Adhesive products having polymer-treated embrittled zones
Assignee: Avery Dennison Corp
•
Filing: 1978-10-02
•
Granted: 1981-04-28
•
Expires: 1998-10-02
Abstract
Abstract Adhesive products such as label stock, labels, tapes, and the like having a facestock, an adhesive layer and a removable, fibrous backing are described. The backing is provided with integral embrittled zones which crack when the adhesive product is flexed and offer gripping points for removal of the backing. The embrittled zones contain brittle, film-forming organic polymer suffused among the fibers. The presence of the polymer in the embrittled zone helps to enhance the brittleness of the zones and to reduce the transfer of residual chemical embrittling agent from embrittled zones of the backing to portions of the facestock brought into contact therewith when the adhesive product is stacked or rolled. Embrittled zones are preferably formed by applying a thickened acidic solution comprising a polymer emulsion to the backing of the adhesive product and then curing and drying the solution by heating.
Inventors
- 👤 Benjamin J. Taylor
- 👤 Robert M. Lacy
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 06:43
CPC Classifications
C; C09; C09J; C09J7/00; C09J7/20; Y; Y10; Y10S; Y10S206/00; Y10S206/813; Y10T; Y10T428/00; Y10T428/14; Y10T428/1424; Y10T428/1462; Y10T428/15; Y10T428/24; Y10T428/24802; Y10T428/24934
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
75 words
An adhesive laminate comprising a facestock, an adhesive layer on the facestock, and a removable fibrous paper backing in contact with the adhesive layer, the paper backing having at least one narrow embrittled zone integrally included in the paper backing comprising an organic, brittle film-forming polymer within the fibrous paper backing said film-forming polymer being selected from the group consisting of polyvinyl chloride, polyvinyl alcohol, polyvinyl acetate, polystyrene acrylate, and thermoplastic and self-cross-linking acrylic polymers.
Claim 2
Dependent Claim
75 words
An adhesive laminate comprising a facestock, an adhesive layer on the facestock, and a removable fibrous paper backing in contact with the adhesive layer, the paper backing having at least one narrow embrittled zone integrally included in the paper backing comprising an organic, brittle film-forming polymer within the fibrous paper backing said film-forming polymer being selected from the group consisting of polyvinyl chloride, polyvinyl alcohol, polyvinyl acetate, polystyrene acrylate, and thermoplastic and self-cross-linking acrylic polymers.
Claim 3
Dependent Claim
30 words
An adhesive laminate according to claim 1 wherein the embrittled zone comprises residual chemical embrittling agent and the polymer retards transfer of residual chemical embrittling agent from the embrittled zone.
Claim 4
Dependent Claim
26 words
An adhesive laminate according to claim 2 wherein the backing is paper, the residual embrittling agent comprises hydrogen chloride, and the polymer is a poly(vinyl acetate).
Claim 5
Dependent Claim
20 words
An adhesive laminate according to claim 1 or claim 2 wherein the polymer enhances the brittleness of the embrittled zone.
Claim 6
Dependent Claim
19 words
An adhesive laminate according to claim 1 wherein substantially all of the polymer present is within the embrittled zone.
Claim 7
Dependent Claim
133 words
A process for the production for an adhesive laminate comprising a facestock, an adhesive layer on the facestock, and a removable fibrous paper backing, with the fibrous paper backing having at least one embrittled zone, the process comprising the steps of: a. applying to a portion of the fibrous paper backing an aqueous embrittling solution containing 1 to 15 weight percent hydrogen chloride, 0.5 to 3 weight percent organic thickener, and 1 to 10 weight percent organic, brittle film-forming polymer in emulsion form, said film-forming polymer being selected from the group consisting of polyvinyl chloride, polyvinyl alcohol, polyvinyl acetate, polystyrene acrylate, and thermoplastic and self-cross-linking acrylic polymers and b. curing and drying the applied solution at 150° to 250° C. to form an embrittled zone comprising said polymer integrated within the paper backing.
Claim 8
Dependent Claim
133 words
A process for the production for an adhesive laminate comprising a facestock, an adhesive layer on the facestock, and a removable fibrous paper backing, with the fibrous paper backing having at least one embrittled zone, the process comprising the steps of: a. applying to a portion of the fibrous paper backing an aqueous embrittling solution containing 1 to 15 weight percent hydrogen chloride, 0.5 to 3 weight percent organic thickener, and 1 to 10 weight percent organic, brittle film-forming polymer in emulsion form, said film-forming polymer being selected from the group consisting of polyvinyl chloride, polyvinyl alcohol, polyvinyl acetate, polystyrene acrylate, and thermoplastic and self-cross-linking acrylic polymers and b. curing and drying the applied solution at 150° to 250° C. to form an embrittled zone comprising said polymer integrated within the paper backing.
Claim 9
Dependent Claim
75 words
A process for the production of an adhesive laminate comprising a facestock, an adhesive layer on the facestock, and a removable fibrous paper backing in contact with the adhesive layer in which at least one integral embrittled zone is formed in the paper backing, comprising introducing into the embrittled zone an organic, brittle film-forming polymer selected from the group consisting of polyvinyl chloride, polyvinyl alcohol, polyvinyl acetate, polystyrene acrylate, and thermoplastic and self-cross-linking acrylic polymers.
Claim 10
Dependent Claim
75 words
A process for the production of an adhesive laminate comprising a facestock, an adhesive layer on the facestock, and a removable fibrous paper backing in contact with the adhesive layer in which at least one integral embrittled zone is formed in the paper backing, comprising introducing into the embrittled zone an organic, brittle film-forming polymer selected from the group consisting of polyvinyl chloride, polyvinyl alcohol, polyvinyl acetate, polystyrene acrylate, and thermoplastic and self-cross-linking acrylic polymers.
Claim 11
Dependent Claim
27 words
A process according to claim 7 wherein the polymer is introduced by applying a solution of polymer in solvent to the embrittled zone and removing the solvent.
Claim 12
Dependent Claim
28 words
A process according to claim 7 wherein the polymer is introduced by applying an aqueous emulsion of the polymer to the embrittled zone and drying the applied emulsion.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-04-27 | 1984-10-27 | 1985-04-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-04-27 | 1988-10-27 | 1989-04-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-04-27 | 1992-10-27 | 1993-04-28 | $7700.00 | Window Closed / Lapsed |