US4255195A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Compositions containing silicon dioxide
Assignee: Individual
•
Filing: 1979-03-26
•
Granted: 1981-03-10
•
Expires: 1999-03-26
Abstract
Abstract The present invention relates to the use of amorphous, dust-like silicon dioxide emission products from electro-thermic manufacture of ferrosilicon and/or silicon as fillers in refractory compositions. The advantages obtained from the use of the products include improvement in mechanical abrasion resistance, heat stability, and electrical, thermal and sound insulation.
Inventors
- 👤 Heinz Holter
- 👤 Heinz Gresch
- 👤 Heinrich Igelbuscher
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 03:00
CPC Classifications
C; C04; C04B; C04B18/00; C04B18/04; C04B18/14; C04B18/146; C04B28/00; C04B28/02; C04B2111/00; C04B2111/00034; C04B2111/00146; C04B2111/00155; C04B2111/00474; C04B2111/00482; C04B2111/00525; C04B2111/20; C04B2111/28; C04B2111/52; Y; Y02; Y02W; Y02W30/00; Y02W30/50; Y02W30/91
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
131 words
In a heat- or fire-resistant refractory composition compatible with silicon dioxide and containing binder in admixture with at least one other ingredient, the improvement wherein the composition is sprayable or tampable and is suitable for coating steel girders or for lining an industrial furnace or metallurgical vessel, the binder is other than sodium silicate and the composition further comprises a heat-, flame- or fire-resistance increasing amount of dust-like silicon dioxide having a bulk weight within the approximate range of from 0.25 to 0.5 gram per milliliter, 95 percent of which has a grain size below 50 microns, approximately 82 to 95 percent of which is amorphous silicon dioxide and approximately 5 to 18 percent of which is crystalline quartz, the dust-like silicon dioxide comprising up to 50 percent of the composition.
Claim 2
Dependent Claim
131 words
In a heat- or fire-resistant refractory composition compatible with silicon dioxide and containing binder in admixture with at least one other ingredient, the improvement wherein the composition is sprayable or tampable and is suitable for coating steel girders or for lining an industrial furnace or metallurgical vessel, the binder is other than sodium silicate and the composition further comprises a heat-, flame- or fire-resistance increasing amount of dust-like silicon dioxide having a bulk weight within the approximate range of from 0.25 to 0.5 gram per milliliter, 95 percent of which has a grain size below 50 microns, approximately 82 to 95 percent of which is amorphous silicon dioxide and approximately 5 to 18 percent of which is crystalline quartz, the dust-like silicon dioxide comprising up to 50 percent of the composition.
Claim 3
Dependent Claim
22 words
A refractory composition according to claim 1 wherein the dust-like silicon dioxide is predominantly-amorphous silicon-dioxide-dust-emission product of electro-thermic ferro-silicon or silicon manufacture.
Claim 4
Dependent Claim
27 words
A refractory composition according to claim 2 for use in industrial furnaces and metallurgical vessels and comprising sand and cement in addition to the dust-like silicon dioxide.
Claim 5
Dependent Claim
28 words
A sprayable composition according to claim 3 which comprises 30 percent chamotte, 30 percent sand, 10 percent alumina cement and 30 percent of the predominantly-amorphous, dust-like silicon dioxide.
Claim 6
Dependent Claim
28 words
A tampable composition according to claim 3 comprising 15 percent sand, 50 percent chamotte B, 15 percent alumina cement and 20 percent of the predominantly-amorphous, dust-like silicon dioxide.
Claim 7
Dependent Claim
29 words
A tampable composition according to claim 3 comprising 66 percent sand, 5 percent chamotte A, 7 percent Portland cement 450 and 22 percent of the predominantly-amorphous, dust-like silicon dioxide.
Claim 8
Dependent Claim
20 words
A refractory composition according to claim 2 comprising from 5 to 50 percent by weight of the dust-like silicon dioxide.
Claim 9
Dependent Claim
18 words
A refractory composition according to claim 7 having about 20 percent by weight of the dust-like silicon dioxide.
Claim 10
Dependent Claim
18 words
A refractory composition according to claim 7 having about 30 percent by weight of the dust-like silicon dioxide.
References Cited (Backward Citations)
US1861317A
Cited
US2410954A
Cited
US2511724A
Cited
US3131075A
Cited
US3075848A
Cited
US3467535A
Cited
US3681113A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-03-09 | 1984-09-08 | 1985-03-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-03-09 | 1988-09-08 | 1989-03-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-03-09 | 1992-09-08 | 1993-03-10 | $7700.00 | Window Closed / Lapsed |