Interpenetrating polymer network comprising epoxy polymer and polysiloxane
Assignee: Ameron Inc
•
Filing: 1979-09-06
•
Granted: 1981-02-10
•
Expires: 1999-09-06
Abstract
Abstract Polymeric structures having interpenetrating matrices in cured form comprising an epoxy-polyamine network and a polysiloxane network. The interpenetrating network physical and chemical properties are improved over those of either polymeric component alone. The network can be prepared by simultaneously reacting epoxy resin having at least two oxirane groups with amine curing agent, and having present at least 0.1 equivalent of silane, water being substantially uniformly distributed throughout the mixture in an amount sufficient to bring about substantial hydrolytic polycondensation of the silane to form a cross-linked interpenetrating polymer network. The amine curing agent may be substituted wholly or in part by aminosilane. Sources of silane may include aminosilane and epoxysilane. Relative reaction rates of formation of the polymeric networks are controlled, to get good intertwining of the two polymers.
Inventors
- 👤 Raymond E. Foscante
- 👤 Albert P. Gysegem
- 👤 Pamela J. Martinich
- 👤 Gabriel H. Law
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 14:53
CPC Classifications
C; C08; C08G; C08G77/00; C08G77/42; C08L; C08L63/00; C08G59/00; C08G59/18; C08G59/40; C08G59/4007; C08G59/4085; C08G59/50; C08G59/56; Y; Y10; Y10S; Y10S525/00; Y10S525/903
Claims Analysis
Total Claims: 64
Claim 1
Independent Claim
107 words
A method for preparing an interpenetrating polymer network having an epoxy network intertwined with a polysiloxane network comprising the steps of: (a) mixing a silane with an epoxy resin having at least two oxirane groups per molecular, the silane being selected from the group consisting of aminosilane, epoxysilane, alkoxysilane, alkyltrialkoxysilane, aryltrialkoxysilane, and hydrolytic polycondensation products thereof; (b) distributing water substantially uniformly throughout the mixture in an amount sufficient to bring about substantial hydrolytic polycondensation of the silane to form a polysiloxane network; and (c) substantially simultaneously reacting the epoxy resin with an amine curing agent to form a polymerized epoxy resin network intertwined with the polysiloxane network.
Claim 2
Independent Claim
107 words
A method for preparing an interpenetrating polymer network having an epoxy network intertwined with a polysiloxane network comprising the steps of: (a) mixing a silane with an epoxy resin having at least two oxirane groups per molecular, the silane being selected from the group consisting of aminosilane, epoxysilane, alkoxysilane, alkyltrialkoxysilane, aryltrialkoxysilane, and hydrolytic polycondensation products thereof; (b) distributing water substantially uniformly throughout the mixture in an amount sufficient to bring about substantial hydrolytic polycondensation of the silane to form a polysiloxane network; and (c) substantially simultaneously reacting the epoxy resin with an amine curing agent to form a polymerized epoxy resin network intertwined with the polysiloxane network.
Claim 3
Dependent Claim
56 words
The method of claim 1 in which the amine curing agent has the general formula: H[HNR--.sub.a NH.sub.2 where a is an integer from 1 to about 6, each R is a difunctional radical independently selected from the group consisting of alkyl, aryl, dialkylaryl, alkoxyalkyl, and cycloalkyl radicals, and R may vary within the amine curing agent.
Claim 4
Dependent Claim
36 words
The method of claim 1 in which the mixture includes a carbon-containing compound with less than about nine carbon atoms and which contains a linkage selected from the group consisting of oxygen-hydrogen, nitrogen-hydrogen, ether, and carbonyl.
Claim 5
Dependent Claim
22 words
The method of claim 1 wherein at least 0.1 equivalent weight of silane is present for each equivalent weight of epoxy resin.
Claim 6
Dependent Claim
14 words
The method of claim 2 in which R is --CH 2 --CH 2 --.
Claim 7
Dependent Claim
34 words
The method of claim 1 wherein the epoxy resin is cured with sufficient amine curing agent to provide from 0.5 to about 1.2 equivalent weight of amine for each equivalent weight of epoxy resin.
Claim 8
Dependent Claim
21 words
The method of claim 6 in which about one equivalent weight of amine is present for each epoxy resin equivalent weight.
Claim 9
Dependent Claim
11 words
The method of claim 1 wherein the silane is a trimethoxysilane.
Claim 10
Dependent Claim
26 words
The method of claim 1 wherein the epoxy-polysiloxane interpenetrating polymer network is formed in the presence of sufficient filler to avoid the formation of visible domains.
Claim 11
Dependent Claim
21 words
The method of claim 9 in which the pigment volume concentration of the filler is from about 20 to about 50%.
Claim 12
Dependent Claim
29 words
The method of claim 1 wherein the interpenetrating polymer network is prepared by spraying the mixture to form a coating having a thickness from about 0.005" to about 0.02".
Claim 13
Dependent Claim
26 words
The method of claim 1 wherein substantially uniform distribution of water throughout the mixture is obtained by spraying the mixture in the presence of atmospheric moisture.
Claim 14
Dependent Claim
36 words
The method of claim 1 wherein the epoxy resin is dissolved in a ketone solvent which reversibly reacts with the amine curing agent to form a ketimine and water for the hydrolytic polycondensation of the silane.
Claim 15
Dependent Claim
28 words
The method of claim 13 wherein the ketone solvent is selected from the group consisting of acetone, methyl ethyl ketone, methyl propyl ketone, diethyl ketone, 2-hexanone, and 3-hexanone.
Claim 16
Dependent Claim
25 words
The method of claim 13 which includes exposing the mixture to water in the atmosphere to hydrolyze the ketimine to ketone and amine curing agent.
Claim 17
Dependent Claim
18 words
The method of claim 1 wherein the epoxy resin is dissolved in a mixture of xylene and alcohol.
Claim 18
Dependent Claim
24 words
The method of claim 16 wherein the alcohol is selected from the group consisting of methanol, ethanol, propanol, isopropanol, n-butanol, isobutanol, sec-butanol, and tert-butanol.
Claim 19
Dependent Claim
19 words
The method of claim 16 wherein the ratio of alcohol to xylene is at least about 1:1 by weight.
Claim 20
Dependent Claim
19 words
The method of claim 1 wherein the epoxy resin is dissolved in a mixture of a ketone and alcohol.
Claim 21
Dependent Claim
27 words
The method of claim 19 wherein the ketone is selected from the group consisting of acetone, methyl ethyl ketone, methyl propyl ketone, diethyl ketone, 2-hexanone, and 3-hexanone.
Claim 22
Dependent Claim
24 words
The method of claim 18 wherein the alcohol is selected from the group consisting of methanol, ethanol, propanol, isopropanol, n-butanol, isobutanol, sec-butanol, and tert-butanol.
Claim 23
Dependent Claim
21 words
The method of claim 18 wherein the ratio of the alcohol to the ketone is at least about 1:1 by weight.
Claim 24
Dependent Claim
87 words
The method of claim 1 wherein the amine curing agent includes an aminosilane of the general formula: Y--Si--[O--X].sub.3 where each X is independently selected from the group consisting of alkyl, hydroxyalkyl, alkoxyalkyl, and hydroxyalkoxyalkyl radicals containing less than six carbon atoms, and where Y is H[HNR-- a , in which a is an integer from 2 to about 6, and each R is a difunctional radical independently selected from the group consisting of alkyl, aryl, dialkylaryl, alkoxyalkyl, and cycloalkyl radicals, and R may vary within a Y.
Claim 25
Dependent Claim
21 words
The method of claim 23 in which at least 0.1 silane equivalent weight is present for each epoxy resin equivalent weight.
Claim 26
Dependent Claim
28 words
The method of claim 23 wherein the epoxy resin is cured with a mixture of amine curing agent having the general formula of claim 2 and an aminosilane.
Claim 27
Dependent Claim
44 words
The method of claim 23 in which Y is H[HN(CH 2 ) b -- a , where a is an integer from 1 to about 10, and b is an integer from 1 to about 6, and b may vary within a given molecule.
Claim 28
Dependent Claim
44 words
The method of claim 23 wherein the epoxy resin is cured with sufficient amine of the general formula of claim 2 and of the general formula of claim 23 to provide from 0.5 to about 1.2 amine equivalent weights per epoxy resin equivalent weight.
Claim 29
Dependent Claim
24 words
The method of claim 27 wherein the ratio of the number of amine equivalent weights to the epoxy resin equivalent weights is about 1:1.
Claim 30
Dependent Claim
25 words
The method of claim 23 wherein the epoxy-polysiloxane interpenetrating network is formed in the presence of sufficient filler to avoid the formation of visible domains.
Claim 31
Dependent Claim
20 words
The method of claim 29 in which the volume concentration of the filler is from about 20 to about 50%.
Claim 32
Dependent Claim
29 words
The method of claim 23 wherein the interpenetrating polymer network is prepared by spraying the mixture to form a coating having a thickness from about 0.005" to about 0.02".
Claim 33
Dependent Claim
27 words
The method of claim 23 wherein the substantially uniform distribution of water throughout the mixture is obtained by spraying the mixture, in the presence of atmospheric moisture.
Claim 34
Dependent Claim
34 words
The method of claim 23 wherein the epoxy resin is dissolved in a ketone solvent which reversibly reacts with amine to form a ketimine and the water for the hydrolytic polycondensation of the silane.
Claim 35
Dependent Claim
28 words
The method of claim 33 wherein the ketone solvent is selected from the group consisting of acetone, methyl ethyl ketone, methyl propyl ketone, diethyl ketone, 2-hexanone, or 3-hexanone.
Claim 36
Dependent Claim
22 words
The method of claim 33 wherein water is absorbed from the atmosphere to hydrolyze the ketimine to ketone and amine curing agent.
Claim 37
Dependent Claim
18 words
The method of claim 23 wherein the epoxy resin is dissolved in a mixture of xylene and alcohol.
Claim 38
Dependent Claim
24 words
The method of claim 36 wherein the alcohol is selected from the group consisting of methanol, ethanol, propanol, isopropanol, n-butanol, isobutanol, sec-butanol, or tert-butanol.
Claim 39
Dependent Claim
18 words
The method of claim 37 wherein the ratio of alcohol to xylene is at least 1:1 by weight.
Claim 40
Dependent Claim
19 words
The method of claim 23 wherein the epoxy resin is dissolved in a mixture of a ketone and alcohol.
Claim 41
Dependent Claim
27 words
The method of claim 39 wherein the ketone is selected from the group consisting of acetone, methyl ethyl ketone, methyl propyl ketone, diethyl ketone, 2-hexanone, and 3-hexanone.
Claim 42
Dependent Claim
24 words
The method of claim 39 wherein the alcohol is selected from the group consisting of methanol, ethanol, propanol, isopropanol, n-butanol, isobutanol, sec-butanol, and tert-butanol.
Claim 43
Dependent Claim
20 words
The method of claim 39 wherein the ratio of the alcohol to the ketone is at least 1:1 by weight.
Claim 44
Dependent Claim
129 words
The method of claim 1 where the silane is selected from the group consisting of aminosilanes and epoxysilanes, the aminosilanes having the general formula: Y--Si--[O--X].sub.3 where each X is independently selected from the group consisting of alkyl, hydroxyalkyl, alkoxyalkyl, or hydroxyalkoxyalkyl radicals containing less than 6 carbon atoms, and where Y is H[HNR-- a , where a is an integer from 2 to about 6, and each R is a difunctional radical independently selected from the group consisting of alkyl, aryl, dialkylaryl, alkoxyalkyl, and cycloalkyl radicals, and R may vary within a Y; and the epoxysilanes having the general formula: Z--Si--[O--X].sub.3 where X is defined above, and where Z is an alkyl or oxyalkyl group containing from 2 to about 8 carbon atoms and at least one oxirane group.
Claim 45
Dependent Claim
19 words
The method of claim 43 wherein the ratio of total silane equivalents to oxirane equivalents is at least 1:1.
Claim 46
Dependent Claim
35 words
The method of claim 43 wherein the source of silane is a mixture of an aminosilane, an epoxysilane, and other silanes selected from the group consisting of alkoxysilanes, alkyltrialkoxysilanes, aryltrialkoxysilanes, and hydrolytic polycondensation products thereof.
Claim 47
Dependent Claim
25 words
The method of claim 43 wherein an epoxysilane is at least about 20 molar percent of the total epoxy resin used in the interpenetrating network.
Claim 48
Dependent Claim
45 words
The method of claim 43 wherein the epoxy resin is cured with sufficient amine of the general formula of claim 2 or of the general formula of claim 23 to provide from 0.5 to about 1.2 amine equivalent weights per one epoxy resin equivalent weight.
Claim 49
Dependent Claim
24 words
The method of claim 47 wherein the ratio of the number of amine equivalents weights to the epoxy resin equivalent weights is about 1:1.
Claim 50
Dependent Claim
25 words
The method of claim 43 wherein the epoxy-polysiloxane interpenetrating network is formed in the presence of sufficient filler to avoid the formation of visible domains.
Claim 51
Dependent Claim
18 words
The method of claim 49 in which the filler volume concentration is from about 20 to about 50%.
Claim 52
Dependent Claim
29 words
The method of claim 43 wherein the interpenetrating polymer network is prepared by spraying the mixture to form a coating having a thickness from about 0.005" to about 0.02".
Claim 53
Dependent Claim
28 words
The method of claim 43 wherein the substantially uniform distribution of water throughout the mixture is obtained by spraying the mixture, thus allowing it to absorb atmospheric moisture.
Claim 54
Dependent Claim
46 words
The method of claim 43 wherein the epoxy resin is dissolved in a ketone solvent which reversibly reacts with the amine of the general formula of claim 2 or of claim 23 to form a ketimine and the water for the hydrolytic polycondensation of the silane.
Claim 55
Dependent Claim
28 words
The method of claim 53 wherein the ketone solvent is selected from the group consisting of acetone, methyl ethyl ketone, methyl propyl ketone, diethyl ketone, 2-hexanone, or 3-hexanone.
Claim 56
Dependent Claim
22 words
The method of claim 53 wherein water is absorbed from the atmosphere to hydrolyze the ketimine to ketone and amino curing agent.
Claim 57
Dependent Claim
18 words
The method of claim 43 wherein the epoxy resin is dissolved in a mixture of xylene and alcohol.
Claim 58
Dependent Claim
24 words
The method of claim 56 wherein the alcohol is selected from the group consisting of methanol, ethanol, propanol, isopropanol, n-butanol, isobutanol, sec-butanol, or tert-butanol.
Claim 59
Dependent Claim
18 words
The method of claim 56 wherein the ratio of alcohol to xylene is at least 1:1 by weight.
Claim 60
Dependent Claim
19 words
The method of claim 43 wherein the epoxy resin is dissolved in a mixture of a ketone and alcohol.
Claim 61
Dependent Claim
27 words
The method of claim 59 wherein the ketone is selected from the group consisting of acetone, methyl ethyl ketone, methyl propyl ketone, diethyl ketone, 2-hexanone, and 3-hexanone.
Claim 62
Dependent Claim
24 words
The method of claim 59 wherein the alcohol is selected from the group consisting of methanol, ethanol, propanol, isopropanol, n-butanol, isobutanol, sec-butanol, and tert-butanol.
Claim 63
Dependent Claim
20 words
The method of claim 59 wherein the ratio of the alcohol to the ketone is at least 1:1 by weight.
Claim 64
Dependent Claim
74 words
An interpenetrating polymer network prepared by the method defined in any of claims 1, 2, 3, 4, 5, 6, 7, 8, 9, 10, 11, 12, 13, 14, 15, 16, 17, 18, 19, 20, 21, 22, 23, 24, 25, 26, 27, 28, 29, 30, 31, 32, 33, 34, 35, 36, 37, 38, 39, 40, 41, 42, 43, 44, 45, 46, 47, 48, 49, 50, 51, 52, 53, 54, 55, 56, 57, 58, 59, or 60.
References Cited (Backward Citations)
US2843560A
Cited
US3455877A
Cited
US3072594A
Cited
US3131161A
Cited
US3247280A
Cited
US3496139A
Cited
US3725501A
Cited
US3868342A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-02-10 | 1984-08-11 | 1985-02-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-02-10 | 1988-08-11 | 1989-02-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-02-10 | 1992-08-11 | 1993-02-10 | $7700.00 | Window Closed / Lapsed |