Process for producing ceramic sintered bodies
Assignee: Research Institute for Special Inorganic Materials
•
Filing: 1979-01-23
•
Granted: 1981-02-03
•
Expires: 1999-01-23
Abstract
Abstract A process for producing a heat-resistant ceramic sintered body, which comses preparing polycarbosilane partly containing siloxane bonds by adding 0.01 to 15% by weight of polyborosiloxane containing phenyl groups in at least a part of the side chains of Si and having a skeletal structure composed of B, Si and O to a polysilane having the structure ##STR1## wherein n is at least 3, and R 1 and R 2 , independently from each other, represent methyl, ethyl, phenyl or hydrogen, and heating the polymer mixture in an atmosphere inert to the reaction thereby polymerizing it; mixing said polycarbosilane with a ceramic powder composed of at least one member selected from the group consisting of oxides, carbides, nitrides, borides and silicides; shaping the resulting mixture; and simultaneously with, or after, the shaping of the mixture, sintering the mixture at a temperature of from 800° C. to 2,000° C. in vacuum or in an atmosphere composed of at least one gas selected from the group consisting of inert gases, carbon monoxide gas, carbon dioxide gas, hydrogen gas, nitrogen gas and hydrocarbon gases.
Inventors
- 👤 Seishi Yajima
- 👤 Kiyohito Okamura
- 👤 Toetsu Shishido
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 04:22
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/515; C04B35/58; C04B35/584; C04B35/589; C04B33/00; C04B33/02; C04B33/13; C04B35/56; C04B35/563; C04B35/565; C04B35/571; C04B35/622; C04B35/626; C04B35/63; C04B35/6303; C04B35/6316; C08; C08G; C08G79/00; C08G79/08; C08L; C08L83/00; C08L83/16
Claims Analysis
Total Claims: 5
Claim 1
Independent Claim
181 words
A process for producing a heat-resistant ceramic sintered body, which comprises preparing polycarbosilane partly containing siloxane bonds by adding 0.01 to 15% by weight of polyborosiloxane containing phenyl groups in at least a part of the side chains of Si and having a skeletal structure composed of B, Si and O to a polysilane having the structure ##STR8## wherein n is at least 3, and R 1 and R 2 , independently from each other, represent methyl, ethyl, phenyl or hydrogen, and heating the polymer mixture in an atmosphere inert to the reaction thereby polymerizing it; mixing said polycarbosilane with a ceramic powder composed of at least one member selected from the group consisting of oxides, carbides, nitrides, borides and silicides; shaping the resulting mixture; and simultaneously with, or after, the shaping of the mixture, sintering the mixture at a temperature of from 800° C. to 2,000° C. in vacuum or in an atmosphere composed of at least one gas selected from the group consisting of inert gases, carbon monoxide gas, carbon dioxide gas, hydrogen gas, nitrogen gas and hydrocarbon gases.
Claim 2
Dependent Claim
181 words
A process for producing a heat-resistant ceramic sintered body, which comprises preparing polycarbosilane partly containing siloxane bonds by adding 0.01 to 15% by weight of polyborosiloxane containing phenyl groups in at least a part of the side chains of Si and having a skeletal structure composed of B, Si and O to a polysilane having the structure ##STR8## wherein n is at least 3, and R 1 and R 2 , independently from each other, represent methyl, ethyl, phenyl or hydrogen, and heating the polymer mixture in an atmosphere inert to the reaction thereby polymerizing it; mixing said polycarbosilane with a ceramic powder composed of at least one member selected from the group consisting of oxides, carbides, nitrides, borides and silicides; shaping the resulting mixture; and simultaneously with, or after, the shaping of the mixture, sintering the mixture at a temperature of from 800° C. to 2,000° C. in vacuum or in an atmosphere composed of at least one gas selected from the group consisting of inert gases, carbon monoxide gas, carbon dioxide gas, hydrogen gas, nitrogen gas and hydrocarbon gases.
Claim 3
Dependent Claim
60 words
The process of claim 1 wherein the ceramic powder is a ceramic powder obtained by heating said polycarbosilane partly containing siloxane bonds in vacuum or in an atmosphere composed of at least one gas selected from the group consisting of inert gases, carbon monoxide gas, carbon dioxide gas, hydrogen gas, nitrogen gas and hydrocarbon gases, and pulverizing the heated polymer.
Claim 4
Dependent Claim
85 words
The process of claim 1 wherein the mixture of the polycarbosilane and ceramic powder is heated at a temperature of not more than 800° C. in vacuum or in an atmosphere of at least one gas selected from the group consisting of inert gases, carbon monoxide gas, carbon dioxide gas, hydrogen gas, nitrogen gas and hydrocarbon gases, and then pulverized, the resulting powder is further mixed with the polycarbosilane partly containing siloxane bonds, and the mixture is then subjected to said shaping and sintering steps.
Claim 5
Dependent Claim
84 words
The process of claim 1 wherein the ceramic sinter obtained by the sintering is subjected at least once to a series of treatments consisting of impregnating the sinter with said polycarboxilane partly containing siloxane bonds and then heating the impregnated product at a temperature of from 800° C. to 2,000° C. in vacuum or in an atmosphere composed of at least one gas selected from the group consisting of inert gases, carbon monoxide gas, carbon dioxide gas, hydrogen gas, nitrogen gas and hydrocarbon gases.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-02-03 | 1984-08-04 | 1985-02-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-02-03 | 1988-08-04 | 1989-02-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-02-03 | 1992-08-04 | 1993-02-03 | $7700.00 | Window Closed / Lapsed |