Assignee: Toyobo Co Ltd
•
Filing: 1978-05-23
•
Granted: 1981-04-28
•
Expires: 1998-05-23
Abstract
Abstract A transparent polyester film having excellent antistatic properties, which are little effected with variation of the humidity, and further having excellent flexing resistance, pinhole resistance and printability, which is made from a mixture comprising (i) a polyester consisting essentially of a residue of dibasic acids wherein at least 80% by mol is terephthalic acid and a residue of at least one glycol and (ii) a block copolyester consisting of a crystalline polyester segment having a high melting point and a soft polymer segment having a low melting point and a number average molecular weight of 400 to 8,000, said soft polymer segment having a low melting point being contained in an amount of 0.5 to 10% by weight on the basis of the whole weight of the components (i) and (ii), and (iii) a sulfonic and/or phosphoric acid metal salt having a good heat resistance, and which is produced by melt-extruding the mixture of the components (i), (ii) and (iii), drawing at least uniaxially and then heat-treating the resultant at a temperature of 170° C. or higher and lower than the melting point of the polyester (i).
Inventors
- 👤 Tetsushi Murakami
- 👤 Koichi Matsunami
- 👤 Tsutomu Isaka
- 👤 Yasutomi Yoshino
- 👤 Yukinobu Miyazaki
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 22:52
CPC Classifications
C; C08; C08L; C08L67/00; C08L67/02; Y; Y10; Y10T; Y10T428/00; Y10T428/24; Y10T428/24802; Y10T428/31504; Y10T428/31786
Claims Analysis
Total Claims: 29
Claim 1
Independent Claim
221 words
A polyester film printed with a printing ink for cellulose films, said polyester film being made from a mixture comprising: (1) a polyester consisting essentially of a residue of dibasic acids wherein at least 80% by mol is terephthalic acid and a residue of at least one glycol; (2) A block copolyester consisting of a crystalline polyester segment having a melting point of at least 170° C. when a polymer is produced by the monomers composing this segment alone and a polymer segment having a melting or softening point of 100° C. or lower, said polymer segment having a melting or softening point of 100° C. or lower being contained in an amount of 0.5 to 10% by weight on the basis of the whole weight of the components (1) and (2); and (3) a sulfonic and/or phosphoric acid alkali metal or alkaline earth metal salt having good heat resistance, said sulfonic and/or phosphoric acid metal salt being contained in an amount of 0.05 to 5% by weight on the basis of the whole weight of the components (1), (2), and (3), which is produced by melt-extruding the mixture of the components (1), (2), and (3), drawing at least uniaxially and then heat-treating at a temperature of 170° C. or higher, and lower than the melting point of the polyester (1).
Claim 2
Dependent Claim
221 words
A polyester film printed with a printing ink for cellulose films, said polyester film being made from a mixture comprising: (1) a polyester consisting essentially of a residue of dibasic acids wherein at least 80% by mol is terephthalic acid and a residue of at least one glycol; (2) A block copolyester consisting of a crystalline polyester segment having a melting point of at least 170° C. when a polymer is produced by the monomers composing this segment alone and a polymer segment having a melting or softening point of 100° C. or lower, said polymer segment having a melting or softening point of 100° C. or lower being contained in an amount of 0.5 to 10% by weight on the basis of the whole weight of the components (1) and (2); and (3) a sulfonic and/or phosphoric acid alkali metal or alkaline earth metal salt having good heat resistance, said sulfonic and/or phosphoric acid metal salt being contained in an amount of 0.05 to 5% by weight on the basis of the whole weight of the components (1), (2), and (3), which is produced by melt-extruding the mixture of the components (1), (2), and (3), drawing at least uniaxially and then heat-treating at a temperature of 170° C. or higher, and lower than the melting point of the polyester (1).
Claim 3
Dependent Claim
66 words
The polyester film according to claim 1, wherein the block copolyester is a polyester comprising a crystalline polyester segment having a metling point of at least 170° C. when a polymer is produced by the monomers composing this segment alone and a polymer segment having a melting point or softening point of 100° C. or lower and a number average molecular weight of 400 to 8,000.
Claim 4
Dependent Claim
113 words
The polyester film according to claim 1, wherein the sulfonic acid metal salt is a compound of the formula: R.sub.1 --SO.sub.3 Me wherein R 1 is an alkyl, aryl, aralkyl or alkylaryl having 8 to 20 carbon atoms, or the group: --(R 4 O) p --R 5 wherein R 4 is a divalent saturated hydrocarbon group having 2 to 4 carbon atoms, R 5 is an alkyl, aryl, aralkyl or alkylaryl having 8 to 20 carbon atoms, and p is such a numeral that the molecular weight of the chain: --(R 4 O)-- is included in the range of 32 to 2000; and Me is an alkali metal or an alkaline earth metal.
Claim 5
Dependent Claim
16 words
The polyester film according to claim 3, wherein the sulfonic acid metal salt is sodium dodecylbenzenesulfonate.
Claim 6
Dependent Claim
16 words
The polyester film according to claim 3, wherein the sulfonic acid metal salt is sodium stearylsulfonate.
Claim 7
Dependent Claim
25 words
The polyester film according to claim 3, wherein the sulfonic acid metal salt is sodium alkylsulfonate having an average carbon number of 8 to 20.
Claim 8
Dependent Claim
205 words
The polyester film according to claim 1, wherein the phosphoric acid metal salt is a compound of the formula: ##STR16## wherein R 1 is an alkyl, aryl, aralkyl or alkylaryl having 8 to 20 carbon atoms, or the group: --(R 4 O) p --R 5 wherein R 4 is a divalent saturated hydrocarbon group having 2 to 4 carbon atoms, R 5 is an alkyl, aryl, aralkyl or alkylaryl having 8 to 20 carbon atoms, and p is such a numeral that the molecular weight of the chain: --(R 4 O)-- is included in the range of 32 to 2000; Me is an alkali metal or an alkaline earth metal; X is hydrogen or the group R 1 or Me above-mentioned, when two groups of R 1 or Me are present, they may be the same or different from each other; l and m are each such a numeral that the molecular weight of the chain: --(OR 2 )-- or --(R 3 0)-- is included in the range of 32 to 2000, respectively; n is an integer of 2 to 50; and R 2 and R 3 are the same or different, and are each a saturated hydrocarbon group having 2 to 4 carbon atoms.
Claim 9
Dependent Claim
32 words
The polyester film according to claim 7, wherein the phosphoric acid metal salt is a compound of the formula: ##STR17## wherein R 5 is an alkyl having 8 to 20 carbon atoms.
Claim 10
Dependent Claim
35 words
The polyester film according to claim 7, wherein the phosphoric acid metal salt is a mixture of the compounds of the formulae: ##STR18## wherein R 5 is an alkyl having 8 to 20 carbon atoms.
Claim 11
Dependent Claim
32 words
The polyester film according to claim 1, wherein the crystalline polyester segment is a segment comprising predominantly a polyester consisting of a residue of terephthalic acid and a residue of ethylene glycol.
Claim 12
Dependent Claim
22 words
The polyester film according to claim 1, wherein the metal of the sulfonic and/or phosphoric acid metal salt is sodium or potassium.
Claim 13
Dependent Claim
32 words
The polyester film according to claim 1, wherein the crystalline polyester segment is a segment comprising predominantly a polyester consisting of a residue of terephthalic acid and a residue of tetramethylene glycol.
Claim 14
Dependent Claim
35 words
The polyester film according to claim 1, wherein the crystalline polyester segment is a segment comprising predominantly a polyester consisting of a residue of terephthalic acid and isophthalic acid and a residue of ethylene glycol.
Claim 15
Dependent Claim
35 words
The polyester film according to claim 1, wherein the crystalline polyester segment is a segment comprising predominantly a polyester consisting of a residue of terephthalic acid and isophthalic acid and a residue of tetramethylene glycol.
Claim 16
Dependent Claim
34 words
The polyester film according to claim 1 wherein the polymer segment having a melting or softening point of 100° C. or lower is polyethylene oxide glycol having a molecular weight of 400 to 8000.
Claim 17
Dependent Claim
34 words
The polyester film according to claim 1 wherein the polymer segment having a melting or softening point of 100° C. or lower is polytetramethylene oxide glycol having a molecular weight of 400 to 8000.
Claim 18
Dependent Claim
17 words
The polyester film according to claim 1, wherein the block copolyester is polyethylene terephthalate-polyethylene oxide block copolymer.
Claim 19
Dependent Claim
17 words
The polyester film according to claim 1, wherein the block copolyester is polytetramethylene terephthalate-polytetramethylene oxide block copolymer.
Claim 20
Dependent Claim
18 words
The polyester film according to claim 1, wherein the block copolyester is polytetramethylene terephthalate isophthalate-polytetramethylene oxide block copolymer.
Claim 21
Dependent Claim
17 words
The polyester film according to claim 1, wherein the block copolyester is polytetramethylene terephthalate-polyethylene oxide block copolymer.
Claim 22
Dependent Claim
14 words
The polyester film according to claim 1, wherein the polyester (i) is polyethylene terephthalate.
Claim 23
Dependent Claim
14 words
The polyester film according to claim 1, wherein the polyester (i) is polytetramethylene terephthalate.
Claim 24
Dependent Claim
28 words
The polyester film according to claim 1, wherein the mixed ratio of the polyester and the block copolyester is in the range of 99.4:0.6 to 20:80 by weight.
Claim 25
Dependent Claim
17 words
The polyester film according to claim 1, which is drawn 1.2 to 6 times at least uniaxially.
Claim 26
Dependent Claim
18 words
The polyester film according to claim 1, which is drawn perpendicularly and laterally 1.2 to 6 times, respectively.
Claim 27
Dependent Claim
21 words
The polyester film according to claim 1, which is drawn biaxially 1.2 to 6 times, respectively, at 60° to 120° C.
Claim 28
Dependent Claim
15 words
The polyester film according to claim 26, wherein the biaxial drawing is carried out successively.
Claim 29
Dependent Claim
24 words
The polyester film according to claim 1, wherein the heat treatment of the drawn film is carried out for 0.1 second to 5 minutes.
References Cited (Backward Citations)
US2823421A
Cited
US3652713A
Cited
US3702350A
Cited
US4064312A
Cited
US3970729A
Cited
US4061615A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-04-27 | 1984-10-27 | 1985-04-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-04-27 | 1988-10-27 | 1989-04-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-04-27 | 1992-10-27 | 1993-04-28 | $7700.00 | Window Closed / Lapsed |