US4260432A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method for producing copper based spinodal alloys
Assignee: AT&T Inc
•
Filing: 1979-01-10
•
Granted: 1981-04-07
•
Expires: 1999-01-10
Abstract
Abstract Alloys are disclosed which contain Cu, Ni, Sn, and prescribed amounts of Mo, Nb, Ta, V, or Fe. A predominantly spinodal structure is developed in such alloys by a treatment which requires annealing, quenching, and aging, and which does not require cold working to develop alloy properties. The shape of articles made from such alloys may be as cast, forged, extruded, hot worked, hot pressed, or cold worked. Shaped articles are strong, ductile, and have isotropic formability.
Inventors
- 👤 John T. Plewes
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 16:04
CPC Classifications
C; C22; C22F; C22F1/00; C22F1/08
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
254 words
A method for manufacturing a body of a predominantly spinodal alloy by a treatment of an initial body which, in an amount of at least 95 percent by weight, consists of Cu, Ni, Sn, and at least one additional element, Ni being present in said alloy in an amount of from 3-20 weight percent, Sn being present in said alloy in an amount of from 3.5-10 weight percent at 3 percent Ni to from 3.5-12 weight percent at 20 percent Ni, and characterized in that (1) said additional element is selected from the group consisting of Mo in an amount of 0.02-0.07 weight percent at 3 percent Ni to 0.05-0.1 weight percent at 20 percent Ni, Nb in an amount of 0.05-0.3 weight percent at 3 percent Ni to 0.08-0.35 weight percent at 20 percent Ni, Ta in an amount of 0.02-0.1 weight percent at 3 percent Ni to 0.05-0.3 weight percent at 20 percent Ni, V in an amount of 0.1-0.5 weight percent at 3 percent Ni to 0.2-0.5 weight percent at 20 percent Ni, and Fe in an amount of 1-5 weight percent at 3 percent Ni to 2-7 weight percent at 20 percent Ni, and (2) said treatment comprises the steps, carried out in the order stated, of (a) short term, low temperature annealing to form a solid solution of the Cu-Ni-Sn component of said alloy and to precipitate said additional element, (b) rapid quenching, (c) cold working in an amount of less than 25 percent area reduction, and (d) aging.
Claim 2
Independent Claim
254 words
A method for manufacturing a body of a predominantly spinodal alloy by a treatment of an initial body which, in an amount of at least 95 percent by weight, consists of Cu, Ni, Sn, and at least one additional element, Ni being present in said alloy in an amount of from 3-20 weight percent, Sn being present in said alloy in an amount of from 3.5-10 weight percent at 3 percent Ni to from 3.5-12 weight percent at 20 percent Ni, and characterized in that (1) said additional element is selected from the group consisting of Mo in an amount of 0.02-0.07 weight percent at 3 percent Ni to 0.05-0.1 weight percent at 20 percent Ni, Nb in an amount of 0.05-0.3 weight percent at 3 percent Ni to 0.08-0.35 weight percent at 20 percent Ni, Ta in an amount of 0.02-0.1 weight percent at 3 percent Ni to 0.05-0.3 weight percent at 20 percent Ni, V in an amount of 0.1-0.5 weight percent at 3 percent Ni to 0.2-0.5 weight percent at 20 percent Ni, and Fe in an amount of 1-5 weight percent at 3 percent Ni to 2-7 weight percent at 20 percent Ni, and (2) said treatment comprises the steps, carried out in the order stated, of (a) short term, low temperature annealing to form a solid solution of the Cu-Ni-Sn component of said alloy and to precipitate said additional element, (b) rapid quenching, (c) cold working in an amount of less than 25 percent area reduction, and (d) aging.
Claim 3
Dependent Claim
19 words
Method of claim 1 in which cold working is in an amount of less than 20 percent area reduction.
Claim 4
Dependent Claim
19 words
Method of claim 2 in which cold working is in an amount of less than 15 percent area reduction.
Claim 5
Dependent Claim
21 words
A method of claim 1 in which aging is at temperatures in the range of from 300° C. to 475° C.
Claim 6
Dependent Claim
24 words
Method of claim 1 in which said treatment terminates in the sequential steps of annealing, quenching, cold working, aging, quenching, cold working, and aging.
Claim 7
Dependent Claim
141 words
Method of claim 1 in which said additional element is selected from the group consisting of Mo, Nb, Ta, and V and in which said initial body is cast from a final melt which is prepared by providing a first melt of constituent elements Cu and Ni, placing a cover of dry graphite on said first melt, bubbling an inert gas through said first melt, adding constituent element Sn to said first melt to obtain a second melt of Cu, Ni, and Sn, adding to said second melt an amount of Mn in the range of from 0.1 to 0.3 weight percent and an amount of Mg in the range of from 0.05 to 0.1 weight percent to obtain a third melt, and plunging into said third melt a fourth constituent element selected from said group to obtain said final melt.
Claim 8
Dependent Claim
27 words
Method of claim 6 in which said fourth constituent element is plunged into said third melt in the form of a low melting eutectic mixture with Ni.
Claim 9
Dependent Claim
14 words
A method of claim 1 in which quenching is water quenching or brine quenching.
References Cited (Backward Citations)
US4073667A
Cited
US4052204A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-04-06 | 1984-10-06 | 1985-04-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-04-06 | 1988-10-06 | 1989-04-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-04-06 | 1992-10-06 | 1993-04-07 | $7700.00 | Window Closed / Lapsed |