which comprises: (a) mixing water, latex in an amount of from about 0.1 to 5% by weight of the gypsum, a surfactant, and a latex frothing agent, said surfactant and frothing agent being used in a total amount of from about 0.075 to 0.3% by weight of gypsum, (b) agitating the same to entrain air and form a froth, (c) adding calcined gypsum and partially expanded thermoplastic particles at a density of less than 3 pounds per cubic foot in a finite amount of up to 3% by weight of gypsum in a controlled manner to obtain a smooth flowable mixture. (d) adding the balance of a predetermined amount of the water, whereby said mixture contains a minimum of water in excess of that required for reaction with said gypsum and only sufficient to obtain a usable flowable mixture required to be able to place said mixture in a means for molding said core.
Claim 19
Dependent Claim
62 words
The process as claimed in claim 13 in which the latex is added in an amount of about 2% by weight of the gypsum, the surfactant and frothing agent are added in a total amount of about 0.1 to 0.2% by weight of the gypsum and the thermoplastic particles are added in an amount of about 2.8% by weight of the gypsum.
References Cited (Backward Citations)
US2965528A
Cited
US3516882A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-05-04 | 1984-11-03 | 1985-05-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-05-04 | 1988-11-03 | 1989-05-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-05-04 | 1992-11-03 | 1993-05-05 | $7700.00 | Window Closed / Lapsed |