Abstract A process for the production of polyolefin foam materials from crosslinked polyolefin foam scraps includes the steps of comminuting scraps of crosslinked polyolefin-containing foam; admixing the comminuted scraps with a synthetic resin on a polyolefin basis; compressing the resulting admixture at a temperature lying below the decomposition temperature of the crosslinking agent to form an aggregate product; comminuting this product to form a particulate material; plasticizing the particulate material at a temperature lying below the decomposition temperature of the crosslinking agent to form a shaped article; and crosslinking and expanding, i.e. foaming, the shaped article by heating the article to above the decomposition temperatures of the crosslinking agent and of the blowing agent. The foam scraps are obtained from a foam article produced by mixing a polyolefin or a blend of a polyolefin with an elastomer and/or synthetic resins with an organic peroxide crosslinking agent and a particulate blowing agent, the decomposition temperature of the crosslinking agent being below the decomposition temperature of the blowing agent, and optionally with customary additives; by forming the mixture, at a temperature lying below the decomposition temperatures of the crosslinking agent and the blowing agent, into a shaped article; and by subsequently crosslinking and expanding, i.e. foaming, this shaped article with the application of heat to above the decomposition temperatures of the crosslinking agent and the blowing agent.
A process for the production of polyolefin foam materials from crosslinked polyolefin foam scraps which comprises mixing a polyolefin or a blend of a polyolefin with an elastomer and/or synthetic resins with an organic peroxide as the crosslinking agent and a blowing agent, the decomposition temperature of the crosslinking agent being below the decomposition temperature of the blowing agent, and optionally with customary additives; forming the mixture, at a temperature lying below the decomposition temperatures of the crosslinking agent and the blowing agent, into a first shaped article; subsequently crosslinking and expanding the first shaped article by heating to above the decomposition temperatures of the crosslinking agent and the blowing agent; obtaining scraps of said crosslinked polyolefin-containing foam material comminuting the crosslinked polyolefin-containing foam scraps; thereafter admixing the comminuted scraps with a synthetic resin on a polyolefin basis, and then compressing the admixture at a temperature lying below the decomposition temperature of the crosslinking agent to form an aggregate product; comminuting this product to form a particulate material; plasticizing this material at a temperature lying below the decomposition temperature of the crosslinking agent to form a second shaped article; and crosslinking and expanding the second shaped article by heating to above the decomposition temperatures of the crosslinking agent and of the blowing agent.
Claim 2
Dependent Claim
213 words
A process for the production of polyolefin foam materials from crosslinked polyolefin foam scraps which comprises mixing a polyolefin or a blend of a polyolefin with an elastomer and/or synthetic resins with an organic peroxide as the crosslinking agent and a blowing agent, the decomposition temperature of the crosslinking agent being below the decomposition temperature of the blowing agent, and optionally with customary additives; forming the mixture, at a temperature lying below the decomposition temperatures of the crosslinking agent and the blowing agent, into a first shaped article; subsequently crosslinking and expanding the first shaped article by heating to above the decomposition temperatures of the crosslinking agent and the blowing agent; obtaining scraps of said crosslinked polyolefin-containing foam material comminuting the crosslinked polyolefin-containing foam scraps; thereafter admixing the comminuted scraps with a synthetic resin on a polyolefin basis, and then compressing the admixture at a temperature lying below the decomposition temperature of the crosslinking agent to form an aggregate product; comminuting this product to form a particulate material; plasticizing this material at a temperature lying below the decomposition temperature of the crosslinking agent to form a second shaped article; and crosslinking and expanding the second shaped article by heating to above the decomposition temperatures of the crosslinking agent and of the blowing agent.
Claim 3
Dependent Claim
34 words
A process according to claim 1, characterized in that up to about 100 parts by weight of the synthetic resin on a polyolefin basis is added per 100 parts by weight of foam scraps.
Claim 4
Dependent Claim
85 words
A process according to claim 1 or 2, characterized in that the comminuted and compressed foam scraps are formed into a shaped article under plasticization at a temperature lying below the decomposition temperature of the crosslinking agent, together with an optionally compounded raw material mixture for the production of a crosslinked polyolefin foam material, this mixture having a weight proportion of synthetic resin reduced by the weight proportion of the compressed foam scraps; and that this shaped article is then crosslinked and expanded by heating.
Claim 5
Dependent Claim
32 words
A process according to claim 3, characterized in that, of 100 parts by weight of total mixture, 10-70 parts by weight is constituted by foam scraps compressed together with the synthetic resin.