US4257932A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Curable compositions and process
Assignee: General Electric Co
•
Filing: 1979-08-28
•
Granted: 1981-03-24
•
Expires: 1999-08-28
Abstract
Abstract Self-bonding one-package room temperature vulcanizing silicone compositions, curable in the presence of moisture to rubbery materials, comprise (a) a silanol chain-stopped polydiorganopolysiloxane; (b) a fluid polysiloxane having a high degree of tri- and/or tetrafunctionality; (c) a silica filler; (d) a cross-linking silane evolving relatively low volatility carboxylic acid fragments on hydrolysis; and (e) a highly reactive tin-containing silanol condensation catalyst. Such compositions can be applied to a variety of difficulty bondable substrates. They are especially useful when subjected to hot oil environments, as in automobile engines. High temperature performance is markedly improved with the addition of an iron oxide thermal stabilizer. Gasketed constructions and methods for forming them are also disclosed.
Inventors
- 👤 Melvin D. Beers
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 19:12
CPC Classifications
C; C08; C08L; C08L83/00; C08L83/04; C08K; C08K3/00; C08K3/18; C08K3/20; C08K3/22; C08K3/34; C08K3/36; C08K5/00; C08K5/54; C08K5/56; C08K5/57; C08G; C08G77/00; C08G77/04; C08G77/12; C08G77/14; C08G77/16; C08G77/22; C08G77/24; C08G77/26; C08G77/70; Y; Y10; Y10S; Y10S528/00; Y10S528/901; Y10T; Y10T428/00; Y10T428/31504; Y10T428/31652; Y10T428/31663
Claims Analysis
Total Claims: 48
Claim 1
Independent Claim
278 words
A fluid composition stable under substantially anhydrous conditions and curable in the presence of moisture to a self-bonding highly thermally stable elastic solid resistant to hot hydrocarbon oils, said composition comprising: (a) 100 parts by weight of a silanol chain-stopped polydiorganosiloxane of the formula: ##STR6## wherein R and R 1 are each, independently, organic radicals of up to 8 carbon atoms selected from hydrocarbyl, halohydrocarbyl and cyano lower alkyl and n is an average number of from about 10 to 15,000; (b) from 2 to 20 parts by weight of a fluid polysiloxane containing a high degree of trifunctionality, tetrafunctionality or a mixture of tri- and tetrafunctionality and comprising (i) from 25 to 60 mole percent of monoalkylsiloxy units, siloxy units or a mixture of such units; (ii) from 1 to 6 mole percent of trialkylsiloxy units; and (iii) from 34 to 74 mole percent of dialkylsiloxy units, said polysiloxane containing from about 0.1 to about 2% by weight of silicon-bonded hydroxyl groups; (c) from 10 to 100 parts by weight of a finely divided silica filler; (d) from 3 to 10 parts by weight of a cross-linking silane of the formula: R.sub.m.sup.2 Si (OR.sup.3).sub.4-m wherein R 2 has the values defined from R and R 1 hereinabove, R 3 is an organic radical of 6 to 30 carbon atoms selected from hydrocarboyl and halohydrocarboyl and m has a value of 0 or 1; and (e) from 0.01 to 10 parts by weight of a curing catalyst of the group consisting of an organic tin salt of an organic acid and a tin salt of an organic acid, said organic acid containing from 2 to 6 carbon atoms.
Claim 2
Dependent Claim
278 words
A fluid composition stable under substantially anhydrous conditions and curable in the presence of moisture to a self-bonding highly thermally stable elastic solid resistant to hot hydrocarbon oils, said composition comprising: (a) 100 parts by weight of a silanol chain-stopped polydiorganosiloxane of the formula: ##STR6## wherein R and R 1 are each, independently, organic radicals of up to 8 carbon atoms selected from hydrocarbyl, halohydrocarbyl and cyano lower alkyl and n is an average number of from about 10 to 15,000; (b) from 2 to 20 parts by weight of a fluid polysiloxane containing a high degree of trifunctionality, tetrafunctionality or a mixture of tri- and tetrafunctionality and comprising (i) from 25 to 60 mole percent of monoalkylsiloxy units, siloxy units or a mixture of such units; (ii) from 1 to 6 mole percent of trialkylsiloxy units; and (iii) from 34 to 74 mole percent of dialkylsiloxy units, said polysiloxane containing from about 0.1 to about 2% by weight of silicon-bonded hydroxyl groups; (c) from 10 to 100 parts by weight of a finely divided silica filler; (d) from 3 to 10 parts by weight of a cross-linking silane of the formula: R.sub.m.sup.2 Si (OR.sup.3).sub.4-m wherein R 2 has the values defined from R and R 1 hereinabove, R 3 is an organic radical of 6 to 30 carbon atoms selected from hydrocarboyl and halohydrocarboyl and m has a value of 0 or 1; and (e) from 0.01 to 10 parts by weight of a curing catalyst of the group consisting of an organic tin salt of an organic acid and a tin salt of an organic acid, said organic acid containing from 2 to 6 carbon atoms.
Claim 3
Dependent Claim
26 words
A composition as defined in claim 1 which also includes from 1 to 10 parts by weight of (f) a finely divided iron oxide thermal stabilizer.
Claim 4
Dependent Claim
25 words
A composition as defined in claim 1 wherein the viscosity of component (a) is within the range of 2,000 to 200,000 cps. at 25° C.
Claim 5
Dependent Claim
25 words
A composition as defined in claim 3 wherein the viscosity of component (a) is within the range of 2,000 to 30,000 cps. at 25° C.
Claim 6
Dependent Claim
34 words
A composition as defined in claim 1 wherein, in component (a), at least 50% of the total number of R and R 1 groups are alkyl radicals and any remaining groups are aryl radicals.
Claim 7
Dependent Claim
22 words
A composition as defined in claim 5 wherein the alkyl radicals are methyl radicals and any remaining aryl radicals are phenyl radicals.
Claim 8
Dependent Claim
25 words
A composition as defined in claim 1 wherein the viscosity of component (b) is in the range of 30 to 5,000 cps. at 25° C.
Claim 9
Dependent Claim
37 words
A composition as defined in claim 1 wherein, in component (b), at least 50 percent of the alkyl substituents are methyl radicals and the fluid comprises from 0.2 to 0.6 percent by weight of silicon-bonded hydroxyl groups.
Claim 10
Dependent Claim
59 words
A composition as defined in claim 8 wherein, in component (b), the monoalkylsiloxy units, siloxy units or mixed such units comprise about 35 to 45 mole percent, the trialkylsiloxy units comprise from 3 to 5 mole percent, the dialkylsiloxy units comprise from 45 to 67 mole percent, and the silicon-bonded hydroxyl content is about 0.2 to 0.5% by weight.
Claim 11
Dependent Claim
47 words
A composition as defined in claim 1 wherein the finely divided silica component (c) has been treated with dimethylcyclic siloxanes, has a surface area of about 200 square meters/gram and comprises about 20 to 30 parts by weight per 100 parts by weight of the total composition.
Claim 12
Dependent Claim
36 words
A composition as defined in claim 1 wherein in component (d), at least 50% of the total number of R 2 groups are alkyl radicals and any remaining groups are aryl radicals and m is 1.
Claim 13
Dependent Claim
22 words
A composition as defined in claim 11 wherein the alkyl radicals are methyl radicals and any remaining aryl radicals are phenyl radicals.
Claim 14
Dependent Claim
15 words
A composition as defined in claim 11 wherein the R 3 groups are 2-ethylhexanoxy radicals.
Claim 15
Dependent Claim
15 words
A composition as defined in claim 11 wherein the R 3 groups are benzoxy radicals.
Claim 16
Dependent Claim
27 words
A composition as defined in claim 1 wherein catalyst component (e), is an organic tin salt of an organic acid containing from 2 to 6 carbon atoms.
Claim 17
Dependent Claim
12 words
A composition as defined in claim 15 wherein said catalyst is dibutyltindiacetate.
Claim 18
Dependent Claim
38 words
A composition as defined in claim 2 wherein iron oxide component (f) has a pH range of 6.0 to 7.5 and comprises about 3 to 6 parts by weight per 100 parts by weight of the total composition.
Claim 19
Dependent Claim
201 words
A fluid composition highly thermally stable and stable under substantially anhydrous conditions and curable in the presence of moisture to a self-bonding elastic solid resistant to hot hydrocarbon oils, said composition comprising: (a) 100 parts by weight of a silanol chain-stopped polydiorgnosiloxane of the formula: ##STR7## wherein n is 100 to 3,000; (b) from 5 to 15 parts by weight of a fluid polymethylsiloxane containing a high degree of trifunctionality, and comprising: (i) from 35 to 45 mole percent of methylsiloxy units; (ii) from 3 to 5 mole percent of trimethylsiloxy units; and (iii) from 50 to 62 mole percent of dimethylsiloxy units, and from about 0.2 to about 0.6 percent by weight of silicon-bonded hydroxyl groups; (c) from 20 to 30 parts by weight of a finely divided fumed silica filler having a surface area of about 200 square meters per gram; (d) from 5 to 7 parts of a cross-linking silane of the formula (CH.sub.3).sub.m Si (OR.sup.3).sub.4-m wherein R 3 is hydrocarboyl of from 6 to 10 carbon atoms and m is 0 or 1; and (e) from 0.02 to 5 parts by weight of an organotin salt of an organic acid of from 2 to 6 carbon atoms.
Claim 20
Dependent Claim
201 words
A fluid composition highly thermally stable and stable under substantially anhydrous conditions and curable in the presence of moisture to a self-bonding elastic solid resistant to hot hydrocarbon oils, said composition comprising: (a) 100 parts by weight of a silanol chain-stopped polydiorgnosiloxane of the formula: ##STR7## wherein n is 100 to 3,000; (b) from 5 to 15 parts by weight of a fluid polymethylsiloxane containing a high degree of trifunctionality, and comprising: (i) from 35 to 45 mole percent of methylsiloxy units; (ii) from 3 to 5 mole percent of trimethylsiloxy units; and (iii) from 50 to 62 mole percent of dimethylsiloxy units, and from about 0.2 to about 0.6 percent by weight of silicon-bonded hydroxyl groups; (c) from 20 to 30 parts by weight of a finely divided fumed silica filler having a surface area of about 200 square meters per gram; (d) from 5 to 7 parts of a cross-linking silane of the formula (CH.sub.3).sub.m Si (OR.sup.3).sub.4-m wherein R 3 is hydrocarboyl of from 6 to 10 carbon atoms and m is 0 or 1; and (e) from 0.02 to 5 parts by weight of an organotin salt of an organic acid of from 2 to 6 carbon atoms.
Claim 21
Dependent Claim
35 words
A composition as defined in claim 18 which also includes (f) from 3 to 7 parts by weight of a finely divided iron oxide stabilizer having a pH in the range of 6.0 to 7.5.
Claim 22
Dependent Claim
30 words
A composition as defined in claim 2 wherein, in component (a), R and R 1 are each methyl; in component (d), R 3 is 2-ethylhexanoyl; and component (e) comprises dibutyltindiacetate.
Claim 23
Dependent Claim
25 words
A composition as defined in claim 1 wherein from 0.2 to 2 parts of an adhesion promoter per 100 parts total composition is also included.
Claim 24
Dependent Claim
13 words
A composition as defined in claim 21 wherein said adhesion promoter is glycidoxypropyltrimethoxysilane.
Claim 25
Dependent Claim
13 words
A composition as defined in claim 21 wherein said adhesion promoter is 1,3,5-tris-trimethoxysilylpropylisocyanurate.
Claim 26
Dependent Claim
35 words
A method of preparing a rubbery material which comprises preparing a composition in accordance with claim 1 under substantially anhydrous conditions and thereafter exposing the composition to moisture until it cures to a rubbery material.
Claim 27
Dependent Claim
35 words
A method of preparing a rubbery material which comprises preparing a composition in accordance with claim 2 under substantially anhydrous conditions and thereafter exposing the composition to moisture until it cures to a rubbery material.
Claim 28
Dependent Claim
292 words
An article of manufacture comprising a plurality of metal surfaced pieces, each piece having at least a part of a surface portion in close proximity to another and a gasket layer therebetween, said gasket comprising a rubbery, moisture-cured composition which is highly thermally stable comprising: (a) 100 parts by weight of a silanol chain-stopped polydiorganosiloxane of the formula: ##STR8## wherein R and R 1 are each, independently, organic radicals of up to 8 carbon atoms selected from hydrocarbyl, halohydrocarbyl and cyano lower alkyl and n is an average number of from about 10 to 15,000; (b) from 2 to 20 parts by weight of a fluid polysiloxane containing a high degree of trifunctionality, tetrafunctionality or a mixture of tri- and tetrafunctionality and comprising (i) from 25 to 60 mole percent of monoalkylsiloxy units, siloxy units or a mixture of such units; (ii) from 1 to 6 mole percent of trialkylsiloxy units; and (iii) from 34 to 74 mole percent of dialkylsiloxy units, said polysiloxane containing from about 0.1 to about 2% by weight of silicon-bonded hydroxyl groups; (c) from 10 to 100 parts by weight of a finely divided silica filler; (d) from 3 to 10 parts by weight of a cross-linking silane of the formula: R.sub.m.sup.2 Si (OR.sup.3).sub.4-m wherein R 2 has the values defined from R and R 1 hereinabove, R 3 is an organic radical of 6 to 30 carbon atoms selected from hydrocarboyl and halohydrocarboyl and m has a value of 0 or 1; and (e) from 0.01 to 10 parts by weight of a curing catalyst of the group consisting of an organic tin salt of an organic acid and a tin salt of an organic acid, said organic acid containing from 2 to 6 carbon atoms.
Claim 29
Dependent Claim
292 words
An article of manufacture comprising a plurality of metal surfaced pieces, each piece having at least a part of a surface portion in close proximity to another and a gasket layer therebetween, said gasket comprising a rubbery, moisture-cured composition which is highly thermally stable comprising: (a) 100 parts by weight of a silanol chain-stopped polydiorganosiloxane of the formula: ##STR8## wherein R and R 1 are each, independently, organic radicals of up to 8 carbon atoms selected from hydrocarbyl, halohydrocarbyl and cyano lower alkyl and n is an average number of from about 10 to 15,000; (b) from 2 to 20 parts by weight of a fluid polysiloxane containing a high degree of trifunctionality, tetrafunctionality or a mixture of tri- and tetrafunctionality and comprising (i) from 25 to 60 mole percent of monoalkylsiloxy units, siloxy units or a mixture of such units; (ii) from 1 to 6 mole percent of trialkylsiloxy units; and (iii) from 34 to 74 mole percent of dialkylsiloxy units, said polysiloxane containing from about 0.1 to about 2% by weight of silicon-bonded hydroxyl groups; (c) from 10 to 100 parts by weight of a finely divided silica filler; (d) from 3 to 10 parts by weight of a cross-linking silane of the formula: R.sub.m.sup.2 Si (OR.sup.3).sub.4-m wherein R 2 has the values defined from R and R 1 hereinabove, R 3 is an organic radical of 6 to 30 carbon atoms selected from hydrocarboyl and halohydrocarboyl and m has a value of 0 or 1; and (e) from 0.01 to 10 parts by weight of a curing catalyst of the group consisting of an organic tin salt of an organic acid and a tin salt of an organic acid, said organic acid containing from 2 to 6 carbon atoms.
Claim 30
Dependent Claim
29 words
An article of manufacture as defined in claim 26 wherein said composition also includes from 1 to 10 parts by weight of a finely divided iron oxide thermal stabilizer.
Claim 31
Independent Claim
311 words
A method comprising: (i) providing a plurality of metal surfaced pieces; (ii) applying a layer of a moisture-curable gasket-forming composition to at least a portion of at least one of the metal surfaces; (iii) bringing at least two metal surfaced pieces into proximity so as to complete the formation of a moisture-curable gasketing layer therebetween; and (iv) exposing the article of step (iii) to moisture until the gasketing layer has cured to a rubbery material, said moisture-curable gasketing composition comprising: (a) 100 parts by weight of a silanol chain-stopped polydiorganosiloxane of the formula: ##STR9## wherein R and R 1 are each, independently, organic radicals of up to 8 carbon atoms selected from hydrocarbyl, halohydrocarbyl and cyano lower alkyl and n is an average number of from about 10 to 15,000; (b) from 2 to 20 parts by weight of a fluid polysiloxane containing a high degree of trifunctionality, tetrafunctionality or a mixture of tri- and tetrafunctionality and comprising (i) from 25 to 60 mole percent of monoalkylsiloxy, siloxy units or a mixture of such units; (ii) from 1 to 6 mole percent of trialkylsiloxy units; and (iii) from 34 to 74 mole percent of dialkylsiloxy units; (c) from 10 to 100 parts by weight of a finely divided silica filler; (d) from 3 to 10 parts by weight of a cross-linking silane of the formula: R.sub.m.sup.2 Si (OR.sup.3).sub.4-m wherein R 2 has the values defined from R and R 1 hereinabove, R 3 is an organic radical of 6 to 30 carbon atoms selected from hydrocarboyl and halohydrocarboyl and m has a value of 0 or 1; and (e) from 0.01 to 10 parts by weight of a curing catalyst of the group consisting of an organic tin salt of a fatty acid and a tin salt of a fatty acid, said fatty acids containing from 2 to 6 carbon atoms.
Claim 32
Independent Claim
311 words
A method comprising: (i) providing a plurality of metal surfaced pieces; (ii) applying a layer of a moisture-curable gasket-forming composition to at least a portion of at least one of the metal surfaces; (iii) bringing at least two metal surfaced pieces into proximity so as to complete the formation of a moisture-curable gasketing layer therebetween; and (iv) exposing the article of step (iii) to moisture until the gasketing layer has cured to a rubbery material, said moisture-curable gasketing composition comprising: (a) 100 parts by weight of a silanol chain-stopped polydiorganosiloxane of the formula: ##STR9## wherein R and R 1 are each, independently, organic radicals of up to 8 carbon atoms selected from hydrocarbyl, halohydrocarbyl and cyano lower alkyl and n is an average number of from about 10 to 15,000; (b) from 2 to 20 parts by weight of a fluid polysiloxane containing a high degree of trifunctionality, tetrafunctionality or a mixture of tri- and tetrafunctionality and comprising (i) from 25 to 60 mole percent of monoalkylsiloxy, siloxy units or a mixture of such units; (ii) from 1 to 6 mole percent of trialkylsiloxy units; and (iii) from 34 to 74 mole percent of dialkylsiloxy units; (c) from 10 to 100 parts by weight of a finely divided silica filler; (d) from 3 to 10 parts by weight of a cross-linking silane of the formula: R.sub.m.sup.2 Si (OR.sup.3).sub.4-m wherein R 2 has the values defined from R and R 1 hereinabove, R 3 is an organic radical of 6 to 30 carbon atoms selected from hydrocarboyl and halohydrocarboyl and m has a value of 0 or 1; and (e) from 0.01 to 10 parts by weight of a curing catalyst of the group consisting of an organic tin salt of a fatty acid and a tin salt of a fatty acid, said fatty acids containing from 2 to 6 carbon atoms.
Claim 33
Dependent Claim
27 words
A method as defined in claim 28 wherein said composition also includes from 1 to 10 parts by weight of a finely divided iron oxide thermal stabilizer.
Claim 34
Dependent Claim
280 words
A fluid composition stable under substantially anhydrous conditions and curable in the presence of moisture to a self-bonding highly thermally stable elastic solid resistant to hot hydrocarbon oils, said composition comprising: (a) 100 parts by weight of a silanol chain-stopped polydiorganosiloxane of the formula: ##STR10## wherein R and R 1 are each, independently, organic radicals of up to 8 carbon atoms selected from hydrocarbyl, halohydrocarbyl and cyano lower alkyl and n is an average number of from about 10 to 15,000; (b) from 2 to 20 parts by weight of a fluid polysiloxane containing a high degree of triflunctionality, tetrafunctionality or a mixture of tri- and tetrafunctionality and comprising (i) from 25 to 60 mole percent of monoalkylsiloxy units, siloxy units or a mixture of such units; (ii) from 1 to 6 mole percent of trialkylsiloxy units; and (iii) from 34 to 74 mole percent of dialkylsiloxy units, said polysiloxane containing from about 0.1 to about 2% by weight of silicon-bonded hydroxyl groups; (c) from 10 to 100 parts by weight of a finely divided silica filler; (d) from 3 to 10 parts by weight of a cross-linking silane of the formula: R.sub.m.sup.2 Si (OR.sup.3).sub.4-m wherein R 2 has the values defined from R and R 1 hereinabove, R 3 is an organic radical of 6 to 30 carbon atoms selected from hydrocarboyl and halohydrocarboyl and m has a value of 0 or 1; and (e) from 0.1 to 10 parts by weight of a highly reactive curing catalyst of the group consisting of an organic tin salt of an organic acid or a tin salt of an organic acid, said organic acid containing from 2 to 12 carbon atoms.
Claim 35
Dependent Claim
280 words
A fluid composition stable under substantially anhydrous conditions and curable in the presence of moisture to a self-bonding highly thermally stable elastic solid resistant to hot hydrocarbon oils, said composition comprising: (a) 100 parts by weight of a silanol chain-stopped polydiorganosiloxane of the formula: ##STR10## wherein R and R 1 are each, independently, organic radicals of up to 8 carbon atoms selected from hydrocarbyl, halohydrocarbyl and cyano lower alkyl and n is an average number of from about 10 to 15,000; (b) from 2 to 20 parts by weight of a fluid polysiloxane containing a high degree of triflunctionality, tetrafunctionality or a mixture of tri- and tetrafunctionality and comprising (i) from 25 to 60 mole percent of monoalkylsiloxy units, siloxy units or a mixture of such units; (ii) from 1 to 6 mole percent of trialkylsiloxy units; and (iii) from 34 to 74 mole percent of dialkylsiloxy units, said polysiloxane containing from about 0.1 to about 2% by weight of silicon-bonded hydroxyl groups; (c) from 10 to 100 parts by weight of a finely divided silica filler; (d) from 3 to 10 parts by weight of a cross-linking silane of the formula: R.sub.m.sup.2 Si (OR.sup.3).sub.4-m wherein R 2 has the values defined from R and R 1 hereinabove, R 3 is an organic radical of 6 to 30 carbon atoms selected from hydrocarboyl and halohydrocarboyl and m has a value of 0 or 1; and (e) from 0.1 to 10 parts by weight of a highly reactive curing catalyst of the group consisting of an organic tin salt of an organic acid or a tin salt of an organic acid, said organic acid containing from 2 to 12 carbon atoms.
Claim 36
Dependent Claim
26 words
A composition as defined in claim 30 which also includes from 1 to 10 parts by weight of (f) a finely divided iron oxide thermal stabilizer.
Claim 37
Dependent Claim
13 words
A composition as defined in claim 30 wherein said catalyst is dimethyltin bis-neodecanoate.
Claim 38
Dependent Claim
203 words
A fluid composition highly thermally stable and stable under substantially anhydrous conditions and curable in the presence of moisture to a self-bonding elastic solid resistant to hot hydrocarbon oils, said composition comprising: (a) 100 parts by weight of a silanol chain-stopped polydiorganosiloxane of the formula: ##STR11## wherein n is 100 to 3,000; (b) from 5 to 15 parts by weight of a fluid polymethylsiloxane containing a high degree of trifunctionality, and comprising: (i) from 35 to 45 mole percent of methylsiloxy units; (ii) from 3 to 5 mole percent of trimethylsiloxy units; and (iii) from 50 to 62 mole percent of dimethylsiloxy units, and from about 0.2 to about 0.6 percent by weight of silicon-bonded hydroxyl groups; (c) from 20 to 30 parts by weight of a finely divided fumed silica filler having a surface area of about 200 square meters per gram; (d) from 5 to 7 parts of a cross-linking silane of the formula (CH.sub.3).sub.m Si (OR.sup.3).sub.4-m wherein R 3 is hydrocarboyl of from 6 to 10 carbon atoms and m is 0 or 1; and (e) from 0.02 to 5 parts by weight of a highly reactive organotin salt of an organic acid of from 2 to 12 carbon atoms.
Claim 39
Dependent Claim
203 words
A fluid composition highly thermally stable and stable under substantially anhydrous conditions and curable in the presence of moisture to a self-bonding elastic solid resistant to hot hydrocarbon oils, said composition comprising: (a) 100 parts by weight of a silanol chain-stopped polydiorganosiloxane of the formula: ##STR11## wherein n is 100 to 3,000; (b) from 5 to 15 parts by weight of a fluid polymethylsiloxane containing a high degree of trifunctionality, and comprising: (i) from 35 to 45 mole percent of methylsiloxy units; (ii) from 3 to 5 mole percent of trimethylsiloxy units; and (iii) from 50 to 62 mole percent of dimethylsiloxy units, and from about 0.2 to about 0.6 percent by weight of silicon-bonded hydroxyl groups; (c) from 20 to 30 parts by weight of a finely divided fumed silica filler having a surface area of about 200 square meters per gram; (d) from 5 to 7 parts of a cross-linking silane of the formula (CH.sub.3).sub.m Si (OR.sup.3).sub.4-m wherein R 3 is hydrocarboyl of from 6 to 10 carbon atoms and m is 0 or 1; and (e) from 0.02 to 5 parts by weight of a highly reactive organotin salt of an organic acid of from 2 to 12 carbon atoms.
Claim 40
Dependent Claim
35 words
A composition as defined in claim 18 which also includes (f) from 3 to 7 parts by weight of a finely divided iron oxide stabilizer having a pH in the range of 6.0 to 7.5.
Claim 41
Dependent Claim
35 words
A method of preparing a rubbery material which comprises preparing a composition in accordance with claim 30 under substantially anhydrous conditions and thereafter exposing the composition to moisture until it cures to a rubbery material.
Claim 42
Dependent Claim
35 words
A method of preparing a rubbery material which comprises preparing a composition in accordance with claim 31 under substantially anhydrous conditions and thereafter exposing the composition to moisture until it cures to a rubbery material.
Claim 43
Dependent Claim
294 words
An article of manufacture comprising a plurality of metal surfaced pieces, each piece having at least a part of a surface portion in close proximity to another and a gasket layer therebetween, said gasket comprising a rubbery, moisture-cured composition which is highly thermally stable comprising: (a) 100 parts by weight of a silanol chain-stopped polydiorganosiloxane of the formula: ##STR12## wherein R and R 1 are each, independently, organic radicals of up to 8 carbon atoms selected from hydrocarbyl, halohydrocarbyl and cyano lower alkyl and n is an average number of from about 10 to 15,000; (b) from 2 to 20 parts by weight of a fluid polysiloxane containing a high degree of trifunctionality, tetrafunctionality or a mixture of tri- and tetrafunctionality and comprising (i) from 25 to 60 mole percent of monoalkylsiloxy units, siloxy units or a mixture of such units; (ii) from 1 to 6 mole percent of trialkylsiloxy units; and (iii) from 34 to 74 mole percent of dialkylsiloxy units, said polysiloxane containing from about 0.1 to about 2% by weight of silicon-bonded hydroxyl groups; (c) from 10 to 100 parts by weight of a finely divided silica filler; (d) from 3 to 10 parts by weight of a cross-linking silane of the formula: R.sub.m.sup.2 Si (OR.sup.3).sub.4-m wherein R 2 has the values defined from R and R 1 hereinabove, R 3 is an organic radical of 6 to 30 carbon atoms selected from hydrocarboyl and halohydrocarboyl and m has a value of 0 or 1; and (e) from 0.01 to 10 parts by weight of a highly reactive curing catalyst of the group consisting of an organic tin salt of an organic acid or a tin salt of an organic acid, said organic acid containing from 2 to 12 carbon atoms.
Claim 44
Dependent Claim
294 words
An article of manufacture comprising a plurality of metal surfaced pieces, each piece having at least a part of a surface portion in close proximity to another and a gasket layer therebetween, said gasket comprising a rubbery, moisture-cured composition which is highly thermally stable comprising: (a) 100 parts by weight of a silanol chain-stopped polydiorganosiloxane of the formula: ##STR12## wherein R and R 1 are each, independently, organic radicals of up to 8 carbon atoms selected from hydrocarbyl, halohydrocarbyl and cyano lower alkyl and n is an average number of from about 10 to 15,000; (b) from 2 to 20 parts by weight of a fluid polysiloxane containing a high degree of trifunctionality, tetrafunctionality or a mixture of tri- and tetrafunctionality and comprising (i) from 25 to 60 mole percent of monoalkylsiloxy units, siloxy units or a mixture of such units; (ii) from 1 to 6 mole percent of trialkylsiloxy units; and (iii) from 34 to 74 mole percent of dialkylsiloxy units, said polysiloxane containing from about 0.1 to about 2% by weight of silicon-bonded hydroxyl groups; (c) from 10 to 100 parts by weight of a finely divided silica filler; (d) from 3 to 10 parts by weight of a cross-linking silane of the formula: R.sub.m.sup.2 Si (OR.sup.3).sub.4-m wherein R 2 has the values defined from R and R 1 hereinabove, R 3 is an organic radical of 6 to 30 carbon atoms selected from hydrocarboyl and halohydrocarboyl and m has a value of 0 or 1; and (e) from 0.01 to 10 parts by weight of a highly reactive curing catalyst of the group consisting of an organic tin salt of an organic acid or a tin salt of an organic acid, said organic acid containing from 2 to 12 carbon atoms.
Claim 45
Dependent Claim
29 words
An article of manufacture as defined in claim 37 wherein said composition also includes from 1 to 10 parts by weight of a finely divided iron oxide thermal stabilizer.
Claim 46
Independent Claim
313 words
A method comprising: (i) providing a plurality of metal surfaced pieces; (ii) applying a layer of a moisture-curable gasket-forming composition to at least a portion of at least one of the metal surfaces; (iii) bringing at least two metal surfaced pieces into proximity so as to complete and formation of a moisture-curable gasketing layer therebetween; and (iv) exposing the article of step (iii) to moisture until the gasketing layer has cured to a rubbery material, said moisture-curable gasketing composition comprising: (a) 100 parts by weight of a silanol chain-stopped polydiorganosiloxane of the formula: ##STR13## wherein R and R 1 are each, independently, organic radicals of up to 8 carbon atoms selected from hydrocarbyl, halohydrocarbyl and cyano lower alkyl and n is an average number of from about 10 to 15,000; (b) from 2 to 20 parts by weight of a fluid polysiloxane containing a high degree of trifunctionality, tetrafunctionality or a mixture of tri- and tetrafunctionality and comprising (i) from 25 to 60 mole percent of monoalkylsiloxy, siloxy units or a mixture of such units; (ii) from 1 to 6 mole percent of trialkylsiloxy units; and (iii) from 34 to 74 mole percent of dialkylsiloxy units; (c) from 10 to 100 parts by weight of a finely divided silica filler; (d) from 3 to 10 parts by weight of a cross-linking silane of the formula: R.sub.m.sup.2 Si (OR.sup.3).sub.4-m wherein R 2 has the values defined from R and R 1 hereinabove, R 3 is an organic radical of 6 to 30 carbon atoms selected from hydrocarboyl and halohydrocarboyl and m has a value of 0 or 1; and (e) from 0.01 to 10 parts by weight of a highly reactive curing catalyst of the group consisting of an organic tin salt of a fatty acid or a tin salt of a fatty acid, said fatty acid containing from 2 to 12 carbon atoms.
Claim 47
Independent Claim
313 words
A method comprising: (i) providing a plurality of metal surfaced pieces; (ii) applying a layer of a moisture-curable gasket-forming composition to at least a portion of at least one of the metal surfaces; (iii) bringing at least two metal surfaced pieces into proximity so as to complete and formation of a moisture-curable gasketing layer therebetween; and (iv) exposing the article of step (iii) to moisture until the gasketing layer has cured to a rubbery material, said moisture-curable gasketing composition comprising: (a) 100 parts by weight of a silanol chain-stopped polydiorganosiloxane of the formula: ##STR13## wherein R and R 1 are each, independently, organic radicals of up to 8 carbon atoms selected from hydrocarbyl, halohydrocarbyl and cyano lower alkyl and n is an average number of from about 10 to 15,000; (b) from 2 to 20 parts by weight of a fluid polysiloxane containing a high degree of trifunctionality, tetrafunctionality or a mixture of tri- and tetrafunctionality and comprising (i) from 25 to 60 mole percent of monoalkylsiloxy, siloxy units or a mixture of such units; (ii) from 1 to 6 mole percent of trialkylsiloxy units; and (iii) from 34 to 74 mole percent of dialkylsiloxy units; (c) from 10 to 100 parts by weight of a finely divided silica filler; (d) from 3 to 10 parts by weight of a cross-linking silane of the formula: R.sub.m.sup.2 Si (OR.sup.3).sub.4-m wherein R 2 has the values defined from R and R 1 hereinabove, R 3 is an organic radical of 6 to 30 carbon atoms selected from hydrocarboyl and halohydrocarboyl and m has a value of 0 or 1; and (e) from 0.01 to 10 parts by weight of a highly reactive curing catalyst of the group consisting of an organic tin salt of a fatty acid or a tin salt of a fatty acid, said fatty acid containing from 2 to 12 carbon atoms.
Claim 48
Dependent Claim
27 words
A method as defined in claim 39 wherein said composition also includes from 1 to 10 parts by weight of a finely divided iron oxide thermal stabilizer.
References Cited (Backward Citations)
US2938009A
Cited
US3133891A
Cited
US3004859A
Cited
US3035016A
Cited
US3065194A
Cited
US3170894A
Cited
US3122522A
Cited
US3161614A
Cited
US3175993A
Cited
US3382205A
Cited
US3294739A
Cited
US3383355A
Cited
US3334067A
Cited
US3517001A
Cited
US3542901A
Cited
US3499859A
Cited
US3635743A
Cited
US3689454A
Cited
US3779986A
Cited
US3708467A
Cited
US3719635A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-03-23 | 1984-09-22 | 1985-03-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-03-23 | 1988-09-22 | 1989-03-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-03-23 | 1992-09-22 | 1993-03-24 | $7700.00 | Window Closed / Lapsed |