Leaching agglomerated gold - silver ores
Assignee: United States Department of the Interior
•
Filing: 1980-04-17
•
Granted: 1981-03-17
•
Expires: 2000-04-17
Abstract
Abstract Percolation leaching of gold or silver ores, tailings or wastes is accomplished by a process comprising initial agglomeration of fines in the feed by means of a binding agent and cyanide solution, followed by aging and, subsequently, leaching to recover gold or silver values.
Inventors
- 👤 Harold J. Heinen
- 👤 Gene E. McClelland
- 👤 Roald E. Lindstrom
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 21:13
CPC Classifications
C; C22; C22B; C22B1/00; C22B1/14; C22B1/24; C22B1/242; C22B1/243; C22B11/00; C22B11/08
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
131 words
A process for percolation leaching of gold or silver values from a feed material consisting of ores, tailings or wastes comprising: (1) admixing the feed with about 0.25 to 0.75 weight percent of a binding agent consisting of lime, portland cement, or mixtures thereof, and about 8 to 16 weight percent of an aqueous cyanide solution, (2) mechanically manipulating the admixture to effect agglomeration of fines in the feed, (3) aging the admixture at ambient conditions for a time sufficient to provide the resulting agglomerates with green strength sufficient to withstand further wetting without disintegration, and for substantial reaction of the cyanide with gold or silver values in the feed, and (4) subjecting the aged admixture to percolation leaching with water or cyanide solution, whereby gold or silver is selectively leached.
Claim 2
Dependent Claim
131 words
A process for percolation leaching of gold or silver values from a feed material consisting of ores, tailings or wastes comprising: (1) admixing the feed with about 0.25 to 0.75 weight percent of a binding agent consisting of lime, portland cement, or mixtures thereof, and about 8 to 16 weight percent of an aqueous cyanide solution, (2) mechanically manipulating the admixture to effect agglomeration of fines in the feed, (3) aging the admixture at ambient conditions for a time sufficient to provide the resulting agglomerates with green strength sufficient to withstand further wetting without disintegration, and for substantial reaction of the cyanide with gold or silver values in the feed, and (4) subjecting the aged admixture to percolation leaching with water or cyanide solution, whereby gold or silver is selectively leached.
Claim 3
Dependent Claim
21 words
The process of claim 1 in which the feed material is a low-grade clayey gold or silver ore, tailing or waste.
Claim 4
Dependent Claim
13 words
The process of claim 2 in which the binding agent is portland cement.
Claim 5
Dependent Claim
16 words
The process of claim 1 in which the aging time is about 5 to 72 hours.
Claim 6
Dependent Claim
22 words
The process of claim 1 in which the aqueous cyanide solution consists of a 1.16 to 1.27 molar solution of sodium cyanide.
Claim 7
Dependent Claim
14 words
The process of claim 1 in which the percolation leaching consists of heap leaching.
Claim 8
Dependent Claim
16 words
The process of claim 1 in which the percolation leaching consists of vat or flood leaching.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-03-16 | 1984-09-15 | 1985-03-17 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-03-16 | 1988-09-15 | 1989-03-17 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-03-16 | 1992-09-15 | 1993-03-17 | $7700.00 | Window Closed / Lapsed |