US4256877A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method of manufacturing cellulose derivative
Assignee: SCA Development AB
•
Filing: 1977-12-13
•
Granted: 1981-03-17
•
Expires: 1997-12-13
Abstract
Abstract An absorbent cellulose material is disclosed which comprises a substituted cellulose having an average degree of substitution sufficiently low to render the material insoluble and in which the fibers have an increased surface area formed by bursting the fibers during drying. In addition, a method of manufacturing such absorbent material is also disclosed which comprises providing an insoluble substituted cellulose material having an average degree of substitution sufficiently low to render the material insoluble, swelling the material to its maximum swelled state, fixing the material in that state, and drying the material while maintaining the material in its swelled state to thereby prevent shrinkage of the material during drying and to cause the fibers to burst during drying.
Inventors
- 👤 Alf H. Karlsson
- 👤 Hans E. Lundstrom
- 👤 Lars-Henrik Olsson
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 20:06
CPC Classifications
C; C08; C08B; C08B11/00; C08B11/20; A; A61; A61L; A61L15/00; A61L15/16; A61L15/22; A61L15/28; C08B3/00; C08B3/22
Claims Analysis
Total Claims: 25
Claim 1
Independent Claim
63 words
An absorbent cellulose material, comprising a substituted cellulose material having an average degree of substitution sufficiently low to render said material insoluble in water, said material comprising fibers having an increased surface area formed by swelling said material, fixing said material in said swelled state, and drying said material while maintaining said material in said swelled state, thereby bursting said fibers during drying.
Claim 2
Dependent Claim
63 words
An absorbent cellulose material, comprising a substituted cellulose material having an average degree of substitution sufficiently low to render said material insoluble in water, said material comprising fibers having an increased surface area formed by swelling said material, fixing said material in said swelled state, and drying said material while maintaining said material in said swelled state, thereby bursting said fibers during drying.
Claim 3
Dependent Claim
21 words
An absorbent cellulose material according to claim 1, wherein said material has an average degree of substitution of less than 0.40.
Claim 4
Dependent Claim
37 words
An absorbent cellulose material according to claim 1 wherein said cellulose material is selected from the group comprising carboxymethyl cellulose, carboxyethylene cellulose, carboxymethylhydroxyethylene cellulose, hydroxyethylene cellulose, hydroxypropylene cellulose, methyl cellulose, cellulose sulphate, cellulose phosphate, and mixtures thereof.
Claim 5
Dependent Claim
16 words
The absorbent cellulose material of claim 1 wherein said material is combined with additional absorbent material.
Claim 6
Dependent Claim
32 words
The absorbent cellulose material of claim 4 wherein said additional material is selected from the group consisting of cellulose wadding, chemical defibrated pulp, mechanical defibrated pulp, thermomechanical pulp, bentonite, and mixtures thereof.
Claim 7
Dependent Claim
58 words
An absorbent cellulose material, comprising a substituted cellulose material having an average degree of substitution of at most 0.40, said material comprising fibers having an increased surface area formed by swelling said material, fixing said material in said swelled state, and drying said material while maintaining said material in said swelled state, thereby bursting said fibers during drying.
Claim 8
Dependent Claim
58 words
An absorbent cellulose material, comprising a substituted cellulose material having an average degree of substitution of at most 0.40, said material comprising fibers having an increased surface area formed by swelling said material, fixing said material in said swelled state, and drying said material while maintaining said material in said swelled state, thereby bursting said fibers during drying.
Claim 9
Independent Claim
74 words
A method of manufacturing absorbent cellulose material comprising, providing a substituted cellulose material having an average degree of substitution sufficiently low to render said material insoluble in water, swelling said material to its maximum swelled state, fixing said material in said swelled state, and drying said material while maintaining said material in said swelled state, thereby preventing shrinkage of said material during drying and causing the fibers of said material to burst during drying.
Claim 10
Independent Claim
74 words
A method of manufacturing absorbent cellulose material comprising, providing a substituted cellulose material having an average degree of substitution sufficiently low to render said material insoluble in water, swelling said material to its maximum swelled state, fixing said material in said swelled state, and drying said material while maintaining said material in said swelled state, thereby preventing shrinkage of said material during drying and causing the fibers of said material to burst during drying.
Claim 11
Dependent Claim
18 words
The method of claim 7 wherein the average degree of substitution of said material is less than 0.40.
Claim 12
Dependent Claim
22 words
The method of claim 7 wherein said material is fixed by freezing said material and said material is dried by freeze drying.
Claim 13
Dependent Claim
35 words
The method of claim 7 wherein said material is fixed by applying said material to a heating roller in the form of a paste and said material is dried by applying heat to said roller.
Claim 14
Dependent Claim
34 words
The method of claim 7 wherein said cellulose material is selected from the group comprising carboxymethyl cellulose, carboxyethylene cellulose, carboxymethylhydroxyethylene cellulose, hydroxyethylene cellulose, hydroxypropylene cellulose, methyl cellulose, cellulose sulphate, cellulose phosphate, and mixtures thereof.
Claim 15
Dependent Claim
12 words
The method of claim 11 wherein said cellulose material is carboxymethyl cellulose.
Claim 16
Dependent Claim
18 words
The method of claim 7 wherein the average degree of substitution of said material is less than 0.30.
Claim 17
Dependent Claim
17 words
The method of claim 7 wherein the average substitution degree of said material is less than 0.24.
Claim 18
Dependent Claim
16 words
The method of claim 7, further comprising the step of defibrating said material subsequent to drying.
Claim 19
Dependent Claim
17 words
The method of claim 7 wherein said material is combined with additional absorbent material subsequent to drying.
Claim 20
Dependent Claim
30 words
The method of claim 16 wherein said additional material is selected from the group consisting of cellulose wadding, chemical defibrated pulp, mechanical defibrated pulp, thermomechanical pulp, bentonite, and mixtures thereof.
Claim 21
Dependent Claim
17 words
The method of claim 7 wherein said material is combined with additional absorbent material prior to drying.
Claim 22
Dependent Claim
30 words
The method of claim 18 wherein said additional material is selected from the group consisting of cellulose wadding, chemical defibrated pulp, mechanical defibrated pulp, thermomechanical pulp, bentonite, and mixtures thereof.
Claim 23
Dependent Claim
17 words
The method of claim 7 wherein said material is provided with a creped surface subsequent to drying.
Claim 24
Independent Claim
204 words
A method of manufacturing an absorbent cellulose material for use in sanitary products containing a water-insoluble cellulose derivative, which method comprises mechanically working a water-insoluble cellulose ether or a cellulose ester having an average degree of substitution of at most 0.40 in fiber form with water so as to achieve maximum swelling of the separate fibers, whereby a material in the form of a paste having approximately 10% dry content is obtained, supplying the paste to a roller nip between rollers heated by steam at a pressure of from 3.5 to 10 bars so that a film containing material in a swollen state is formed, the said film being fixed to the roller so that the separate fibers of the material are maintained in their mutual relationship which was achieved during the swelling, rapidly removing a substantial portion of the water in the paste so that the fibers burst whereby when the film is fixed onto the roller shrinkage of the material is avoided, and then removing the material which has been dried in this manner from the roller in the form of a continuous mat by means of a doctor blade, the said mat being capable of being provided with a creped surface.
Claim 25
Independent Claim
204 words
A method of manufacturing an absorbent cellulose material for use in sanitary products containing a water-insoluble cellulose derivative, which method comprises mechanically working a water-insoluble cellulose ether or a cellulose ester having an average degree of substitution of at most 0.40 in fiber form with water so as to achieve maximum swelling of the separate fibers, whereby a material in the form of a paste having approximately 10% dry content is obtained, supplying the paste to a roller nip between rollers heated by steam at a pressure of from 3.5 to 10 bars so that a film containing material in a swollen state is formed, the said film being fixed to the roller so that the separate fibers of the material are maintained in their mutual relationship which was achieved during the swelling, rapidly removing a substantial portion of the water in the paste so that the fibers burst whereby when the film is fixed onto the roller shrinkage of the material is avoided, and then removing the material which has been dried in this manner from the roller in the form of a continuous mat by means of a doctor blade, the said mat being capable of being provided with a creped surface.
References Cited (Backward Citations)
CA762553A
Cited
US962505A
Cited
GB581711A
Cited
US2602042A
Cited
US2940890A
Cited
US3005456A
Cited
GB820826A
Cited
US3525735A
Cited
GB1135936A
Cited
US3382140A
Cited
US3589364A
Cited
US3658790A
Cited
US3691154A
Cited
US3739782A
Cited
GB1391725A
Cited
US3821068A
Cited
US3919385A
Cited
US3804092A
Cited
US3997647A
Cited
US4084591A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-03-16 | 1984-09-15 | 1985-03-17 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-03-16 | 1988-09-15 | 1989-03-17 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-03-16 | 1992-09-15 | 1993-03-17 | $7700.00 | Window Closed / Lapsed |