Process for preparing calcined gypsum and gypsum board using ligno sulfonates

Claim 2

In a process for manufacturing beta calcium sulfate hemihydrate stucco of the type wherein stucco is fed to a blender, about 1 to about 10% by weight of water is blended with the stucco in the blender, and the water treated stucco is allowed to heal whereby the healed stucco has a reduced water demand; the improvement which comprises: in the step of blending the stucco with a small amount of water, adding on a dry solids weight basis about 1/2 lb. to about 5 lbs. per 2,000 lbs. ton of dry stucco of a sulfonate selected from the group consisting of (1) alkali metal, alkaline earth metal and ammonium ligno sulfonates, (2) alkali metal, alkaline earth metal, and ammonium polymerized salts of sulfonic acid and (3) mixtures of such sulfonates whereby the surface area of the healed stucco is reduced.

Claim 3

The process of claim 1 in which the sulfonate is present in an amount of about 1-3 lbs. per ton of the dry stucco to be treated and water is present in an amount of about 40-60 lbs. per ton of the dry stucco to be treated.

Claim 4

The process of claim 1 in which a solid form sulfonate is dissolved in the water or a liquid sulfonate is diluted in the treatment water.

Claim 5

The process of claim 1 in which the solution treated stucco is allowed to heal for about 1-30 minutes.

Claim 6

An improved process for preparing beta calcium sufate hemihydrate stucco characterized by providing the stucco with a reduced water demand obtaining greater rheological and powder flow behavior of the treated stucco particles, which comprises: (1) supplying beta calcium sulfate hemihydrate stucco feed to be conveyed to a blender; (2) conveying the stucco feed to the blender; (3) Blending with the stucco feed a water solution of sulfonate, the amount of water ranging from about 1% to about 10% by weight of the stucco feed and the sulfonate ranging from about 1/2 lb. to about 5 lbs. per 2,000 lb. ton on a dry solids weight basis to the stucco feed, said sulfonate being selected from the group consisting of (a) alkali metal, alkaline earth metal and ammonium ligno sulfonates, (b) alkali metal, alkaline earth metal and ammonium high molecular weight polymerized sulfonic acid salts and (c) mixtures of such sulfonates; (4) Allowing the solution treated stucco to heal; (5) Drying the healed stucco by subjecting it to elevated temperatures; (6) Grinding the dried, healed stucco to reactivate the surface so as to improve the rate of strength development and ultimate strength in a gypsum product and; (7) Recovering a dried, healed calcined stucco which is storage stable, has reduced water demand, is capable of developing substantially full compressive strength in a gypsum product and has improved hydrophilic characteristics.

Claim 7

An improved process for preparing beta calcium sufate hemihydrate stucco characterized by providing the stucco with a reduced water demand obtaining greater rheological and powder flow behavior of the treated stucco particles, which comprises: (1) supplying beta calcium sulfate hemihydrate stucco feed to be conveyed to a blender; (2) conveying the stucco feed to the blender; (3) Blending with the stucco feed a water solution of sulfonate, the amount of water ranging from about 1% to about 10% by weight of the stucco feed and the sulfonate ranging from about 1/2 lb. to about 5 lbs. per 2,000 lb. ton on a dry solids weight basis to the stucco feed, said sulfonate being selected from the group consisting of (a) alkali metal, alkaline earth metal and ammonium ligno sulfonates, (b) alkali metal, alkaline earth metal and ammonium high molecular weight polymerized sulfonic acid salts and (c) mixtures of such sulfonates; (4) Allowing the solution treated stucco to heal; (5) Drying the healed stucco by subjecting it to elevated temperatures; (6) Grinding the dried, healed stucco to reactivate the surface so as to improve the rate of strength development and ultimate strength in a gypsum product and; (7) Recovering a dried, healed calcined stucco which is storage stable, has reduced water demand, is capable of developing substantially full compressive strength in a gypsum product and has improved hydrophilic characteristics.

Claim 8

An improved process for manufacturing gypsum board characterized by improved handling properties and decreased surface area of the treated calcium sulfate hemihydrate stucco and by using a reduced amount of water to fluidize the treated stucco in forming a slurry which is fed to a board making machine which comprises: (1) Supplying stucco feed to be conveyed to a gypsum slurry mixer; (2) Conveying the stucco feed to a blender; (3) Blending with the stucco about from 20 to 200 lbs. per ton of water and about from 1/2 to 5 lbs. per ton of a sulfonate selected from the group consisting of (a) alkali metal, alkaline earth metal and ammonium ligno sulfonates, (b) alkali metal, alkaline earth metal and ammonium high molecular weight polymerized sulfonic acid salts and (c) mixtures of such sulfonates; (4) Allowing the sulfonate-water treated stucco to heal; (5) Feeding the healed stucco to a gypsum slurry mixer; (6) Adding additional water to the healed stucco in the slurry mixer, said additional water being added in an amount sufficient to provide about from 50 to 85 parts of water, including water added in the blender, per 100 parts of stucco which results in a substantially reduced amount of water to be evaporated from the wet board; (7) Mixing the healed stucco and water in the slurry mixer to form a homogeneous slurry; (8) Feeding the slurry to a gypsum board making machine to form wet gypsum board; (9) Drying the wet gypsum board; and (10) Recovering dry gypsum board consisting essentially of calcium sulfate dihydrate.

Claim 9

An improved process for manufacturing gypsum board characterized by improved handling properties and decreased surface area of the treated calcium sulfate hemihydrate stucco and by using a reduced amount of water to fluidize the treated stucco in forming a slurry which is fed to a board making machine which comprises: (1) Supplying stucco feed to be conveyed to a gypsum slurry mixer; (2) Conveying the stucco feed to a blender; (3) Blending with the stucco about from 20 to 200 lbs. per ton of water and about from 1/2 to 5 lbs. per ton of a sulfonate selected from the group consisting of (a) alkali metal, alkaline earth metal and ammonium ligno sulfonates, (b) alkali metal, alkaline earth metal and ammonium high molecular weight polymerized sulfonic acid salts and (c) mixtures of such sulfonates; (4) Allowing the sulfonate-water treated stucco to heal; (5) Feeding the healed stucco to a gypsum slurry mixer; (6) Adding additional water to the healed stucco in the slurry mixer, said additional water being added in an amount sufficient to provide about from 50 to 85 parts of water, including water added in the blender, per 100 parts of stucco which results in a substantially reduced amount of water to be evaporated from the wet board; (7) Mixing the healed stucco and water in the slurry mixer to form a homogeneous slurry; (8) Feeding the slurry to a gypsum board making machine to form wet gypsum board; (9) Drying the wet gypsum board; and (10) Recovering dry gypsum board consisting essentially of calcium sulfate dihydrate.

Claim 10

The process of claim 6 in which the sulfonate is present in an amount of about 1-3 lbs. per ton of stucco and the sulfonate is sodium ligno sulfonate.

Claim 11

The process of claim 6 in which the sulfonate is present in an amount of about 1--3 lbs. per ton of stucco and the sulfonate is calcium ligno sulfonate.

Claim 12

The process of claim 6 in which the sulfonate is present in an amount of about 1-3 lbs. per ton of stucco and the sulfonate is ammonium ligno sulfonate.

Claim 13

The process of claim 6 in which the sulfonate is present in an amount of about 1-3 lbs. per ton of stucco and the sulfonate is a polymerized alkyl naphthalene sulfonic acid potassium acid.