US4263373A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method of making an ultra thin glue adherable decorative laminate
Assignee: International Paper Co
•
Filing: 1977-05-24
•
Granted: 1981-04-21
•
Expires: 1997-05-24
Abstract
Abstract An ultra thin laminate is made by: (1) assembling a laminate stack-up consisting of: one paper sheet having a top decorative surface and a bottom surface coated with a resinous film, about 0.25 mil to about 5 mil thick, effective to opacify the paper and provide a barrier to resin flow, and one abrasion resistant protective overlay sheet disposed in contact with the decorative surface of the paper sheet; (2) heat and pressure consolidating the stack-up to form a unitary decorative laminate having a thickness of between about 5 mil and about 15 mil, and having a resinous film on one side that is glue adherable.
Inventors
- 👤 Harold O. McCaskey, Jr.
- 👤 Daniel L. Cannady, Jr.
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 01:19
CPC Classifications
B; B32; B32B; B32B38/00; B32B38/08; B32B7/00; B32B7/04; B32B7/12; B44; B44C; B44C1/00; B44C1/10; B44C1/105; B44C5/00; B44C5/04; B44C5/0469; B44C5/0476; D; D21; D21H; D21H27/00; D21H27/18; D21H27/22; D21H27/26; D21H5/00; D21H5/0085; D21H5/009; B32B2260/00; B32B2260/02; B32B2260/028; B32B2307/00; B32B2307/50; B32B2307/554; B32B2317/00; B32B2317/12; B32B2451/00; Y; Y10; Y10T; Y10T428/00; Y10T428/31504; Y10T428/31942; Y10T428/31949; Y10T428/31964; Y10T428/31967; Y10T428/31971; Y10T428/31975; Y10T428/31978; Y10T428/31982
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
200 words
A method of making an ultra thin, glue adherable, high pressure decorative thermoset veneer laminate, comprising the steps of: (A) assembling a laminate stack-up consisting of: (1) one thermosetting resin impregnated paper sheet having a top decorative surface, and a bottom surface coated with an alginate resinous film, about 0.25 mil to about 5 mil thick, to an alginate content of from between about 2 weight percent and about 40 weight percent of the coated paper sheet, said film being effective to opacify the paper sheet and provide a barrier to resin flow, and (2) one thermosetting resin impregnated abrasion resistant, protective overlay sheet disposed in contact with the decorative surface of the paper sheet, (B) placing the stack-up in a press and molding the stack-up at temperatures of between about 100° C. and about 200° C. and pressures of between about 500 psi. and about 2,000 psi., and (C) cooling and releasing the press and removing the stack-up; wherein the stack-up is heat and pressure consolidated to form a unitary decorative laminate, the laminate having a thickness of between about 5 mil and about 15 mil and a resinous film on one side that is glue adherable without sanding.
Claim 2
Independent Claim
200 words
A method of making an ultra thin, glue adherable, high pressure decorative thermoset veneer laminate, comprising the steps of: (A) assembling a laminate stack-up consisting of: (1) one thermosetting resin impregnated paper sheet having a top decorative surface, and a bottom surface coated with an alginate resinous film, about 0.25 mil to about 5 mil thick, to an alginate content of from between about 2 weight percent and about 40 weight percent of the coated paper sheet, said film being effective to opacify the paper sheet and provide a barrier to resin flow, and (2) one thermosetting resin impregnated abrasion resistant, protective overlay sheet disposed in contact with the decorative surface of the paper sheet, (B) placing the stack-up in a press and molding the stack-up at temperatures of between about 100° C. and about 200° C. and pressures of between about 500 psi. and about 2,000 psi., and (C) cooling and releasing the press and removing the stack-up; wherein the stack-up is heat and pressure consolidated to form a unitary decorative laminate, the laminate having a thickness of between about 5 mil and about 15 mil and a resinous film on one side that is glue adherable without sanding.
Claim 3
Dependent Claim
37 words
The method of claim 1, wherein the resinous film coating on the paper sheet is an alginate film selected from the group consisting of sodium alginate, potassium alginate, iron alginate, ammonium alginate, lithium alginate and mixtures thereof.
Claim 4
Dependent Claim
38 words
The method of claim 1, wherein the paper sheet has a printed decorative surface, is about 3 mil to about 10 mil thick and the stack-up is molded for about 15 minutes to about 60 minutes before cooling.
Claim 5
Dependent Claim
21 words
The method of claim 1, wherein the abrasion resistant protective overlay sheet is about 2 mil to about 5 mil thick.
Claim 6
Dependent Claim
23 words
The method of claim 4, wherein the overlay sheet is paper sheet and the decorative paper sheet is impregnated with a phenolic resin.
Claim 7
Dependent Claim
34 words
The method of claim 4 also including the additional steps of applying an adhesive directly to the alginate film and glueing the decorative laminate to a thick support to form an adhesive bonded composite.
Claim 8
Dependent Claim
10 words
The decorative laminate made by the method of claim 4.
References Cited (Backward Citations)
US1597539A
Cited
US2118549A
Cited
US2631960A
Cited
US3075863A
Cited
US3050434A
Cited
US3135643A
Cited
US3378433A
Cited
US3418189A
Cited
US3547767A
Cited
US3620899A
Cited
US3756901A
Cited
US3701706A
Cited
US3995090A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-04-20 | 1984-10-20 | 1985-04-21 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-04-20 | 1988-10-20 | 1989-04-21 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-04-20 | 1992-10-20 | 1993-04-21 | $7700.00 | Window Closed / Lapsed |