Rhodium catalyzed silicone rubber compositions

Claim 2

Silicone rubber release coating composition with a good shelf life for coating plastic and cellulosic substrates comprising (a) 100 parts by weight of silanol end-stopped diorganopolysiloxane polymer having 100 to 1,000 centipoise viscosity at 25° C. where the organo groups are selected from the class consisting of alkyl radicals of 1 to 8 carbon atoms and mixturees thereof; (b) from 1 to 20 parts by weight of a silicone hydride having from 0.5 to 1.6% by weight of hydrogen and viscosity varying from 5 to 200 centipoise at 25° C.; (c) from 10 to 500 parts per million as rhodium metal of a rhodium complex catalyst of the formula, RhX.sub.3 (R.sub.2 S).sub.3 where R is an alkyl radical that has from 4 to 12 carbon atoms and X is selected from the class consisting of chlorine and bromine; and (d) from 0.1 to 10 parts by weight of an inhibitor compound selected from the class consisting of (1) a dialkyl maleate where the alkyl radical contains from 1 to 8 carbon atoms; (2) a compound containing an acetylenic group; (3) a olefinic carboxylic acid ester of aliphatic alcohols where the aliphatic alcohol contains from 1 to 4 carbon atoms and the olefinic carboxylic acid contains from 3 to 10 atoms; and (4) a alkenyl isocyanurate wherein the alkenyl groups contains from 3 to 8 carbon atoms and mixtures thereof.

Claim 3

The composition of claim 1 wherein the silicone hydride has the formula, ##STR3## where R' is selected from the class consisting of alkyl radicals of 1 to 8 carbon atoms and a mixture of hydrogen and alkyl radicals of 1 to 8 carbon atoms and R 2 is an alkyl radical of 1 to 8 carbon atoms and t varies such that the polymer has a viscosity varying from 5 to 200 centipoise at 25° C.

Claim 4

The composition of claim 1 wherein the silicone hydride has the formula, (R.sup.3 HSiO).sub.4 wherein R 3 is an alkyl radical of 1 to 8 carbon atoms.

Claim 5

The composition of claim 1 wherein the rhodium catalyst has the formula, RhCl.sub.3 [(C.sub.4 H.sub.9).sub.2 S].sub.3.

Claim 6

The composition of claim 1 wherein the rhodium catalyst has the formula, RhCl.sub.3 [(C.sub.8 H.sub.17).sub.2 S].sub.3.

Claim 7

The composition of claim 1 wherein the inhibitor compound is diethylmaleate.

Claim 8

The composition of claim 1 wherein the inhibitor compound is diethylacetylenedicarboxylate.

Claim 9

The composition of claim 1 wherein the inhibitor compound is vinyl acetate.

Claim 10

The composition of claim 1 wherein the inhibitor compound is triallylisocyanurate.

Claim 11

The composition of claim 1 wherein the inhibitor compound is a mixture of diethylmaleate and a linear silanol end-stopped dimethylpolysiloxane having a viscosity of 25 to 60 centipoise at 25° C. and a silanol content varying from 7.3 to 14.1% by weight.

Claim 12

A process for forming a silicone rubber release coating composition with a good shelf life for coating plastic and cellulosic substrates comprising (i) mixing (a) 100 parts by weight of silanol end-stopped diorganopolysiloxane polymer having 100 to 1,000 centipoise viscosity at 25° C. where the organo groups are selected from the class consisting of alkyl radicals, fluoroalkyl radicals of 1 to 8 carbon atoms and mixturees thereof; (b) from 1 to 20 parts by weight of a silicone hydride having from 0.5 to 1.6% by weight of hydrogen and viscosity varying from 5 to 200 centipoise at 25° C.; (c) from 10 to 500 parts per million as rhodium metal of a rhodium complex catalyst of the formula, RhX.sub.3 (R.sub.2 S).sub.3 where R is an alkyl radical that has from 4 to 12 carbon atoms and X is selected from the class consisting of chlorine and bromine; and (d) from 0.1 to 10 parts by weight of an inhibitor compound selected from the class consisting of (1) a dialkyl maleate where the alkyl radical contain from 1 to 8 carbon atoms; (2) a compound containing an acetylenic group; (3) a olefinic carboxylic acid ester of aliphatic alcohols where the aliphatic alcohol contains from 1 to 4 carbon atoms and the olefinic carboxyic acid contains from 3 to 10 atoms; and (4) a alkenyl isocyanurate wherein the alkenyl groups contains from 3 to 8 carbon atoms and mixtures thereof; and (ii) curing the mixture by heating it at a temperature in the range of 300°-500° F. for 5 to 60 seconds.

Claim 13

A process for forming a silicone rubber release coating composition with a good shelf life for coating plastic and cellulosic substrates comprising (i) mixing (a) 100 parts by weight of silanol end-stopped diorganopolysiloxane polymer having 100 to 1,000 centipoise viscosity at 25° C. where the organo groups are selected from the class consisting of alkyl radicals, fluoroalkyl radicals of 1 to 8 carbon atoms and mixturees thereof; (b) from 1 to 20 parts by weight of a silicone hydride having from 0.5 to 1.6% by weight of hydrogen and viscosity varying from 5 to 200 centipoise at 25° C.; (c) from 10 to 500 parts per million as rhodium metal of a rhodium complex catalyst of the formula, RhX.sub.3 (R.sub.2 S).sub.3 where R is an alkyl radical that has from 4 to 12 carbon atoms and X is selected from the class consisting of chlorine and bromine; and (d) from 0.1 to 10 parts by weight of an inhibitor compound selected from the class consisting of (1) a dialkyl maleate where the alkyl radical contain from 1 to 8 carbon atoms; (2) a compound containing an acetylenic group; (3) a olefinic carboxylic acid ester of aliphatic alcohols where the aliphatic alcohol contains from 1 to 4 carbon atoms and the olefinic carboxyic acid contains from 3 to 10 atoms; and (4) a alkenyl isocyanurate wherein the alkenyl groups contains from 3 to 8 carbon atoms and mixtures thereof; and (ii) curing the mixture by heating it at a temperature in the range of 300°-500° F. for 5 to 60 seconds.

Claim 14

The process of claim 11 wherein the silicone hydride has the formula, ##STR4## wherein R' is selected from the class consisting of alkyl radicals of 1 to 8 carbon atoms and a mixture of hydrogen and alkyl radicals of 1 to 8 carbon atoms and R 2 is an alkyl radical of 1 to 8 carbon atoms and 6 varies such that the polymer has a viscosity varying from 5 to 200 centipoise at 25° C.

Claim 15

The process of claim 11 wherein the silicone hydride has the formula, (R.sup.3 HSiO).sub.4 wherein R 3 is an alkyl radical of 1 to 8 carbon atoms.

Claim 16

The process of claim 11 wherein the rhodium catalyst has the formula, RhCl.sub.3 [(C.sub.4 H.sub.9).sub.2 S].sub.3.

Claim 17

The process of claim 11 wherein the rhodium catalyst has the formula, RhCl.sub.3 [(C.sub.8 H.sub.17).sub.2 S].sub.3.

Claim 18

The process of claim 11 wherein the inhibitor compound is diethylmaleate.

Claim 19

The process of claim 11 wherein the inhibitor compound is diethylacetylenedicarboxylate.

Claim 20

The process of claim 11 wherein the inhibitor compound is vinyl acetate.

Claim 21

The process of claim 11 wherein the inhibitor compound is triallylisocyanurate.

Claim 22

The process of claim 11 wherein the inhibitor compound is a mixture of diethylmaleate and a linear silano end-stopped dimethylpolysiloxane having a viscosity of 25 to 60 centipoise at 25° C. and a silanol content varying from 7.3 to 14.1% by weight.

Claim 23

A substrate with a silicone release coating thereon comprising (i) a substrate selected from the class consisting of cellulosic and plastic substrates over which is applied a coating of (ii) (a) 100 parts by weight of silanol end-stopped diorganopolysiloxane polymer having 100 to 1,000 are selected from the class consisting of alkyl radicals, fluoroalkyl radicals of 1 to 8 carbon atoms and mixtures thereof; (b) from 1 to 20 parts by weight of a silicone hydride having from 0.5 to 1.6% by weight of hydrogen and viscosity varying from 5 to 200 centipoise at 25° C.; (c) from 10 to 500 parts per million as rhodium metal of a rhodium complex catalyst of the formula, RhX.sub.3 (R.sub.2 S).sub.3 where R is an alkyl radical that has from 4 to 12 carbon atoms and X is selected from the class consisting of chlorine and bromine; and (d) from 0.1 to 10 parts by weight of an inhibitor compound selected from the class consisting of (1) a dialkyl maleate where the alkyl radical contains from 1 to 8 carbon atoms; (2) a compound containing an acetylenic group; (3) a olefinic carboxylic acid ester of aliphatic alcohols where the aliphatic alcohol contains from 1 to 4 carbon atoms and the olefinic carboxylic acid contains from 3 to 10 atoms; and (4) a alkenyl isocyanurate wherein the alkenyl groups contains from 3 to 8 carbon atoms and mixtures thereof.

Claim 24

A substrate with a silicone release coating thereon comprising (i) a substrate selected from the class consisting of cellulosic and plastic substrates over which is applied a coating of (ii) (a) 100 parts by weight of silanol end-stopped diorganopolysiloxane polymer having 100 to 1,000 are selected from the class consisting of alkyl radicals, fluoroalkyl radicals of 1 to 8 carbon atoms and mixtures thereof; (b) from 1 to 20 parts by weight of a silicone hydride having from 0.5 to 1.6% by weight of hydrogen and viscosity varying from 5 to 200 centipoise at 25° C.; (c) from 10 to 500 parts per million as rhodium metal of a rhodium complex catalyst of the formula, RhX.sub.3 (R.sub.2 S).sub.3 where R is an alkyl radical that has from 4 to 12 carbon atoms and X is selected from the class consisting of chlorine and bromine; and (d) from 0.1 to 10 parts by weight of an inhibitor compound selected from the class consisting of (1) a dialkyl maleate where the alkyl radical contains from 1 to 8 carbon atoms; (2) a compound containing an acetylenic group; (3) a olefinic carboxylic acid ester of aliphatic alcohols where the aliphatic alcohol contains from 1 to 4 carbon atoms and the olefinic carboxylic acid contains from 3 to 10 atoms; and (4) a alkenyl isocyanurate wherein the alkenyl groups contains from 3 to 8 carbon atoms and mixtures thereof.

Claim 25

The silicone coated substrate of claim 21 wherein the silicone hydride has the formula, ##STR5## where R' is selected from the class consisting of alkyl radicals of 1 to 8 carbon atoms and a mixture of hydrogen and alkyl radicals of 1 to 8 carbon atoms and R 2 is an alkyl radical of 1 to 8 carbon atoms and t varies such that the polymer has a viscosity varying from 5 to 200 centipoise at 25° C.

Claim 26

The silicone coated substrate of claim 21 wherein the silicone hydride has the formula, (R.sup.3 HSiO).sub.4 wherein R 3 is an alkyl radical of 1 to 8 carbon atoms.

Claim 27

The silicone coated substrate of claim 21 wherein the rhodium catalyst has the formula, RhCl.sub.3 [C.sub.4 H.sub.9).sub.2 S].sub.3.

Claim 28

The silicone coated substrate of claim 21 wherein the rhodium catalyst has the formula, RhCl.sub.3 [(C.sub.8 H.sub.17).sub.2 S].sub.3.

Claim 29

The silicone coated substrate of claim 21 wherein the inhibitor compound is diethylmaleate.

Claim 30

The silicone coated substrate of claim 21 wherein the inhibitor compound is diethylacetylenedicarboxylate.

Claim 31

The silicone coated substrate of claim 21 wherein the inhibitor compound is vinyl acetate.

Claim 32

The silicone coated substrate of claim 21 wherein the inhibitor compound is triallylisocyanurate.

Claim 33

The silicone coated substrate of claim 21 wherein the inhibitor compound is a mixture of diethylmaleate and a linear silanol end-stopped dimethylpolysiloxane having a viscosity of 25 to 50 centipoise at 25° C. and a silanol content varying from 7.3 to 14.1% by weight.

Claim 34

The process for applying a silicone release coating on a substrate comprising (i) applying to a substrate selected from the class consisting of a cellulosic substrates and plastics substrates silicone coating mixture of (a) 100 parts by weight of silanol end-stopped diorganopolysiloxane polymer having 100 to 1,000 centipoise viscosity at 25° C. where the organo groups are selected from the class consisting of alkyl radicals, fluoroalkyl radicals of 1 to 8 carbon atoms and mixtures thereof; (b) from 1 to 20 parts by weight of a silicone hydride having from 0.5 to 1.6% by weight of hydrogen and viscosity varying from 5 to 200 centipoise at 25° C.; (c) from 10 to 500 parts per million as rhodium metal of a rhodium complex catalyst of the formula, RhX.sub.3 (R.sub.2 S).sub.3 where R is an alkyl radical that has from 4 to 12 carbon atoms and X is selected from the class consisting of chlorine and bromine; and (d) from 0.1 to 10 parts by weight of an inhibitor compound selected from the class consisting of silanol end-stopped diorganopolysiloxane having 5.5 to 14.1% by weight silanol, a viscosity of 20 to 80 centipoise at 25° and where the organo groups are alkyl radicals of 1 to 8 carbon atoms; (1) a dialkyl maleate where the alkyl radical contains from 1 to 8 carbon atoms; (2) a compound containing an acetylenic group; (3) a olefinic carboxylic acid ester of aliphatic alcohols where the aliphatic alcohol contains from 1 to 4 carbon atoms and the olefinic carboxylic acid contains from 3 to 10 atoms; and (4) a alkenyl isocyanurate wherein the alkenyl groups contains from 3 to 8 carbon atoms and mixtures thereof; and (ii) heating said silicone mixture at a temperature in the range of 300° to 500° F. for 60 seconds.

Claim 35

The process for applying a silicone release coating on a substrate comprising (i) applying to a substrate selected from the class consisting of a cellulosic substrates and plastics substrates silicone coating mixture of (a) 100 parts by weight of silanol end-stopped diorganopolysiloxane polymer having 100 to 1,000 centipoise viscosity at 25° C. where the organo groups are selected from the class consisting of alkyl radicals, fluoroalkyl radicals of 1 to 8 carbon atoms and mixtures thereof; (b) from 1 to 20 parts by weight of a silicone hydride having from 0.5 to 1.6% by weight of hydrogen and viscosity varying from 5 to 200 centipoise at 25° C.; (c) from 10 to 500 parts per million as rhodium metal of a rhodium complex catalyst of the formula, RhX.sub.3 (R.sub.2 S).sub.3 where R is an alkyl radical that has from 4 to 12 carbon atoms and X is selected from the class consisting of chlorine and bromine; and (d) from 0.1 to 10 parts by weight of an inhibitor compound selected from the class consisting of silanol end-stopped diorganopolysiloxane having 5.5 to 14.1% by weight silanol, a viscosity of 20 to 80 centipoise at 25° and where the organo groups are alkyl radicals of 1 to 8 carbon atoms; (1) a dialkyl maleate where the alkyl radical contains from 1 to 8 carbon atoms; (2) a compound containing an acetylenic group; (3) a olefinic carboxylic acid ester of aliphatic alcohols where the aliphatic alcohol contains from 1 to 4 carbon atoms and the olefinic carboxylic acid contains from 3 to 10 atoms; and (4) a alkenyl isocyanurate wherein the alkenyl groups contains from 3 to 8 carbon atoms and mixtures thereof; and (ii) heating said silicone mixture at a temperature in the range of 300° to 500° F. for 60 seconds.