Assignee: Unilever Patent Holdings BV
•
Filing: 1978-11-27
•
Granted: 1981-04-14
•
Expires: 1998-11-27
Abstract
Abstract A method is disclosed for the manufacture of a biaxially stretched polyolefin film, particularly a polypropylene film, having improved properties, in which the material is first partially prestretched in a longitudinal direction and, thereafter, simultaneously biaxially (longitudinally and laterally) stretched, the apparatus comprising stretching rollers for effecting partial longitudinal stretching of the film, the rollers being arranged upstream of an assembly for effecting simultaneous biaxial stretching of the film. The speed of the stretching rollers is infinitely variable so as to influence the total degree of film-stretching only by changing the speed of the rollers. The rollers used for longitudinal prestretching are arranged at the inlet section of the biaxial stretching assembly. A system is provided to maintain the film exactly at the temperature required by the film characteristics for stretching, and biaxial stretching is done such that any given point on the film in the region the film is being biaxially stretched undergoes simultaneous biaxial stretching both in the longitudinal and transverse directions of the film.
Inventors
- 👤 Walter Hufnagel
- 👤 Volker Graap, deceased
- 👤 Friedrich F. von und zu Aufsess
- 👤 Rotger Armsen
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 09:36
CPC Classifications
B; B29; B29C; B29C55/00; B29C55/02; B29C55/10; B29C55/12; B29C55/14; C; C09; C09J; C09J7/00; C09J7/20; C09J7/22; C09J7/24; C09J7/241
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
240 words
A method of fabricating a film from a solvent-free thermoplastic polyolefin material, said method comprising the steps of: (a) forming said thermoplastic polyolefin material into an elongate film; (b) continually advancing said film in a longitudinal direction; (c) partially pre-stretching said film in said longitudinal direction, while advancing it, by an amount of up to 50% of the total longitudinal length said film is to exhibit after being finally stretched; and (d) further stretching successive regions of said film simultaneously biaxially both in said longitudinal direction and in a direction of its width transverse to said longitudinal direction while further advancing said film in said longitudinal direction such that any given point on said film in any region said film is being biaxially stretched is expanded simultaneously biaxially both in said longitudinal and transverse directions, the total stretching of said film in said longitudinal direction resulting from the combination of its being both longitudinally pre-stretched and biaxially further stretched being at least seven times its unstretched longitudinal length as measured before said partial pre-stretching, and the total stretching of said film in said direction of its width transverse to said longitudinal direction resulting from biaxially stretching said film being at least seven times its unstretched width as measured before said biaxial stretching but percentage-wise not greater than the percentage of total longitudinal stretching of said film resulting from the combination of its being both longitudinally pre-stretched and biaxially further stretched.
Claim 2
Independent Claim
240 words
A method of fabricating a film from a solvent-free thermoplastic polyolefin material, said method comprising the steps of: (a) forming said thermoplastic polyolefin material into an elongate film; (b) continually advancing said film in a longitudinal direction; (c) partially pre-stretching said film in said longitudinal direction, while advancing it, by an amount of up to 50% of the total longitudinal length said film is to exhibit after being finally stretched; and (d) further stretching successive regions of said film simultaneously biaxially both in said longitudinal direction and in a direction of its width transverse to said longitudinal direction while further advancing said film in said longitudinal direction such that any given point on said film in any region said film is being biaxially stretched is expanded simultaneously biaxially both in said longitudinal and transverse directions, the total stretching of said film in said longitudinal direction resulting from the combination of its being both longitudinally pre-stretched and biaxially further stretched being at least seven times its unstretched longitudinal length as measured before said partial pre-stretching, and the total stretching of said film in said direction of its width transverse to said longitudinal direction resulting from biaxially stretching said film being at least seven times its unstretched width as measured before said biaxial stretching but percentage-wise not greater than the percentage of total longitudinal stretching of said film resulting from the combination of its being both longitudinally pre-stretched and biaxially further stretched.
Claim 3
Dependent Claim
28 words
A method as claimed in claim 1, wherein said step of biaxial stretching is conducted by pulling the opposite longitudinally directed edges of said film in diverging relation.
Claim 4
Dependent Claim
29 words
A method as claimed in claim 1, wherein said step of partial longitudinal pre-stretching effects an elongation of said film longitudinally in a ratio range approximately 1:1.2 to 1:11.
Claim 5
Dependent Claim
33 words
A method as claimed in claim 1, wherein the amount of partial longitudinal pre-stretching can selectively be varied while the amount of final longitudinal film-stretching effected by the simultaneous biaxial film-stretching remains constant.
Claim 6
Dependent Claim
39 words
A method as claimed in claim 1 wherein said steps of pre-stretching said film and biaxially stretching said film are effected while said film is dry and free from an influence of any solvent for softening the film material.
Claim 7
Dependent Claim
44 words
A method as claimed in claim 1, including heating said film to the thermoelastic temperature range of said thermoplastic material, and conducting said steps of pre-stretching in said longitudinal direction and biaxial stretching in said longitudinal and transverse directions in said thermoelastic temperature range.
Claim 8
Dependent Claim
26 words
A method as claimed in claim 6, including maintaining the temperature of said film continually without interruption in said thermoelastic temperature range of said thermoplastic material.
Claim 9
Dependent Claim
45 words
A method as claimed in claim 6, including heating said film to a temperature higher than the thermoelastic temperature range of said thermoplastic material after completing said step of biaxial stretching in said longitudinal and transverse directions, thereby maintaining the film in its stretched condition.
Claim 10
Dependent Claim
43 words
A method as claimed in claim 8, including cooling said film to a temperature below the minimum thermoelastic temperature of said thermoplastic material after completing said step of heating said film to a temperature higher than the thermoelastic temperature range of said material.
Claim 11
Dependent Claim
41 words
A method as claimed in claim 9, including continually advancing said film without interruption from said step of forming it from said thermoplastic material to said step of cooling it to a temperature below said minimum thermoelastic temperature of said material.
References Cited (Backward Citations)
CA671029A
Cited
US2034716A
Cited
US2851733A
Cited
US2884663A
Cited
US3271495A
Cited
US3046599A
Cited
US3248753A
Cited
US3676539A
Cited
US4134957A
Cited
US3890421A
Cited
JPS4833991A
Cited
US3952073A
Cited
JPS5025680A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-04-13 | 1984-10-13 | 1985-04-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-04-13 | 1988-10-13 | 1989-04-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-04-13 | 1992-10-13 | 1993-04-14 | $7700.00 | Window Closed / Lapsed |