Method of fabricating optical fiber preforms
Assignee: Mitsubishi Materials Corp
•
Filing: 1979-11-15
•
Granted: 1981-04-28
•
Expires: 1999-11-15
Abstract
Abstract An improved method of preparing optical fiber preforms and optical fibers by so called rod-in-tube method, wherein before collapsing a tube to heat-adhere to a rod, a specific glass surface treating agent and oxygen gas are flowed through the clearance between the rod and the tube maintained at a high temperature, whereby an optical fiber preform free from imperfections at the interface between the rod and the tube can be produced so as to give optical fibers of low-loss. As the above glass surface treating agent, those materials are employed which satisfy the following criteria: (i) the hydrogen content thereof being not more than about 1% by weight, and (ii) the substances, produced therefrom in the presence of oxygen gas at a high temperature, having a boiling point or sublimation point of not more than the temperature required for collapsing the tube.
Inventors
- 👤 Takeshi Shintani
- 👤 Atsushi Utsumi
- 👤 Tadaaki Sukawa
- 👤 Ryuji Kobayashi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 17:52
CPC Classifications
C; C03; C03B; C03B37/00; C03B37/01; C03B37/012; C03B37/01205; C03B37/01211; C03B37/02; C03B37/025; C03B37/027; C03C; C03C15/00; C03C23/00; C03B2201/00; C03B2201/06; C03B2201/08; C03B2201/10; C03B2201/14; Y; Y02; Y02P; Y02P40/00; Y02P40/50; Y02P40/57; Y10; Y10S; Y10S65/00; Y10S65/15; Y10S65/16
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
192 words
In a method of fabricating an optical fiber preform by inserting a silicate glass rod into a silicate glass tube and collapsing the tube by heating the resulting assembly, the improvement which comprises, before the tube is collapsed flowing a glass surface treating agent and oxygen gas through the clearance between the rod and the tube while the assembly is heated at a high temperature to produce substances which effect removal of foreign material and cure of surface defects on the surfaces of said rod and tube; said glass surface treating agent: (a) satisfying the following criteria: (i) the hydrogen content thereof being not more than about 1% by weight, and (ii) the substances produced therefrom in the presence of oxygen gas at the high temperature having a boiling point or sublimation point of not more than the temperature required for collapsing the tube so that the substances are substantially removed from the clearance between the surfaces of the rod and the tube before or during collapsing of the tube, and (b) being employed in an amount of at least 0.1 part by volume per 100 parts by volume of oxygen gas.
Claim 2
Dependent Claim
192 words
In a method of fabricating an optical fiber preform by inserting a silicate glass rod into a silicate glass tube and collapsing the tube by heating the resulting assembly, the improvement which comprises, before the tube is collapsed flowing a glass surface treating agent and oxygen gas through the clearance between the rod and the tube while the assembly is heated at a high temperature to produce substances which effect removal of foreign material and cure of surface defects on the surfaces of said rod and tube; said glass surface treating agent: (a) satisfying the following criteria: (i) the hydrogen content thereof being not more than about 1% by weight, and (ii) the substances produced therefrom in the presence of oxygen gas at the high temperature having a boiling point or sublimation point of not more than the temperature required for collapsing the tube so that the substances are substantially removed from the clearance between the surfaces of the rod and the tube before or during collapsing of the tube, and (b) being employed in an amount of at least 0.1 part by volume per 100 parts by volume of oxygen gas.
Claim 3
Dependent Claim
37 words
The method of claim 1, wherein the glass surface treating agent and oxygen gas are flowed while the assembly is heated at a temperature of at least about 1,000° C. at the outer surface of the tube.
Claim 4
Dependent Claim
25 words
The method of claim 1 or 2, wherein the hydrogen content of the glass surface treating agent is not more than about 0.1% by weight.
Claim 5
Dependent Claim
224 words
In a method of fabricating an optical fiber preform by inserting a silicate glass rod into a silicate glass tube and collapsing the tube by heating the resulting assembly, the improvement which comprises, before the tube is collapsed, flowing a glass surface treating agent and oxygen gas through the clearance between the rod and the tube while the assembly is heated at a high temperature to produce substances which effect removal of foreign material and cure of surface defects on the surfaces of said rod and tube; said glass surface treating agent: (a) satisfying the following criteria: (i) the hydrogen content thereof being not more than about 1% by weight, and (ii) the substances produced therefrom in the presence of oxygen gas at the high temperature having a boiling point or sublimation point of not more than the temperature required for collapsing the tube so that the substances are substantially removed from the clearance between the surfaces of the rod and the tube before or during collapsing of the tube, (b) being employed in an amount of at least 0.1 part by volume per 100 parts by volume of oxygen gas, and (c) containing at least one element selected from the group consisting of elements capable of forming a glass network forming oxide, elements capable of forming a glass modifying oxide, halogens and sulfur.
Claim 6
Dependent Claim
224 words
In a method of fabricating an optical fiber preform by inserting a silicate glass rod into a silicate glass tube and collapsing the tube by heating the resulting assembly, the improvement which comprises, before the tube is collapsed, flowing a glass surface treating agent and oxygen gas through the clearance between the rod and the tube while the assembly is heated at a high temperature to produce substances which effect removal of foreign material and cure of surface defects on the surfaces of said rod and tube; said glass surface treating agent: (a) satisfying the following criteria: (i) the hydrogen content thereof being not more than about 1% by weight, and (ii) the substances produced therefrom in the presence of oxygen gas at the high temperature having a boiling point or sublimation point of not more than the temperature required for collapsing the tube so that the substances are substantially removed from the clearance between the surfaces of the rod and the tube before or during collapsing of the tube, (b) being employed in an amount of at least 0.1 part by volume per 100 parts by volume of oxygen gas, and (c) containing at least one element selected from the group consisting of elements capable of forming a glass network forming oxide, elements capable of forming a glass modifying oxide, halogens and sulfur.
Claim 7
Dependent Claim
19 words
The method of claim 4, wherein the glass surface treating agent contains at least one of boron and phosphorus.
Claim 8
Dependent Claim
19 words
The method of claim 4, wherein the glass surface treating agent contains at least one of halogens and sulfur.
Claim 9
Dependent Claim
16 words
The method of claim 6, wherein the glass surface treating agent is a compound containing fluorine.
Claim 10
Dependent Claim
42 words
The method of claim 3 wherein the glass surface treating agent contains at least one element selected from the group consisting of elements capable of forming a glass network forming oxide, elements capable of forming a glass modifying oxide, halogens and sulfur.
Claim 11
Dependent Claim
19 words
The method of claim 8 wherein the glass surface treating agent contains at least one of boron and phosphorus.
Claim 12
Dependent Claim
19 words
The method of claim 8 wherein the glass surface treating agent contains at least one of halogens and sulfur.
Claim 13
Dependent Claim
16 words
The method of claim 10 wherein the glass surface treating agent is a compound containing fluorine.
Claim 14
Dependent Claim
26 words
The method of claim 1, wherein the substance formed from the glass treating agent in the presence of oxygen at the high temperature is an oxide.
Claim 15
Dependent Claim
37 words
The method of claim 4, wherein the glass surface treating agent is at least one member selected from the group consisting of boron halides, phosphorus halides, arsenic halides, antimony halides, phosphorus oxyhalides, halogens, sulfur halides, and chlorofluorocarbons.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-04-27 | 1984-10-27 | 1985-04-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-04-27 | 1988-10-27 | 1989-04-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-04-27 | 1992-10-27 | 1993-04-28 | $7700.00 | Window Closed / Lapsed |