Homogeneous predispersed fiber compositions

Claim 2

A substantially homogeneous predispersed fiber composition useful for dispersing a fibrous material in a rubber or plastic compound stock, said composition comprising a fibrous material and a rubber or plastic polymer binder, wherein said composition is prepared by mixing a latex of the rubber or plastic polymer with the fibrous material to form a wetted fiber mixture, mixing a coagulant with the wetted fiber mixture thereby forming said fiber composition, wherein the percent of total solids in the wetted fiber mixture prior to coagulation which will result in the formation of said fiber composition is determined by first preparing several test predispersed fiber compositions having the same compositions as that desired from several test wetted fiber mixtures, each of which has a different percent of total solids decreasing in equal increments from the point at which the total amount of water present in one of the test wetted fiber mixtures prior to coagulation is substantially equal to that required to completely wet the fibrous material by either capillary action, surface adsorption, or a combination thereof, from each of the several test fiber compositions obtained, a sufficient number of samples of approximately equal weight are analyzed to determine the percent of fibrous material present in each of the samples and to determine the standard deviation in the percent of fibrous material for each of the test fiber compositions, plotting a curve of the standard deviations obtained versus the percent of total solids in the test wetted fiber mixtures used to prepare each of the test fiber compositions, and then selecting a percent of total solids for the wetted fiber mixture prior to coagulation which corresponds to a point on the homogeneous portion of the curve wherein the homogeneity of the test fiber compositions is substantially equal to that obtained at the point where the total amount of water present in one of the test wetted fiber mixtures prior to coagulation is substantially equal to that required to completely wet the fibrous material by either capillary action, surface adsorption, or a combination thereof.

Claim 3

The composition of claim 1 wherein the fibrous material comprises greater than about 50 percent by weight of the composition.

Claim 4

The composition of claim 2 wherein the fibrous material comprises from about 75 to about 95 percent by weight of the composition.

Claim 5

The composition of claim 1 wherein the binder further comprises a plasticizer for the binder.

Claim 6

The composition of claim 1 wherein the binder further comprises a compound which promotes adhesion between the fibrous material and the rubber or plastic compound stock.

Claim 7

The composition of claim 4 wherein the binder further comprises a compound which promotes adhesion between the fibrous material and the rubber or plastic compound stock.

Claim 8

The composition of claim 1 wherein the binder further comprises an antidegradant for the binder.

Claim 9

The composition of claim 4 wherein the binder further comprises an antidegradant for the binder.

Claim 10

The composition of claim 5 wherein the binder further comprises an antidegradant for the binder.

Claim 11

The composition of claim 6 wherein the binder further comprises an antidegradant for the binder.

Claim 12

The composition of claim 1 wherein the fibrous material is selected from the group consisting of rayon, polyester, cotton, asbestos and glass, semisynthetic fibers.

Claim 13

The composition of claim 1 wherein the rubber or plastic polymer binder comprises a rubber or plastic polymer prepared by an emulsion polymerization process.

Claim 14

The composition of claim 12 wherein the rubber or plastic polymer is selected from the group consisting of (a) natural rubber, (b) polybutadiene, (c) copolymers of butadiene and one or more comonomers selected from styrene, acrylonitrile, methylmethacrylate, vinylpyridine or a derivative thereof, and a carboxylic acid, (d) polyisoprene, (e) polychloroprene, (f) copolymers of vinyl acetate and ethylene, (g) butyl rubber, (h) polyisobutylene, (i) poly(vinyl chloride), (j) poly(vinyl chloride-vinylidene chloride), (k) poly(vinylidene chloride), (l) acrylonitrile-butadiene-styrene copolymer and (m) styrene-acrylonitrile copolymer.

Claim 15

The composition of claim 1 wherein the rubber or plastic polymer binder comprises a rubber or plastic polymer prepared by a solution polymerization process.

Claim 16

The composition of claim 14 wherein the rubber or plastic polymer is selected from the group consisting of (a) EPDM, (b) EPR, (c) oxidized polyethylene, (d) block copolymers of styrene and butadiene, and (e) thermoplastic rubbers.

Claim 17

A substantially homogeneous predispersed fiber composition useful for dispersing a fibrous material in a rubber or plastic compound stock, said composition comprising a fibrous material and a rubber or plastic polymer binder, wherein said composition is prepared by mixing a latex of the rubber or plastic polymer with the fibrous material to form a wetted fiber mixture, mixing a coagulant with the wetted fiber mixture thereby forming said fiber composition, wherein the percent of total solids in the wetted fiber mixture prior to coagulation which will result in the formation of said fiber composition is determined by first preparing several test predispersed fiber compositions having the same composition as that desired from several test wetted fiber mixtures, each of which has a different percent of total solids decreasing in equal increments from the point at which the total amount of water present in one of the test wetted fiber mixtures prior to coagulation is substantially equal to that required to completely wet the fibrous material by either capillary action, surface adsorption or a combination thereof, from each of the several test fiber compositions obtained, a sufficient number of samples of approximately equal weight are analyzed to determine the percent of fibrous material present in each of the samples and to determine the standard deviation in the percent of fibrous material for each of the test fiber compositions, plotting a curve of the standard deviations obtained versus the percent of total solids in the test wetted fiber mixtures used to prepare each of the test fiber compositions, and then selecting a percent of total solids for the wetted fiber mixture prior to coagulation which corresponds to a point on the portion of the curve which extends from the point where the total amount of water present in one of the test wetted fiber mixtures prior to coagulation is substantially equal to that required to completely wet the fibrous material by either capillary action, surface adsorption, or a combination thereof to the inflection point.

Claim 18

A substantially homogeneous predispersed fiber composition useful for dispersing a fibrous material in a rubber or plastic compound stock, said composition comprising a fibrous material and a rubber or plastic polymer binder, wherein said composition is prepared by mixing a latex of the rubber or plastic polymer with the fibrous material to form a wetted fiber mixture, mixing a coagulant with the wetted fiber mixture thereby forming said fiber composition, wherein the percent of total solids in the wetted fiber mixture prior to coagulation which will result in the formation of said fiber composition is determined by first preparing several test predispersed fiber compositions having the same composition as that desired from several test wetted fiber mixtures, each of which has a different percent of total solids decreasing in equal increments from the point at which the total amount of water present in one of the test wetted fiber mixtures prior to coagulation is substantially equal to that required to completely wet the fibrous material by either capillary action, surface adsorption or a combination thereof, from each of the several test fiber compositions obtained, a sufficient number of samples of approximately equal weight are analyzed to determine the percent of fibrous material present in each of the samples and to determine the standard deviation in the percent of fibrous material for each of the test fiber compositions, plotting a curve of the standard deviations obtained versus the percent of total solids in the test wetted fiber mixtures used to prepare each of the test fiber compositions, and then selecting a percent of total solids for the wetted fiber mixture prior to coagulation which corresponds to a point on the portion of the curve which extends from the point where the total amount of water present in one of the test wetted fiber mixtures prior to coagulation is substantially equal to that required to completely wet the fibrous material by either capillary action, surface adsorption, or a combination thereof to the inflection point.

Claim 19

The composition of claim 16 wherein the fibrous material comprises greater than about 50 percent by weight of the composition.

Claim 20

The composition of claim 17 wherein the fibrous material comprises from about 75 to about 95 percent by weight of the composition.

Claim 21

The composition of claim 16 wherein the binder further comprises a plasticizer for the binder.

Claim 22

The composition of claim 16 wherein the binder further comprises a compound which promotes adhesion between the fibrous material and the rubber or plastic compound stock.

Claim 23

The composition of claim 19 wherein the binder further comprises a compound which promotes adhesion between the fibrous material and the rubber or plastic compound stock.

Claim 24

The composition of claim 16 wherein the binder further comprises an antidegradant for the binder.

Claim 25

The composition of claim 19 wherein the binder further comprises an antidegradant for the binder.

Claim 26

The composition of claim 20 wherein the binder further comprises an antidegradant for the binder.

Claim 27

The composition of claim 21 wherein the binder further comprises an antidegradant for the binder.

Claim 28

The composition of claim 16 wherein the fibrous material is selected from the group consisting of rayon, polyester, cotton, asbestos and glass fibers.

Claim 29

The composition of claim 16 wherein the rubber or plastic polymer binder comprises a rubber or plastic polymer prepared by an emulsion polymerization process.

Claim 30

The composition of claim 27 wherein the rubber or plastic polymer is selected from the group consisting of (a) natural rubber, (b) polybutadiene, (c) copolymers of butadiene and one or more comonomers selected from styrene, acrylonitrile, methylmethacrylate, vinylpyridine or a derivative thereof, and a carboxylic acid, (d) polyisoprene, (e) polychloroprene, (f) copolymers of vinyl acetate and ethylene, (g) butyl rubber, (h) polyisobutylene, (i) poly(vinyl chloride), (j) poly(vinyl chloride-vinylidene chloride), (k) poly(vinylidene chloride), (l) acrylonitrile-butadiene-styrene copolymer and (m) styrene-acrylonitrile copolymer.

Claim 31

The composition of claim 16 wherein the rubber or plastic polymer binder comprises a rubber or plastic polymer prepared by a solution polymerization process.

Claim 32

The composition of claim 29 wherein the rubber or plastic polymer is selected from the group consisting of (a) EPDM, (b) EPR, (c) oxidized polyethylene, (d) block copolymers of styrene and butadiene, and (e) thermoplastic rubbers.

Claim 33

A substantially homogeneous predispersed fiber composition useful for dispersing a fibrous material in a rubber or plastic polymer binder, wherein said composition is prepared by mixing a latex of the rubber or plastic polymer with the fibrous material to form a wetted fiber mixture, mixing a coagulant with the wetted fiber mixture thereby forming said fiber composition, wherein the percent of total solids in the wetted fiber mixture prior to coagulation which will result in the formation of said fiber composition is determined by first preparing several test predispersed fiber compositions having the same composition as that desired from several test wetted fiber mixtures, each of which has a different percent of total solids decreasing in equal increments from the point at which the total amount of water present in one of the test wetted fiber mixtures prior to coagulation is substantially equal to that required to completely wet the fibrous material by either capillary action, surface adsorption, or a combination thereof, from each of the several test fiber compositions obtained, a sufficient number of samples of approximately equal weight are analyzed to determine the percent of fibrous material present in each of the samples and to determine the standard deviation in the percent of fibrous material for each of the test fiber compositions, plotting a curve of the standard deviations obtained versus the percent of total solids in the test wetted fiber mixtures used to prepare each of the test fiber compositions, and then selecting a percent of total solids for the wetted fiber mixture prior to coagulation which corresponds to a point on the curve at which the value of the standard deviation is less than about 3.

Claim 34

A substantially homogeneous predispersed fiber composition useful for dispersing a fibrous material in a rubber or plastic polymer binder, wherein said composition is prepared by mixing a latex of the rubber or plastic polymer with the fibrous material to form a wetted fiber mixture, mixing a coagulant with the wetted fiber mixture thereby forming said fiber composition, wherein the percent of total solids in the wetted fiber mixture prior to coagulation which will result in the formation of said fiber composition is determined by first preparing several test predispersed fiber compositions having the same composition as that desired from several test wetted fiber mixtures, each of which has a different percent of total solids decreasing in equal increments from the point at which the total amount of water present in one of the test wetted fiber mixtures prior to coagulation is substantially equal to that required to completely wet the fibrous material by either capillary action, surface adsorption, or a combination thereof, from each of the several test fiber compositions obtained, a sufficient number of samples of approximately equal weight are analyzed to determine the percent of fibrous material present in each of the samples and to determine the standard deviation in the percent of fibrous material for each of the test fiber compositions, plotting a curve of the standard deviations obtained versus the percent of total solids in the test wetted fiber mixtures used to prepare each of the test fiber compositions, and then selecting a percent of total solids for the wetted fiber mixture prior to coagulation which corresponds to a point on the curve at which the value of the standard deviation is less than about 3.

Claim 35

The composition of claim 31 wherein the fibrous material comprises greater than about 50 percent by weight of the composition.

Claim 36

The composition of claim 32 wherein the fibrous material comprises from about 75 to about 95 percent by weight of the composition.

Claim 37

The composition of claim 31 wherein the binder further comprises a plasticizer for the binder.

Claim 38

The composition of claim 31 wherein the binder further comprises a compound which promotes adhesion between the fibrous material and the rubber or plastic compound stock.

Claim 39

The composition of claim 34 wherein the binder further comprises a compound which promotes adhesion between the fibrous material and the rubber or plastic compound stock.

Claim 40

The composition of claim 31 wherein the binder further comprises an antidegradant for the binder.

Claim 41

The composition of claim 34 wherein the binder further comprises an antidegradant for the binder.

Claim 42

The composition of claim 35 wherein the binder further comprises an antidegradant for the binder.

Claim 43

The composition of claim 36 wherein the binder further comprises an antidegradant for the binder.

Claim 44

The composition of claim 31 wherein the fibrous material is selected from the group consisting of rayon, polyester, cotton, asbestos and glass fibers.

Claim 45

The composition of claim 31 wherein the rubber or plastic polymer binder comprises a rubber or plastic polymer prepared by an emulsion polymerization process.

Claim 46

The composition of claim 42 wherein the rubber or plastic polymer is selected from the group consisting of (a) natural rubber, (b) polybutadiene, (c) copolymers of butadiene and one or more comonomers selected from styrene, acrylonitrile, methylmethacrylate, vinylpyridine or a derivative thereof, and a carboxylic acid, (d) polyisoprene, (e) polychloroprene, (f) copolymers of vinyl acetate and ethylene, (g) butyl rubber, (h) polyisobutylene, (i) poly(vinyl chloride), (j) poly(vinyl chloride-vinylidene chloride), (k) poly (vinylidene chloride), (l) acrylonitrile-butadiene-styrene copolymer and (m) styrene-acrylonitrile copolymer.

Claim 47

The composition of claim 31 wherein the rubber or plastic polymer binder comprises a rubber or plastic polymer prepared by a solution polymerization process.

Claim 48

The composition of claim 44 wherein the rubber or plastic polymer is selected from the group consisting of (a) EPDM, (b) EPR, (c) oxidized polyethylene, (d) block copolymers of styrene and butadiene, and (e) thermoplastic rubbers.

Claim 49

A process for preparing a homogeneous predispersed fiber composition useful for dispersing a fibrous material in a rubber or plastic compound stock, wherein said composition comprises a fibrous material and a rubber or plastic polymer binder, said process comprising, mixing a latex of the rubber or plastic polymer with the fibrous material to form a wetted fiber mixture wherein the total amount of water present in the wetted fiber mixture prior to coagulation is substantially equal to that required to completely wet the fibrous material by either capillary action, surface adsorption, or a combination thereof, and mixing a coagulant with the wetted fiber mixture thereby forming the predispersed fiber composition.

Claim 50

A process for preparing a homogeneous predispersed fiber composition useful for dispersing a fibrous material in a rubber or plastic compound stock, wherein said composition comprises a fibrous material and a rubber or plastic polymer binder, said process comprising, mixing a latex of the rubber or plastic polymer with the fibrous material to form a wetted fiber mixture wherein the total amount of water present in the wetted fiber mixture prior to coagulation is substantially equal to that required to completely wet the fibrous material by either capillary action, surface adsorption, or a combination thereof, and mixing a coagulant with the wetted fiber mixture thereby forming the predispersed fiber composition.

Claim 51

A process for preparing a substantially homogeneous predispersed fiber composition useful for dispersing a fibrous material in a rubber or plastic compound stock, wherein said composition comprises a fibrous material and a rubber or plastic polymer binder, said process comprising, (a) mixing a latex of the rubber or plastic polymer with the fibrous material to form a wetted fiber mixture wherein the percent of total solids in the wetted fiber mixture prior to coagulation which will result in the formation of said fiber composition is determined by first preparing several test predispersed fiber compositions having the same composition as that desired from several test wetted fiber mixtures, each of which has a different percent of total solids decreasing in equal increments from the point at which the total amount of water present in one of the test wetted fiber mixtures prior to coagulation is substantially equal to that required to completely wet the fibrous material by either capillary action, surface adsorption, or a combination thereof, from each of the several test fiber compositions obtained, a sufficient number of samples of approximately equal weight are analyzed to determine the percent of fibrous material present in each of the samples and to determine the standard deviation in the percent of fibrous material for each of the test fiber compositions, plotting a curve of the standard deviations obtained versus the percent of total solids in the test wetted fiber mixtures used to prepare each of the test fiber compositions, and then selecting a percent of total solids for the wetted fiber mixture prior to coagulation which corresponds to a point on the homogeneous portion of the curve wherein the homogeneity of the test fiber compositions is substantially equal to that obtained at the point where the total amount of water present in one of the test wetted fiber mixtures prior to coagulation is substantially equal to that required to completely wet the fibrous material by either capillary action, surface adsorption, or a combination thereof, and (b) mixing a coagulant with the wetted fiber mixture thereby forming the predispersed fiber composition.

Claim 52

A process for preparing a substantially homogeneous predispersed fiber composition useful for dispersing a fibrous material in a rubber or plastic compound stock, wherein said composition comprises a fibrous material and a rubber or plastic polymer binder, said process comprising, (a) mixing a latex of the rubber or plastic polymer with the fibrous material to form a wetted fiber mixture wherein the percent of total solids in the wetted fiber mixture prior to coagulation which will result in the formation of said fiber composition is determined by first preparing several test predispersed fiber compositions having the same composition as that desired from several test wetted fiber mixtures, each of which has a different percent of total solids decreasing in equal increments from the point at which the total amount of water present in one of the test wetted fiber mixtures prior to coagulation is substantially equal to that required to completely wet the fibrous material by either capillary action, surface adsorption, or a combination thereof, from each of the several test fiber compositions obtained, a sufficient number of samples of approximately equal weight are analyzed to determine the percent of fibrous material present in each of the samples and to determine the standard deviation in the percent of fibrous material for each of the test fiber compositions, plotting a curve of the standard deviations obtained versus the percent of total solids in the test wetted fiber mixtures used to prepare each of the test fiber compositions, and then selecting a percent of total solids for the wetted fiber mixture prior to coagulation which corresponds to a point on the homogeneous portion of the curve wherein the homogeneity of the test fiber compositions is substantially equal to that obtained at the point where the total amount of water present in one of the test wetted fiber mixtures prior to coagulation is substantially equal to that required to completely wet the fibrous material by either capillary action, surface adsorption, or a combination thereof, and (b) mixing a coagulant with the wetted fiber mixture thereby forming the predispersed fiber composition.

Claim 53

A process for preparing a substantially homogeneous predispersed fiber composition useful for dispersing a fibrous material in a rubber or plastic compound stock, wherein said composition comprises a fibrous material and a rubber or plastic polymer binder, said process comprising (a) mixing a latex of the rubber or plastic polymer with the fibrous material to form a wetted fiber mixture wherein the percent of total solids in the wetted fiber mixture prior to coagulation which will result in the formation of said fiber composition is determined by first preparing several test predispersed fiber compositions having the same composition as that desired from several test wetted fiber mixtures, each of which has a different percent of total solids decreasing in equal increments from the point at which the total amount of water present in one of the test wetted fiber mixtures prior to coagulation is substantially equal to that required to completely wet the fibrous material by either capillary action, surface adsorption or a combination thereof, from each of the several test fiber compositions obtained, a sufficient number of samples of approximately equal weight are analyzed to determine the percent of fibrous material present in each of the samples and to determine the standard deviation in the percent of fibrous material for each of the test fiber compositions, plotting a curve of the standard deviations obtained versus the percent of total solids in the test wetted fiber mixtures used to prepare each of the test fiber compositions, and then selecting a percent of total solids for the wetted fiber mixture prior to coagulation which corresponds to a point on the portion of the curve which extends from the point where the total amount of water present in one of the test wetted fiber mixtures prior to coagulation is substantially equal to that required to completely wet the fibrous material by either capillary action, surface adsorption or a combination thereof to the inflection point. (b) mixing a coagulant with the wetted fiber mixture thereby forming the predispersed fiber composition.

Claim 54

A process for preparing a substantially homogeneous predispersed fiber composition useful for dispersing a fibrous material in a rubber or plastic compound stock, wherein said composition comprises a fibrous material and a rubber or plastic polymer binder, said process comprising (a) mixing a latex of the rubber or plastic polymer with the fibrous material to form a wetted fiber mixture wherein the percent of total solids in the wetted fiber mixture prior to coagulation which will result in the formation of said fiber composition is determined by first preparing several test predispersed fiber compositions having the same composition as that desired from several test wetted fiber mixtures, each of which has a different percent of total solids decreasing in equal increments from the point at which the total amount of water present in one of the test wetted fiber mixtures prior to coagulation is substantially equal to that required to completely wet the fibrous material by either capillary action, surface adsorption or a combination thereof, from each of the several test fiber compositions obtained, a sufficient number of samples of approximately equal weight are analyzed to determine the percent of fibrous material present in each of the samples and to determine the standard deviation in the percent of fibrous material for each of the test fiber compositions, plotting a curve of the standard deviations obtained versus the percent of total solids in the test wetted fiber mixtures used to prepare each of the test fiber compositions, and then selecting a percent of total solids for the wetted fiber mixture prior to coagulation which corresponds to a point on the portion of the curve which extends from the point where the total amount of water present in one of the test wetted fiber mixtures prior to coagulation is substantially equal to that required to completely wet the fibrous material by either capillary action, surface adsorption or a combination thereof to the inflection point. (b) mixing a coagulant with the wetted fiber mixture thereby forming the predispersed fiber composition.

Claim 55

A process for preparing a substantially homogeneous predispersed fiber composition useful for dispersing a fibrous material in a rubber or plastic compound stock, wherein said composition comprises a fibrous material and a rubber or plastic polymer binder, said process comprising (a) mixing a latex of the rubber or plastic polymer with the fibrous material to form a wetted fiber mixture wherein the percent of total solids in the wetted fiber mixture prior to coagulation which will result in the formation of said fiber composition is determined by first preparing several test predispersed fiber compositions having the same composition as that desired from several test wetted fiber mixtures, each of which has a different percent of total solids decreasing in equal increments from the point at which the total amount of water present in one of the test wetted fiber mixtures prior to coagulation is substantially equal to that required to completely wet the fibrous material by either capillary action, surface adsorption, or a combination thereof. from each of the several test fiber compositions obtained, a sufficient number of samples of approximately equal weight are analyzed to determine the percent of fibrous material present in each of the samples and to determine the standard deviation in the percent of fibrous material for each of the test fiber compositions, plotting a curve of the standard deviations obtained versus the percent of total solids in the test wetted fiber mixtures used to prepare each of the test fiber compositions, and then selecting a percent of total solids for the wetted fiber mixture prior to coagulation which corresponds to a point on the curve at which the value of the standard deviation is less than about 3, and (b) mixing a coagulant with the wetted fiber mixture thereby forming the predispersed fiber composition.

Claim 56

A process for preparing a substantially homogeneous predispersed fiber composition useful for dispersing a fibrous material in a rubber or plastic compound stock, wherein said composition comprises a fibrous material and a rubber or plastic polymer binder, said process comprising (a) mixing a latex of the rubber or plastic polymer with the fibrous material to form a wetted fiber mixture wherein the percent of total solids in the wetted fiber mixture prior to coagulation which will result in the formation of said fiber composition is determined by first preparing several test predispersed fiber compositions having the same composition as that desired from several test wetted fiber mixtures, each of which has a different percent of total solids decreasing in equal increments from the point at which the total amount of water present in one of the test wetted fiber mixtures prior to coagulation is substantially equal to that required to completely wet the fibrous material by either capillary action, surface adsorption, or a combination thereof. from each of the several test fiber compositions obtained, a sufficient number of samples of approximately equal weight are analyzed to determine the percent of fibrous material present in each of the samples and to determine the standard deviation in the percent of fibrous material for each of the test fiber compositions, plotting a curve of the standard deviations obtained versus the percent of total solids in the test wetted fiber mixtures used to prepare each of the test fiber compositions, and then selecting a percent of total solids for the wetted fiber mixture prior to coagulation which corresponds to a point on the curve at which the value of the standard deviation is less than about 3, and (b) mixing a coagulant with the wetted fiber mixture thereby forming the predispersed fiber composition.

Claim 57

A process comprising the rapid, uniform and thorough dispersion of a fibrous material into a rubber or plastic compound stock by mechanically mixing the predispersed fiber composition prepared by process of claims 46, 47, 48 or 49 with the rubber or plastic compound stock.

Claim 58

The new use of claim 50 wherein the binder further comprises a plasticizer for the binder.

Claim 59

The new use of claim 50 wherein the binder further comprises a compound which promotes adhesion between the fibrous material and the rubber or plastic compound stock.

Claim 60

The new use of claim 50 wherein the binder further comprises an antidegradant for the binder.