Crosslinked EPDM/thermoplastic elastomer blend
Assignee: Phillips Petroleum Co
•
Filing: 1978-05-10
•
Granted: 1981-02-03
•
Expires: 1998-05-10
Abstract
Abstract A blend of a crosslinked ethylene-propylene-diene monomer (EPDM) and a thermoplastic elastomer. Such blends exhibit improved ozone resistance.
Inventors
- 👤 Roy F. Wright
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 16:56
CPC Classifications
C; C08; C08L; C08L53/00; C08L53/02
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
159 words
A now vulcanized blend comprising (a) a thermoplastic elastomer which is a conjugated diene/monovinyl-substituted aromatic compound block copolymer with the formula ABA or (AB)nY wherein A represents a block of polymerized monovinyl-substituted aromatic compound, B represents a block of conjugated diene units and Y is a residual unit from a polyfunctional coupling agent or a polyfunctional initiator and n has a value of from 2 to 6, said conjugated diene having 4 or 5 carbon atoms per molecule and said monovinyl-substituted aromatic compound having 8 or 9 carbon atoms per molecule; and (b) an EPDM polymer which was crosslinked prior to forming said blend so as to exhibit a Mooney viscosity of at least two Mooney points above that of a comparable EPDM polymer which is not crosslinked, said crosslinked EPDM polymer being present in an amount within the range of 10 to 40 weight percent based on the total weight of said EPDM polymer and said thermoplastic elastomer.
Claim 2
Dependent Claim
159 words
A now vulcanized blend comprising (a) a thermoplastic elastomer which is a conjugated diene/monovinyl-substituted aromatic compound block copolymer with the formula ABA or (AB)nY wherein A represents a block of polymerized monovinyl-substituted aromatic compound, B represents a block of conjugated diene units and Y is a residual unit from a polyfunctional coupling agent or a polyfunctional initiator and n has a value of from 2 to 6, said conjugated diene having 4 or 5 carbon atoms per molecule and said monovinyl-substituted aromatic compound having 8 or 9 carbon atoms per molecule; and (b) an EPDM polymer which was crosslinked prior to forming said blend so as to exhibit a Mooney viscosity of at least two Mooney points above that of a comparable EPDM polymer which is not crosslinked, said crosslinked EPDM polymer being present in an amount within the range of 10 to 40 weight percent based on the total weight of said EPDM polymer and said thermoplastic elastomer.
Claim 3
Dependent Claim
40 words
A blend according to claim 1 wherein said EPDM polymer has a ratio of ethylene:propylene within the range of 90:10 to 55:45 and wherein the diene monomer thereof is selected from dicyclopentadiene, 1,4-hexadiene, norbornadiene, 5-methylene-2-norbornene, 5-ethylidene-2-norbornene, 1,5-cyclooctadiene, and mixtures thereof.
Claim 4
Dependent Claim
19 words
A blend according to claim 1 wherein said monovinyl-substituted aromatic compound is styrene and said conjugated diene is butadiene.
Claim 5
Dependent Claim
24 words
A blend according to claim 1 wherein said EPDM is crosslinked with one of dicumyl peroxide, di-t-butyl peroxide, t-butyl hydroperoxide, 2,5-bis(t-butylperoxy)-2,5-dimethylhexane, and mixtures thereof.
Claim 6
Dependent Claim
66 words
A blend according to claim 1 wherein said EPDM polymer is crosslinked prior to forming said blend to an extent that the ML-4 Mooney viscosity at 115.6° C. as measured by ASTM D-1646-63 is less than 185 and at least 15 points above that of the uncrosslinked EPDM, the EPDM in each case containing the same amount of compounding ingredients and hot-mixed in the same manner.
Claim 7
Dependent Claim
56 words
A blend according to claim 1 wherein said EPDM polymer has a 83/17 weight ratio of ethylene/propylene with sufficient 5-ethylidene-2-norbornene to supply 5 carbon-carbon double bonds per 1000 carbon atoms in the polymer chain, said thermoplastic elastomer is a 70/30 weight ratio butadiene/styrene radial teleblock copolymer formed utilizing an n-butyllithium initiator and coupled with silicon tetrachloride.
Claim 8
Dependent Claim
22 words
A blend according to claim 6 containing in addition a processing aid, calcium carbonate, carbon black, naphthenic oil, and a coumarone-indene resin.
Claim 9
Dependent Claim
22 words
A process for making the blend of claim 1 EPDM polymer to crosslinking conditions and thereafter blending same with the thermoplastic elastomer.
Claim 10
Dependent Claim
77 words
A method according to claim 8 wherein said EPDM polymer is an 83/17 weight ratio ethylene/propylene polymer with sufficient 5-ethylidene-2-norbornene to supply 5 carbon-carbon double bonds per 1000 carbon atoms in the polymer chain, said thermoplastic elastomer is a 70/30 weight ratio butadiene/styrene radial block copolymer initiated with n-butyllithium and coupled and said crosslinking is effected by mixing said EPDM polymer in the presence of a peroxide at a temperature sufficient to cause generation of free radicals.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-02-03 | 1984-08-04 | 1985-02-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-02-03 | 1988-08-04 | 1989-02-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-02-03 | 1992-08-04 | 1993-02-03 | $7700.00 | Window Closed / Lapsed |