US4265937A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method for producing a colored reflective plate having excellent durability and fabricability
Assignee: Taiyo Steel Co Ltd
•
Filing: 1979-05-14
•
Granted: 1981-05-05
•
Expires: 1999-05-14
Abstract
Abstract A colored reflective plate having excellent recurrent reflectivity, durability and fabricability is produced economically with high productivity by subjecting a base plate such as a steel plate, an aluminum plate and a plywood successively to the following treatments: coating and drying a colored paint on the base plate to form a primary colored layer, coating or printing a colored paint on said primary colored layer partially or totally with a thickness in the range from 30 to 80% of the mean radius of glass beads to be coated subsequently thereon, to form an intermediate colored layer, scattering glass beads having a refractive index in the range from 1.9 to 2.1 on the surface of said intermediate layer, removing the excess of glass beads unadhered on said layer, pressing the remaining glass beads in the intermediate colored layer until the beads contact the above mentioned primary colored layer, drying said intermediate layer, further coating a clear paint in the cavities among the glass beads so as to bury the beads in said intermediate and clear paint layers up to a depth from 40 to 80% of the mean diameter of the beads in total after drying, and finally drying and curing the clear paint.
Inventors
- 👤 Toru Kameya
- 👤 Shinichi Makino
- 👤 Masayuki Tsuruta
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 03:38
CPC Classifications
G; G02; G02B; G02B5/00; G02B5/12; G02B5/126; G02B5/128
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
174 words
A method for producing a colored reflective plate comprising coating a colored paint on a base plate to form a primary colored layer, coating or printing a colored paint on said primary colored layer to form an intermediate colored layer in a thickness in a range from 30 to 80% of the mean radius of glass beads to be coated subsequently thereon, scattering glass beads having a refractive index in a range from 1.9 to 2.1 on the surface of said intermediate colored layer, removing the excess of glass beads unadhered on said intermediate colored layer, pressing the remaining glass beads in said intermediate colored layer until said beads contact said primary colored layer, drying said intermediate colored layer, coating a clear paint in the cavities among said glass beads so as to bury said glass beads in said intermediate colored layer and said clear paint up to a depth from 40 to 80% of the mean diameter of said beads as calculated in the dried condition, and drying and curing said clear paint.
Claim 2
Independent Claim
174 words
A method for producing a colored reflective plate comprising coating a colored paint on a base plate to form a primary colored layer, coating or printing a colored paint on said primary colored layer to form an intermediate colored layer in a thickness in a range from 30 to 80% of the mean radius of glass beads to be coated subsequently thereon, scattering glass beads having a refractive index in a range from 1.9 to 2.1 on the surface of said intermediate colored layer, removing the excess of glass beads unadhered on said intermediate colored layer, pressing the remaining glass beads in said intermediate colored layer until said beads contact said primary colored layer, drying said intermediate colored layer, coating a clear paint in the cavities among said glass beads so as to bury said glass beads in said intermediate colored layer and said clear paint up to a depth from 40 to 80% of the mean diameter of said beads as calculated in the dried condition, and drying and curing said clear paint.
Claim 3
Dependent Claim
27 words
A method according to claim 1 in which the base plate is selected from the group consisting of a steel plate, an aluminum plate and a plywood.
Claim 4
Dependent Claim
46 words
A method according to claim 1 in which the colored paints for forming the primary and intermediate colored layers are selected from the group consisting of epoxy resin paint, alkyd resin paint, acrylic resin paint, polyester resin paint, poly-vinyl chloride resin paint and polyurethane resin paint.
Claim 5
Independent Claim
152 words
A method for producing a colored reflective plate comprising coating a transparent colored paint on a bright-finished base plate to form a colored layer in a thickness in a range from 30 to 80% of the mean radius of glass beads to be coated subsequently thereon, scattering glass beads having a refractive index in a range from 1.9 to 2.1 on the surface of said colored layer, removing the excess of glass beads unadhered on said colored layer, pressing the remaining glass beads in said colored layer until said beads contact said base plate, drying said colored layer, coating a clear paint in the cavities among said glass beads so as to bury said glass beads in said colored layer and said clear paint up to a depth from 40 to 80% of the mean diameter of said beads as calculated in the dried condition, and drying and curing said clear paint.
Claim 6
Independent Claim
152 words
A method for producing a colored reflective plate comprising coating a transparent colored paint on a bright-finished base plate to form a colored layer in a thickness in a range from 30 to 80% of the mean radius of glass beads to be coated subsequently thereon, scattering glass beads having a refractive index in a range from 1.9 to 2.1 on the surface of said colored layer, removing the excess of glass beads unadhered on said colored layer, pressing the remaining glass beads in said colored layer until said beads contact said base plate, drying said colored layer, coating a clear paint in the cavities among said glass beads so as to bury said glass beads in said colored layer and said clear paint up to a depth from 40 to 80% of the mean diameter of said beads as calculated in the dried condition, and drying and curing said clear paint.
Claim 7
Dependent Claim
35 words
A method according to claim 4 in which the base plate is selected from the group consisting of a bright-finished aluminum plate, a chromium-plated steel plate, a chromium-coated plastic sheet and an aluminum-coated plastic sheet.
Claim 8
Dependent Claim
16 words
A method according to claim 5 in which the base plate is a bright-finished aluminum plate.
References Cited (Backward Citations)
US3573954A
Cited
US4104102A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-05-04 | 1984-11-03 | 1985-05-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-05-04 | 1988-11-03 | 1989-05-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-05-04 | 1992-11-03 | 1993-05-05 | $7700.00 | Window Closed / Lapsed |