Method of forming valve lifters
Assignee: Individual
•
Filing: 1979-03-02
•
Granted: 1981-02-17
•
Expires: 1999-03-02
Abstract
Abstract This invention relates to a method of making a valve lifter or the like wherein elemental iron powder is blended with smaller sized powders of manganese, molybdenum, and nickel, or sources of these metals, the resulting mixture is pressed into a coherent preform which is then sintered to cause solid state diffusion and alloying to occur within the preform. The sintered preform is then pressed into a shape which approaches the theoretical density of the metal and has a nearly uniform density carburized and heat treated, the pressing being carried out at ambient temperatures to produce a valve lifter or similar article having superior wearing properties at a lower cost, when compared with present materials and methods of manufacture.
Inventors
- 👤 David T. Smith
- 👤 Harold R. Biehl
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 00:05
CPC Classifications
C; C22; C22C; C22C33/00; C22C33/02; C22C33/0257; C22C33/0264; B; B22; B22F; B22F3/00; B22F3/20; F; F01; F01L; F01L1/00; F01L1/12; F01L1/14
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
80 words
The method of making a valve lifter or the like which comprises: blending elemental iron powder of -100 mesh size with smaller size powder particles of sources of manganese, molybdenum and nickel, pressing the resulting mixture into a coherent preform, sintering said preform to cause solid state diffusion and alloying within said preform, and pressing the sintered preform to an elongated shape having a large length to wall thickness ratio, said shape having substantially theoretical, uniform density at ambient temperatures.
Claim 2
Independent Claim
80 words
The method of making a valve lifter or the like which comprises: blending elemental iron powder of -100 mesh size with smaller size powder particles of sources of manganese, molybdenum and nickel, pressing the resulting mixture into a coherent preform, sintering said preform to cause solid state diffusion and alloying within said preform, and pressing the sintered preform to an elongated shape having a large length to wall thickness ratio, said shape having substantially theoretical, uniform density at ambient temperatures.
Claim 3
Dependent Claim
16 words
The method of claim 1 in which said last-named pressing is carried out by backward extrusion.
Claim 4
Dependent Claim
16 words
The method of claim 1 in which the last-named pressing is followed by a carburizing treatment.
Claim 5
Dependent Claim
22 words
The method of claim 3 in which said carburizing treatment is followed by a heat treatment to achieve a predetermined hardness value.
Claim 6
Dependent Claim
31 words
The method of claim 1 in which said resulting mixture contains: from 0.75 to 1.50% manganese; from 0.65 to 1.25% molybdenum; from 0.50 to 1.0% nickel; and the balance essentially iron.
Claim 7
Dependent Claim
31 words
The method of claim 1 in which said resulting mixture contains: from 0.80 to 1.25% manganese; from 0.80 to 1.0% molybdenum; from 0.55 to 0.75% nickel; and the balance essentially iron.
Claim 8
Dependent Claim
21 words
The method of claim 1 in which said shape has a length to diameter ratio of at least 2.5 to 1.
Claim 9
Dependent Claim
22 words
The method of claim 1 in which said shape has a length to wall thickness ratio of at least 25 to 1.
Claim 10
Dependent Claim
23 words
The method of claim 1 in which said shape has a length to wall thickness ratio of from 26 to 30 to 1.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-02-17 | 1984-08-18 | 1985-02-17 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-02-17 | 1988-08-18 | 1989-02-17 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-02-17 | 1992-08-18 | 1993-02-17 | $7700.00 | Window Closed / Lapsed |