Method of preparing a sintered lithium aluminate structure for containing electrolyte
Assignee: United States Department of Energy
•
Filing: 1979-12-27
•
Granted: 1981-02-17
•
Expires: 1999-12-27
Abstract
Abstract A porous sintered tile is formed of lithium aluminate for retaining moltenlectrolyte within a fuel cell. The tile is prepared by reacting lithium hydroxide in aqueous solution with alumina particles to form beta lithium aluminate particles. The slurry is evaporated to dryness and the solids dehydrated to form a beta lithium aluminate powder. The powder is compacted into the desired shape and sintered at a temperature in excess of 1200 K. but less than 1900 K. to form a porous integral structure that is subsequently filled with molten electrolyte. A tile of this type is intended for use in containing molten alkali metal carbonates as electolyte for use in a fuel cell having porous metal or metal oxide electrodes for burning a fuel gas such as hydrogen and/or carbon monoxide with an oxidant gas containing oxygen.
Inventors
- 👤 James W. Sim
- 👤 Kimio Kinoshita
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 05:24
CPC Classifications
C; C01; C01F; C01F7/00; C01F7/02; C01F7/04; C01F7/043; C04; C04B; C04B35/00; C04B35/01; C04B35/10; C04B35/111; C04B35/113; H; H01; H01M; H01M8/00; H01M8/02; H01M8/0289; H01M8/0295; H01M2300/00; H01M2300/0017; H01M2300/0048; Y; Y02; Y02E; Y02E60/00; Y02E60/10; Y02E60/30; Y02E60/50
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
115 words
A method of preparing a porous structure for retaining molten electrolyte within an electrochemical cell comprising: preparing a reaction mixture containing oxidized aluminum as alumina or aluminum hydroxide slurry with a solution of lithium hydroxide to react with said oxidized aluminum and form lithium aluminate; reducing said mixture to dryness; calcining said dried mixture to form a dehydrated powder containing beta lithium aluminate; compacting said powder containing beta lithium aluminate to form a porous green compact; and sintering said compact at a temperature in excess of 1200 K but less than the melting point of lithium aluminate simultaneously to form a porous integral structure and to convert said beta lithium aluminate to gamma lithium aluminate.
Claim 2
Independent Claim
115 words
A method of preparing a porous structure for retaining molten electrolyte within an electrochemical cell comprising: preparing a reaction mixture containing oxidized aluminum as alumina or aluminum hydroxide slurry with a solution of lithium hydroxide to react with said oxidized aluminum and form lithium aluminate; reducing said mixture to dryness; calcining said dried mixture to form a dehydrated powder containing beta lithium aluminate; compacting said powder containing beta lithium aluminate to form a porous green compact; and sintering said compact at a temperature in excess of 1200 K but less than the melting point of lithium aluminate simultaneously to form a porous integral structure and to convert said beta lithium aluminate to gamma lithium aluminate.
Claim 3
Dependent Claim
23 words
The method of claim 1 wherein said mixture is prepared by adding a solution of lithium hydroxide to a slurry of oxidized aluminum.
Claim 4
Dependent Claim
25 words
The method of claim 1 wherein said reaction mixture is reduced to dryness at a temperature of 400-500 K and then calcined at 700-800 K.
Claim 5
Dependent Claim
15 words
The method of claim 1 wherein said dehydrated powder consists essentially of beta lithium aluminate.
Claim 6
Dependent Claim
52 words
The method of claim 1 wherein said green compact is sintered at a temperature of 1200-1400 K to form a porous structure with particles of gamma lithium aluminate mutually diffused into adjacent particles to form an integral structure for containing molten alkali metal carbonates for use as electrolyte within a fuel cell.
Claim 7
Dependent Claim
41 words
The method of claim 1 wherein said dehydrated powder containing beta lithium aluminate has a surface area of about 10 to 40 m 2 /g and said porous integral structure for containing molten electrolyte has a porosity in excess of 60%.
Claim 8
Dependent Claim
25 words
The method of claim 1 wherein said dehydrated powder is compacted at a pressure of 5 to 30 MPa to form a porous green compact.
Claim 9
Dependent Claim
21 words
The method of claim 1 wherein said solution of lithium hydroxide and slurry are substantially free of other alkali metal hydroxides.
Claim 10
Dependent Claim
18 words
A porous structure for retaining molten electrolyte within a fuel cell prepared by the method of claim 1.
References Cited (Backward Citations)
US3845185A
Cited
US4115632A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-02-17 | 1984-08-18 | 1985-02-17 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-02-17 | 1988-08-18 | 1989-02-17 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-02-17 | 1992-08-18 | 1993-02-17 | $7700.00 | Window Closed / Lapsed |