Abstract
Abstract A process for preparing acicular gamma ferric oxide (maghemite) crystals exhibiting excellent magnetic recording properties is disclosed. These acicular gamma ferric oxide crystals are new materials and can be used in magnetic media such as magnetic tapes to obtain a low level of white noise without sacrificing other electroacoustic properties. The crystals are basic in character, contain alkali metal ions and have an acicularity ratio of at least 15, often 15 to 40. These crystals are prepared under very carefully controlled reaction conditions, as more fully described in the following specification. In general, however, the process involves (1) reacting ferrous salt with a stoichiometric excess of an alkali hydroxide under non-oxidizing conditions and at a temperature below about 60° C. while substantially avoiding local excesses of the ferrous salt, to form an aqueous dispersion of ferrous hydroxide particles, (2) introducing oxygen into the dispersion to convert the ferrous hydroxide particles to crystals of alpha ferric oxide hydrate, (3) discontinuing introduction of the oxygen into the dispersion, (4) boiling the dispersion to obtain further crystallization of the alpha ferric oxide hydrate crystals and subjecting the crystals to dehydration, reduction and oxidation to form gamma ferric oxide crystals. As indicated in the specification, failure to observe the reaction conditions set out in the specification and claims deleteriously affects the magnetic recording properties of the gamma ferric oxide crystals. Additional doping ions such as alkaline earth metal ions and/or other ions of metals such as cobalt, nickel, chromium, zinc, manganese or calcium can be introduced into the gamma ferric oxide crystals during their preparation to further improve properties for magnetic recording. Products which are useful in magnetic recording such as magnetic tapes, discs, drums and striped motion picture film containing the acicular gamma ferric oxide crystals are disclosed.
Inventors
- 👤 Roger G. L. Audran
- 👤 Bernard J. Pingaud
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 13:44
CPC Classifications
G; G11; G11B; G11B5/00; G11B5/62; G11B5/68; G11B5/70; G11B5/706; G11B5/70626; G11B5/70642; G11B5/70652; C; C01; C01G; C01G49/00; C01G49/02; C01G49/06; G11B5/70647; C01P; C01P2004/00; C01P2004/01; C01P2004/03; C01P2004/10; C01P2004/54; C01P2004/60; C01P2004/62; C01P2006/00; C01P2006/42; Y; Y10; Y10S; Y10S428/00; Y10S428/90
Claims Analysis
Total Claims: 27
Claim 1
Independent Claim
45 words
Gamma ferric oxide consisting essentially of crystals that have an acicularity ratio of at least 15 and an average crystal length less than 0.5 micron and which comprise alkali metal ions that impart a basicity of at least 0.04 meq. per gram to said oxide.
Claim 2
Dependent Claim
45 words
Gamma ferric oxide consisting essentially of crystals that have an acicularity ratio of at least 15 and an average crystal length less than 0.5 micron and which comprise alkali metal ions that impart a basicity of at least 0.04 meq. per gram to said oxide.
Claim 3
Dependent Claim
21 words
Gamma ferric oxide according to claim 1 having a basicity in the range of 0.04 to about 0.2 meq. per gram.
Claim 4
Dependent Claim
19 words
Gamma ferric oxide according to claim 2 also containing doping ions of cobalt, nickel, chromium, zinc, manganese or calcium.
Claim 5
Dependent Claim
32 words
Gamma ferric oxide according to claim 3 in which the acicularity ratio is in the range of about 15 to about 40 and the alkali metal ions are sodium or potassium ions.
Claim 6
Dependent Claim
27 words
A product for magnetic recording comprising a support and a layer of non-magnetic binder in which there is dispersed gamma ferric oxide as defined in claim 3.
Claim 7
Dependent Claim
16 words
A product for magnetic recording according to claim 5 where the doping ions are cobalt ions.
Claim 8
Dependent Claim
28 words
Gamma ferric oxide according to claim 1 also comprising alkaline earth metal ions in a concentration of about 0.25 to about 2 percent, by weight, based on oxide.
Claim 9
Dependent Claim
17 words
Gamma ferric oxide according to claim 7 in which said alkaline earth metal ions are calcium ions.
Claim 10
Dependent Claim
18 words
Gamma ferric oxide according to claim 8 in which the alkali metal ions are sodium or potassium ions.
Claim 11
Dependent Claim
18 words
Gamma ferric oxide according to claim 9 also containing doping ions of cobalt, nickel, chromium, zinc or manganese.
Claim 12
Dependent Claim
14 words
Gamma ferric oxide according to claim 10 where said doping ions are cobalt ions.
Claim 13
Dependent Claim
22 words
Gamma ferric oxide according to claim 1 having a narrow particle size distribution such that its coefficient of polydispersion is above 2.
Claim 14
Dependent Claim
17 words
A product for magnetic recording comprising a support and gamma ferric oxide as defined in claim 1.
Claim 15
Dependent Claim
27 words
A product for magnetic recording comprising a support and a layer of non-magnetic binder in which there is dispersed gamma ferric oxide as defined in claim 1.
Claim 16
Dependent Claim
173 words
A process for preparing acicular gamma ferric oxide crystals for magnetic recording which comprises adding under non-oxidizing conditions, at a temperature below about 60° C., an aqueous solution of ferrous salt to an aqueous solution of a stoichiometric excess of an alkaline hydroxide while substantially avoiding local excesses of said ferrous salt, to form an aqueous dispersion of ferrous hydroxide particles, said alkaline hydroxide being present in said aqueous dispersion in a concentration of at least about a 500% stoichiometric excess; introducing oxygen into said dispersion at a temperature of about 20° C. to about 60° C. for a period of time sufficient to convert said ferrous hydroxide particles to crystals of alpha ferric oxide hydrate, the concentrations of ferric oxide hydrate formed in the oxidized dispersion being no more than about 15 grams per liter; discontinuing introduction of said oxygen into said dispersion; boiling said dispersion to obtain further crystallization of said alpha ferric oxide hydrate crystals; and subjecting said crystals to dehydration, reduction and oxidation to form gamma ferric oxide crystals.
Claim 17
Dependent Claim
173 words
A process for preparing acicular gamma ferric oxide crystals for magnetic recording which comprises adding under non-oxidizing conditions, at a temperature below about 60° C., an aqueous solution of ferrous salt to an aqueous solution of a stoichiometric excess of an alkaline hydroxide while substantially avoiding local excesses of said ferrous salt, to form an aqueous dispersion of ferrous hydroxide particles, said alkaline hydroxide being present in said aqueous dispersion in a concentration of at least about a 500% stoichiometric excess; introducing oxygen into said dispersion at a temperature of about 20° C. to about 60° C. for a period of time sufficient to convert said ferrous hydroxide particles to crystals of alpha ferric oxide hydrate, the concentrations of ferric oxide hydrate formed in the oxidized dispersion being no more than about 15 grams per liter; discontinuing introduction of said oxygen into said dispersion; boiling said dispersion to obtain further crystallization of said alpha ferric oxide hydrate crystals; and subjecting said crystals to dehydration, reduction and oxidation to form gamma ferric oxide crystals.
Claim 18
Dependent Claim
55 words
A process according to claim 15 which comprises directing said solution of ferrous salt to a suction zone created in the midst of said alkaline hydroxide solution where said ferrous salt solution undergoes a lamellar stretching such that it penetrates into said alkaline hydroxide solution in the form of a sheet of large surface area.
Claim 19
Dependent Claim
37 words
A process according to claim 16 in which the aqueous dispersion of ferrous hydroxide particles is formed in less than about 10 minutes and the duration of said introduction of oxygen is less than about 3 hours.
Claim 20
Dependent Claim
16 words
A process according to claim 15 in which said alkaline hydroxide is an alkali metal hydroxide.
Claim 21
Dependent Claim
29 words
A process according to claim 18 in which the oxygen is introduced into the dispersion by directing it to a suction zone created in the midst of the dispersion.
Claim 22
Dependent Claim
22 words
A process according to claim 15 in which said ferrous salt solution contains ions of cobalt, nickel, chromium, zinc, manganese or calcium.
Claim 23
Dependent Claim
35 words
A process according to claim 15 which comprises the additional steps of recovering said alpha ferric oxide hydrate crystals from said dispersion and washing said crystals with an aqueous solution containing alkaline earth metal ions.
Claim 24
Dependent Claim
22 words
A process according to claim 21 in which the ferrous salt solution contains ions of cobalt, nickel chromium, zinc, manganese or calcium.
Claim 25
Dependent Claim
16 words
A process according to claim 21 in which said alkaline earth metal ions are calcium ions.
Claim 26
Dependent Claim
52 words
A process according to claim 15 in which the duration of said introduction of oxygen is less than about 3 hours and said process comprises the additional steps of recovering said alpha ferric oxide hydrate crystals from said dispersion and washing said crystals with an aqueous solution containing alkaline earth metal ions.
Claim 27
Dependent Claim
16 words
A process according to claim 24 in which said alkaline earth metal ions are calcium ions.
References Cited (Backward Citations)
US2558302A
Cited
US3075919A
Cited
US3288563A
Cited
US3399142A
Cited
BE756608A
Cited
US3720618A
Cited
US3843773A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-03-09 | 1984-09-08 | 1985-03-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-03-09 | 1988-09-08 | 1989-03-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-03-09 | 1992-09-08 | 1993-03-10 | $7700.00 | Window Closed / Lapsed |