Method of making a photovoltaic cell
Assignee: Colorado School of Mines Foundation Inc
•
Filing: 1980-02-21
•
Granted: 1981-04-14
•
Expires: 2000-02-21
Abstract
Abstract Photovoltaic cell comprises thin film cadmium telluride in ohmic contact with a smooth conductive substrate, preferably comprising a cadmium surface, through a cadmium-rich layer at the interface with the substrate, the cell further including a rectifying barrier layer. Preferably, the film is electrodeposited on the substrate surface with specific materials and process conditions. Preferably also, the film or cell is subsequently treated to enhance its barrier layer interface function.
Inventors
- 👤 Gabor F. Fulop
- 👤 Jacob F. Betz
- 👤 Peter V. Meyers
- 👤 Mitchell E. Doty
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 16:18
CPC Classifications
C; C25; C25D; C25D9/00; C25D9/04; C25D9/08; C25D3/00; C25D3/02; C25D3/56; H; H10; H10F; H10F10/00; H10F10/10; H10F10/18; H10F71/00; H10F71/125; H10F71/128; H10F77/00; H10F77/10; H10F77/16; H10F77/169; H10F77/1696; H10P; H10P14/00; H10P14/20; H10P14/26; H10P14/265; H10P14/29; H10P14/2901; H10P14/2923; H10P14/32; H10P14/3202; H10P14/3241; H10P14/34; H10P14/3402; H10P14/3424; H10P14/3432; Y; Y02; Y02E; Y02E10/00; Y02E10/50; Y02E10/543; Y02P; Y02P70/00; Y02P70/50; Y10; Y10S; Y10S205/00; Y10S205/917
Claims Analysis
Total Claims: 53
Claim 1
Independent Claim
43 words
A method of making a photovoltaic cell including the step of electrodepositing cadmium telluride on a substrate having a cadmium surface, whereby a photovoltaic cadmium telluride film is formed and ohmic contact is made between said cadmium telluride film and said cadmium surface.
Claim 2
Independent Claim
43 words
A method of making a photovoltaic cell including the step of electrodepositing cadmium telluride on a substrate having a cadmium surface, whereby a photovoltaic cadmium telluride film is formed and ohmic contact is made between said cadmium telluride film and said cadmium surface.
Claim 3
Dependent Claim
28 words
A method for making a photovoltaic cell, as recited in claim 1, wherein a barrier layer, forming a rectifying junction with said cadmium telluride film, is deposited thereon.
Claim 4
Dependent Claim
32 words
A method, as recited in claim 2, wherein said cadmium telluride film is given a pretreatment prior to the deposition of a barrier layer thereon to form a better rectifying junction therewith.
Claim 5
Dependent Claim
20 words
A method, as recited in claim 3, wherein said film is pretreated by heating in a nitrogen or oxygen-containing atmosphere.
Claim 6
Dependent Claim
25 words
A method, as recited in claim 3, wherein said pretreatment consists of electrolytic treatment wherein the film is made anodic in an alkaline electrolytic bath.
Claim 7
Dependent Claim
19 words
A method, as recited in claim 3, wherein said pre-treatment comprises exposing said cadmium telluride film to a flame.
Claim 8
Dependent Claim
32 words
A method, as recited in claim 2, wherein said cadmium telluride film is given a postreatment subsequent to the deposition of a barrier layer thereon to form a better rectifying junction therewith.
Claim 9
Dependent Claim
21 words
A method, as recited in claim 7, wherein said post treatment consists of contacting the surface of said film with hydrazine.
Claim 10
Dependent Claim
22 words
A method, as recited in claim 7, wherein said post treatment consists of contacting the surface of said film with alkaline solution.
Claim 11
Dependent Claim
26 words
A method, as recited in claim 7, wherein said post treatment consists of electrolytic treatment wherein the film is made cathodic in an alkaline electrolytic bath.
Claim 12
Dependent Claim
29 words
A method as in claim 2 wherein said cadmium telluride film is pre-treated prior to formation of the barrier layer and post-treated subsequent to formation of said barrier layer.
Claim 13
Dependent Claim
37 words
A method, as recited in claim 11, wherein said pretreatment consists of etching said CdTe film prior to depositing said barrier layer, and said post-treatment consists of heating in a hydrogen atmosphere to effect hydrogen annealing thereof.
Claim 14
Dependent Claim
42 words
A method, as recited in claim 11, wherein said pre and post treatments include at least two of the steps of nitrogen annealing, air annealing, etching, hydrogen annealing, hydrazine contact, alkaline bath contact, flame treatment and electrolytic treatment in an alkaline bath.
Claim 15
Dependent Claim
26 words
A method, as recited in claim 2, wherein said cadmium telluride film is etched, the barrier layer is formed, and then annealed in a hydrogen atmosphere.
Claim 16
Dependent Claim
38 words
A method, as recited in claim 2, wherein after electrodeposition of said cadmium telluride and the formation of a barrier layer thereon, said photovoltaic cell is treated by immersion thereof in hydrazine for 1-20 minutes at room temperature.
Claim 17
Dependent Claim
30 words
A method, as recited in claim 1, wherein said electrodeposition is made from a bath comprising a solution of cadmium sulfate and tellurium dioxide, and having a pH of 2.5.
Claim 18
Dependent Claim
25 words
A method, as recited in claim 16, said solution being saturated with respect to tellurium dioxide and having a cadmium sulfate concentration of 1.2 molar.
Claim 19
Dependent Claim
25 words
A method, as recited in claim 16, wherein said bath is at a temperature of about 80° C. and is continuously stirred, recirculated, and filtered.
Claim 20
Independent Claim
38 words
A method, as recited in any of claims 16-18, wherein said electrodeposition is made onto a cadmium surface substrate at a constant deposition voltage of -583 mV ±5 mV with respect to a saturated silver/silver chloride reference electrode.
Claim 21
Independent Claim
31 words
A method, as recited in any of claims 16-18, wherein said cadmium telluride film is treated, following electrodeposition, by impressing a positive voltage thereon while immersing it in an alkaline solution.
Claim 22
Independent Claim
37 words
A method, as recited in any of claims 16-18, wherein said cadmium telluride film has deposited on it a barrier layer and is treated by impressing a negative voltage thereon while immersing it in an alkaline solution.
Claim 23
Dependent Claim
36 words
A method, as recited in claim 21, wherein said alkaline solution comprises ammonium hydroxide and potassium hydroxide and said treatment is carried out for about 5-30 seconds at a current of about 3 mA/cm 2 .
Claim 24
Independent Claim
24 words
A method as recited in any of claims 16-18, wherein said cadmium telluride film is treated following electrodeposition by immersion in an alkaline solution.
Claim 25
Independent Claim
28 words
A method as recited in any of claims 16-18, wherein said cadmium telluride film is treated following electrodeposition by immersion in a 25 weight % potassium hydroxide solution.
Claim 26
Independent Claim
36 words
A method, as recited in any of claims 16-18, wherein said cadmium telluride film is treated, following electrodeposition, by treatment in a hot propane flame for a period of time from 1/4 second to 3 seconds.
Claim 27
Independent Claim
48 words
A method, as recited in any of claims 16-18, wherein said electrodeposited cadmium telluride film is first annealed in a nitrogen atmosphere at about 250° C. for about 60 minutes, the barrier layer is formed and the finished photovoltaic cell is then immersed in hydrazine for 1-20 minutes.
Claim 28
Independent Claim
52 words
A method, as recited in any of claims 16-18, wherein said electrodeposited cadmium telluride film is first annealed in air at about 300° for about 60 minutes the barrier layer is formed and the finished photovoltaic cell immersed in potassium hydroxide for 5-15 minutes, and then immersed in hydrazine for 1-20 minutes.
Claim 29
Dependent Claim
31 words
A method, as recited in claim 1, wherein said electrodeposition is carried out at a constant voltage of -538 mV ±5 mV with respect to a saturated silver/silver chloride reference electrode.
Claim 30
Dependent Claim
42 words
A method, as recited in claim 1, wherein said cadmium telluride is electrodeposited on a substrate formed by polishing stainless steel, electroplating gold onto said stainless steel and then electrodepositing cadmium onto said gold from a cadmium cyanide bath at room temperature.
Claim 31
Dependent Claim
28 words
A method, as recited in claim 29, wherein said stainless steel is polished using 1-0.1 micron alumina abrasive on a wet polishing wheel to provide a mirror finish.
Claim 32
Dependent Claim
58 words
A method, as recited in claim 29, wherein said stainless steel is polished by immersion in a concentrated phosphoric acid solution at 50°-60° C. and then is made anodic with respect to a carbon cathode using a constant voltage power supply to provide a current of about 3-5 Amperes per 25 cm 2 surface while agitating the electrolyte.
Claim 33
Dependent Claim
37 words
A method, as recited in claim 1, wherein said cadmium telluride is electrodeposited on a substrate formed by polishing cold rolled steel and then electrodepositing cadmium onto said steel from a cadmium cyanide bath at room temperature.
Claim 34
Dependent Claim
24 words
A method, as recited in claim 1, wherein said cadmium telluride film is treated, following electrodeposition, by annealing in an oxidizing atmosphere or nitrogen.
Claim 35
Dependent Claim
37 words
A method, as rectied in claim 1, wherein said cadimum telluride is deposited from a bath, said bath, having a pH of about 11-13, includes 2-15 g/l cadmium (II) ions 5-30 g/l tellurium(IV) ions and cyanide ions.
Claim 36
Dependent Claim
33 words
A method, as recited in claim 34, wherein said cadmium ions are provided by a water soluble cadmium compound from the group consisting of cadmium chloride, cadmium sulfate, cadmium oxide and cadmium hydroxide.
Claim 37
Dependent Claim
34 words
A method, as recited in claim 34, wherein said cadmium ions are provided in said bath by the inclusion therein of soluble cadmium compounds from the group consisting of cadmium oxide and cadmium hydroxide.
Claim 38
Dependent Claim
22 words
A method, as recited in claim 34, wherein said tellurium ions are provided by the inclusion in said bath of tellurium dioxide.
Claim 39
Dependent Claim
17 words
A method, as recited in claim 34, wherein said bath also includes buffer compounds to control pH.
Claim 40
Dependent Claim
24 words
A method, as recited in claim 34, wherein said electrodeposition is carried out at a current density from 0.1 to 7.0 mA/cm 2 .
Claim 41
Dependent Claim
34 words
A method, as recited in claim 34, wherein said cyanide ions are present in the amount of about 0.5-0.9 moles per liter and cadmium (II) is present in an amount of about 3 g/l.
Claim 42
Dependent Claim
49 words
A method, as recited in claim 34, wherein said electrodeposition is carried out at a temperature of 50° to 90° C., at a cathode voltage with respect to a saturated silver silver chloride reference electrode of 1200 to 1400 mV for a time on the order of 10-30 minutes.
Claim 43
Dependent Claim
29 words
A method, as recited in claim 34 wherein said electrodeposition is carried out at a temperature of 50°-90° C. at a constant current density of 1-4 mA/cm 2 .
Claim 44
Dependent Claim
72 words
In a method of making a photovoltaic cell which includes the step of electrodepositing a cadmium telluride layer on a substrate, the improvement comprising, forming a composite substrate, said composite substrate having a rest potential which is positive relative to the potential required for the substantially stoichiometric electrodeposition of cadmium telluride, and electrodepositing a substantially stoichiometric layer of cadmium telluride on the surface of said composite substrate to form an ohmic junction.
Claim 45
Dependent Claim
72 words
In a method of making a photovoltaic cell which includes the step of electrodepositing a cadmium telluride layer on a substrate, the improvement comprising, forming a composite substrate, said composite substrate having a rest potential which is positive relative to the potential required for the substantially stoichiometric electrodeposition of cadmium telluride, and electrodepositing a substantially stoichiometric layer of cadmium telluride on the surface of said composite substrate to form an ohmic junction.
Claim 46
Dependent Claim
30 words
The method of claim 43 wherein said composite substrate has a cadmium surface layer and said ohmic junction is formed between said cadmium surface layer and said cadmium telluride layer.
Claim 47
Dependent Claim
25 words
A method, as recited in claim 44, wherein said substrate consists of a polished stainless base with a thin gold coating and a cadmium overcoating.
Claim 48
Dependent Claim
24 words
A method, as recited in claim 44, wherein a gold barrier layer, forming a rectifying junction with said cadmium telluride film, is deposited thereon.
Claim 49
Dependent Claim
17 words
A method, as recited in claim 46, wherein said gold barrier layer is formed by vapor deposition.
Claim 50
Dependent Claim
24 words
A method, as recited in claim 43, wherein a gold barrier layer, forming a rectifying junction with said cadmium telluride film, is deposited thereon.
Claim 51
Dependent Claim
17 words
A method, as recited in claim 48, wherein said gold barrier layer is formed by vapor deposition.
Claim 52
Dependent Claim
53 words
A method, as recited in claim 43, wherein said electrodeposited cadmium telluride layer is treated, following deposition by exposure to one or more of the following: hydrogen at elevated temperature, nitrogen at elevated temperature, air at elevated temperature, chemical etching, hydrazine, flame, immersion in an alkaline solution and electrolytic treatment in alkaline solution.
Claim 53
Dependent Claim
38 words
A method, as recited in claim 43, wherein said deposition process is started by immersion of the substrate under constant voltage changing to constant current control, and removal of the substrate from the bath under constant voltage control.
References Cited (Backward Citations)
US3419484A
Cited
US3887446A
Cited
GB1532616A
Cited
US4127449A
Cited
DE2844712A1
Cited
US4204933A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-04-13 | 1984-10-13 | 1985-04-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-04-13 | 1988-10-13 | 1989-04-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-04-13 | 1992-10-13 | 1993-04-14 | $7700.00 | Window Closed / Lapsed |