Abstract
Abstract A catalyst is made by impregnating a highly microporous support with a solution of a substance providing catalytically active material in a mixture of water and an organic liquid that reduces the surface tension of the solution. The preferred solution contains 20 to 50% water and 50 to 80% methanol.
Inventors
- 👤 Robert W. Dale
- 👤 John J. Rooney
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 14:14
CPC Classifications
A; A24; A24D; A24D3/00; A24D3/06; A24D3/16; B; B01; B01D; B01D53/00; B01D53/34; B01D53/74; B01D53/86; B01J; B01J37/00; B01J37/02; B01J37/0201; B01J37/0203
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
99 words
A method of making a catalyst comprising physically adsorbing a substance providing a catalytically active metal selected from the group consisting of groups 6, 7, and 8 of the Periodic Table into a microporous support having an average pore diameter less than 30 A by contacting the support with a solution of the substance in a solvent which is a mixture of water and an organic liquid which reduces the surface tension of the solution and which is inert to said substance, and evaporating at least some of the solvent and thereby depositing the said substance in the micropores.
Claim 2
Independent Claim
99 words
A method of making a catalyst comprising physically adsorbing a substance providing a catalytically active metal selected from the group consisting of groups 6, 7, and 8 of the Periodic Table into a microporous support having an average pore diameter less than 30 A by contacting the support with a solution of the substance in a solvent which is a mixture of water and an organic liquid which reduces the surface tension of the solution and which is inert to said substance, and evaporating at least some of the solvent and thereby depositing the said substance in the micropores.
Claim 3
Dependent Claim
16 words
A method according to claim 1 in which the average pore diameter is below 16 A.
Claim 4
Dependent Claim
15 words
A method according to claim 1 in which the support material is zeolite or alumina.
Claim 5
Dependent Claim
19 words
A method according to claim 1 in which the catalytically active material is selected from platinum, palladium and rhodium.
Claim 6
Dependent Claim
20 words
A method according to claim 1 in which the catalytically active material is present in the solution in anionic form.
Claim 7
Dependent Claim
27 words
A method according to claim 1 in which the solvent in the solution consists of 20 to 50% water and 50 to 80 of the organic liquid.
Claim 8
Dependent Claim
13 words
A method according to claim 6 in which the organic liquid is methanol.
Claim 9
Dependent Claim
59 words
A method according to claim 1 in which the amount of the organic liquid is 10 to 90% by volume of the mixture and the organic liquid is inert to the catalytically active material, reduces the hydrogen bonding within the solution and between the solution and the support material and is wholly miscible with the water in the solution.
Claim 10
Dependent Claim
17 words
A method according to claim 8 in which the organic liquid is an alcohol or cyclic ether.
Claim 11
Dependent Claim
20 words
A method according to claim 8 in which the organic liquid is selected from tetrahydrofuran, methanol, ethanol, dioxan and furan.
Claim 12
Dependent Claim
20 words
A method according to claim 1 in which the support has a surface area of above 400 m 2 /g.
Claim 13
Dependent Claim
25 words
A method according to claim 1 in which the support material has been activated by generating on its surfaces having a deficiency of hydroxyl groups.
Claim 14
Dependent Claim
15 words
A method according to claim 1 in which the substance is subsequently reduced by carbonmonoxide.
Claim 15
Dependent Claim
10 words
A catalyst made by a method according to claim 1.
Claim 16
Dependent Claim
65 words
A method according to claim 1 in which the amount of solvent that is evaporated is at least 50% by volume of the amount of solution that is contacted with the support and the amount of the said substance present in the solution that is contacted with the support is less than about 2.5%, calculated as the metal, based on the weight of the support.
Claim 17
Dependent Claim
26 words
A method according to claim 1 in which the initial concentration of the substance in the solution is from 0.01 to 0.2% by weight catalytic metal.
Claim 18
Dependent Claim
14 words
A method according to claim 1 in which substantially all the solvent is evaporated.
Claim 19
Dependent Claim
20 words
A method according to claim 1 in which the evaporation is continued for a period of at least 10 hours.
Claim 20
Dependent Claim
140 words
In a process for making a catalyst comprising depositing on a porous refractory support material a solution of a substance providing a catalytically active metallic material comprising a metal of groups 6, 7 or 8 of the Periodic Table and converting said substance to said catalytically active metallic material, the improvement comprising making a more active catalyst by using a microporous support material having an average pore diameter of less than 30 A and physically adsorbing a solution of said substance in a mixture of water and 10 to 90% by volume of an inert organic liquid selected from the group comprising tetrahydrofuran, methanol, ethanol, dioxan and furan into said support material and evaporating at least 50% by volume of solvent, based on the volume of said solution, to thereby deposit said substance in the micropores of said support material.
Claim 21
Dependent Claim
140 words
In a process for making a catalyst comprising depositing on a porous refractory support material a solution of a substance providing a catalytically active metallic material comprising a metal of groups 6, 7 or 8 of the Periodic Table and converting said substance to said catalytically active metallic material, the improvement comprising making a more active catalyst by using a microporous support material having an average pore diameter of less than 30 A and physically adsorbing a solution of said substance in a mixture of water and 10 to 90% by volume of an inert organic liquid selected from the group comprising tetrahydrofuran, methanol, ethanol, dioxan and furan into said support material and evaporating at least 50% by volume of solvent, based on the volume of said solution, to thereby deposit said substance in the micropores of said support material.
Claim 22
Dependent Claim
11 words
Process of claim 19, wherein said metal is a noble metal.
References Cited (Backward Citations)
US2874129A
Cited
US2930765A
Cited
US2865867A
Cited
US3033778A
Cited
US3264208A
Cited
US3434479A
Cited
US3657151A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-03-16 | 1984-09-15 | 1985-03-17 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-03-16 | 1988-09-15 | 1989-03-17 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-03-16 | 1992-09-15 | 1993-03-17 | $7700.00 | Window Closed / Lapsed |