Aluminum dross processing
Assignee: Imperial West Chemical Co
•
Filing: 1979-03-29
•
Granted: 1981-02-24
•
Expires: 1999-03-29
Abstract
Abstract There is disclosed a method for the elimination of the chief impurities in aluminum dross tailings. The dross tailings, which are chiefly particles of aluminum oxide, are suspended in an aqueous slurry and the slurry is heated to a temperature from 185 DEG -225 DEG F. and maintained under liquification pressures and sufficient agitation to insure particle-to-particle attrition that removes an aluminum hydroxide coating which would otherwise inhibit the reaction. The reaction rate is accelerated by chemical and physical additives that can be optionally added to the slurry such as trace quantities of caustic, which serves as a source of hydroxyl ligands to increase the solubility of aluminum hydroxide and/or refractory particles such as ceramic spheres which increase the attrition. Other contaminants present in the dross tailings include aluminum nitride, which is decomposed to aluminum oxide and ammonia, and aluminum carbide which is decomposed to aluminum oxide and methane.
Inventors
- 👤 Durward A. Huckabay
- 👤 Arthur D. Skiathas
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 10:20
CPC Classifications
C; C01; C01F; C01F7/00; C01F7/02; C22; C22B; C22B21/00; C22B21/0007; C01P; C01P2004/00; C01P2004/60; C01P2004/61
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
150 words
A method for the treatment of aluminum dross tailings comprising a mixture of water soluble salts, aluminum oxides, and from 0.1 to about 5 weight percent aluminum metal contaminate which comprises: (a) washing said oxides to remove said water soluble salts and form an aqueous slurry of aluminum oxides containing no more than about 1 weight percent soluble salts; (b) heating said slurry to a temperature from 185° to about 225° F. and maintaining sufficient pressure to maintain said aqueous slurry; (c) agitating said slurry in the presence of inert refractory particles having dimensions from 1/8 to about 2 inches to cause sufficient particle-to-particle attrition to remove the aluminum hydroxide protective film on the aluminum metal contaminants; and (d) maintaining said agitation, pressure and temperature for a period of time sufficient to effect substantially complete oxidation of said aluminum metal contaminates in said slurry with the evolution of hydrogen therefrom.
Claim 2
Independent Claim
150 words
A method for the treatment of aluminum dross tailings comprising a mixture of water soluble salts, aluminum oxides, and from 0.1 to about 5 weight percent aluminum metal contaminate which comprises: (a) washing said oxides to remove said water soluble salts and form an aqueous slurry of aluminum oxides containing no more than about 1 weight percent soluble salts; (b) heating said slurry to a temperature from 185° to about 225° F. and maintaining sufficient pressure to maintain said aqueous slurry; (c) agitating said slurry in the presence of inert refractory particles having dimensions from 1/8 to about 2 inches to cause sufficient particle-to-particle attrition to remove the aluminum hydroxide protective film on the aluminum metal contaminants; and (d) maintaining said agitation, pressure and temperature for a period of time sufficient to effect substantially complete oxidation of said aluminum metal contaminates in said slurry with the evolution of hydrogen therefrom.
Claim 3
Dependent Claim
39 words
The treatment of claim 1 wherein said aluminum dross tailings also include aluminum carbide as a contaminant and said heating and agitation is maintained to effect substantially complete decomposition of said aluminum carbide contaminants to aluminum oxide and methane.
Claim 4
Dependent Claim
39 words
The treatment of claim 1 wherein said aluminum dross tailings also contain aluminum nitride contaminants and wherein said temperature and agitation are maintained sufficiently to effect substantially complete decomposition of said aluminum nitride contaminants to aluminum oxide and ammonia.
Claim 5
Dependent Claim
21 words
The treatment of claim 1 wherein said refractory particles are ceramic spheres having a diameter from 1/8 to about 2 inches.
Claim 6
Dependent Claim
13 words
The treatment of claim 4 wherein said ceramic spheres are formed of alumina.
Claim 7
Dependent Claim
29 words
The treatment of claim 1 wherein an alkali metal hydroxide is maintained in said slurry during said agitation at a concentration from about 0.01 to about 1 weight percent.
Claim 8
Dependent Claim
27 words
The treatment of claim 6 wherein said alkali metal hydroxide is sodium hydroxide which is maintained at a concentration from about 0.1 to about 0.5 weight percent.
Claim 9
Dependent Claim
47 words
The treatment of claim 1 wherein said agitation is continuously performed in an upflowing clarification vessel by introducing said slurry into the bottom of said vessel and withdrawing from the top of said vessel a treated slurry of finely subdivided alumina substantially free of aluminum metal contaminants.
Claim 10
Dependent Claim
27 words
The treatment of claim 8 wherein said slurry is agitated in said clarification vessel by a mechanically driven mixer positioned in the lower portion of said vessel.
Claim 11
Dependent Claim
28 words
The treatment of claim 8 wherein said agitation is performed by circulating a stream of said slurry through a pump and returning said stream to the agitation vessel.
Claim 12
Dependent Claim
36 words
The treatment of claim 1 wherein a waste brine solution is separated from said slurry in said washing step and is concentrated and evaporated to dryness to recover a mixture of sodium and potassium chlorides therefrom.
Claim 13
Dependent Claim
30 words
The treatment of claim 1 wherein the hydrogen gas evolved during said agitation is collected, water vapor is condensed therefrom and is used as a fuel source in said treatment.
Claim 14
Dependent Claim
24 words
The treatment of claim 12 wherein said collected hydrogen is used as a fuel supply to the evaporator used to concentrate said waste brine.
Claim 15
Dependent Claim
30 words
The treatment of claim 13 wherein the gases evolved from said agitation step are collected and are contacted with an aqueous spray to cool said gases and separate ammonia therefrom.
Claim 16
Dependent Claim
38 words
The treatment of claim 14 wherein said aqueous spray is a spray of an aqueous solution of sulfuric acid and a dilute solution of ammonium sulfate is recovered from contacting of the collected gases with said aqueous spray.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-02-24 | 1984-08-25 | 1985-02-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-02-24 | 1988-08-25 | 1989-02-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-02-24 | 1992-08-25 | 1993-02-24 | $7700.00 | Window Closed / Lapsed |