Single package additive for thermoplastic formulation
Assignee: Vista Chemical Co
•
Filing: 1979-08-03
•
Granted: 1981-02-03
•
Expires: 1999-08-03
Abstract
Abstract A friable composition single additive package for thermoplastic extrusions is provided in the instant invention. The friable composition can contain paraffin waxes, calcium stearate, various pigments, fillers, lubricants, and stabilizers.
Inventors
- 👤 Paul H. Washecheck
- 👤 Ron G. Hale
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 10:44
CPC Classifications
C; C08; C08L; C08L91/00; C08L91/06; C08L91/08
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
144 words
A process for producing an improved friable composition for addition to thermoplastic formulations during extrusion comprising mixing a paraffinic hydrocarbon wax, calcium hydroxide and a fatty acid, or a calcium salt of a fatty acid while heating to a temperature of at least 150° C. thereafter adding additives and a stabilizer and thereafter cooling to recover a solid glass-like friable composition, said paraffinic hydrocarbon wax having a drop melting point of at least 43° C., an oil content of not greater than 50 percent by weight and a needle penetration value (25° C.) in the range of 1 mm to 20 mm, said fatty acid being a C 16 -C 24 aliphatic hydrocarbon monocarboxylic acid or mixtures thereof; said stabilizer physically blended with sufficient thermoplastic resin to support the quantity of stabilizer used, said blend being formed prior to addition to the reaction mixture.
Claim 2
Dependent Claim
144 words
A process for producing an improved friable composition for addition to thermoplastic formulations during extrusion comprising mixing a paraffinic hydrocarbon wax, calcium hydroxide and a fatty acid, or a calcium salt of a fatty acid while heating to a temperature of at least 150° C. thereafter adding additives and a stabilizer and thereafter cooling to recover a solid glass-like friable composition, said paraffinic hydrocarbon wax having a drop melting point of at least 43° C., an oil content of not greater than 50 percent by weight and a needle penetration value (25° C.) in the range of 1 mm to 20 mm, said fatty acid being a C 16 -C 24 aliphatic hydrocarbon monocarboxylic acid or mixtures thereof; said stabilizer physically blended with sufficient thermoplastic resin to support the quantity of stabilizer used, said blend being formed prior to addition to the reaction mixture.
Claim 3
Dependent Claim
16 words
A process according to claim 1 wherein the mixture is heated to at least 160° C.
Claim 4
Dependent Claim
46 words
A process according to claim 1 wherein the fatty acid is mixed with the paraffinic hydrocarbon wax prior to adding the calcium hydroxide, and wherein the ratio of stablizer to thermoplastic resin is from about 1 to 4 to about 1 to 7 by weight, respectively.
Claim 5
Dependent Claim
23 words
A process according to claim 1 wherein the calcium hydroxide is mixed with the paraffinic hydrocarbon wax prior to adding the fatty acid.
Claim 6
Dependent Claim
24 words
A process according to claim 1 wherein the mole ratio of calcium hydroxide to fatty acid is in the range of 0.5/1 to 1/1.
Claim 7
Dependent Claim
14 words
A process according to claim 5 wherein the mole ratio is 0.55/1 to 1/1.
Claim 8
Dependent Claim
27 words
A process according to claim 5 wherein the weight ratio of wax to calcium salt of a fatty acid is in the range of 0.3/1 to 2.5/1.
Claim 9
Dependent Claim
23 words
A process according to claim 6 wherein the weight ratio of wax to calcium salt of a fatty acid is 0.6/1 to 1.7/1.
Claim 10
Dependent Claim
48 words
A process according to claim 2 wherein the paraffinic hydrocarbon wax has a drop melting point of at least 60° C., an oil content of not greater than 20 weight percent and a needle penetration value at 25° C. in the range of 1 mm to 10 mm.
Claim 11
Dependent Claim
33 words
A process according to claim 9 wherein the fatty acid is palmitic, stearic, oleic acid, tall oil fatty acid, eicosanic acid, behenic acid, hydrogenated tallow fatty acid, hydrogenated vegetable oil, or mixtures thereof.
Claim 12
Dependent Claim
14 words
A process according to claim 1 wherein a mixture of fatty acids is employed.
Claim 13
Dependent Claim
25 words
A process according to claim 11 wherein the mixture of fatty acids contains up to 15 weight percent of C 14 aliphatic hydrocarbon monocarboxylic acid.
Claim 14
Dependent Claim
12 words
A process according to claim 12 wherein mixtures of stabilizers are used.
Claim 15
Dependent Claim
47 words
A process according to claim 11 wherein the additives are selected from the group consisting of paraffin wax, polyethylene wax, oxidized polyethylene wax, high molecular weight esters, calcium stearate, titanium dioxide, carbon black, calcium carbonate, calcium sulfate, talc, silica, methacrylate polymer, styrene copolymers, or mixtures of these.
References Cited (Backward Citations)
US4000100A
Cited
US3905927A
Cited
US3883362A
Cited
US3883363A
Cited
US3960790A
Cited
US3979345A
Cited
US3986995A
Cited
US3985693A
Cited
US4072790A
Cited
US4040997A
Cited
US4040996A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-02-03 | 1984-08-04 | 1985-02-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-02-03 | 1988-08-04 | 1989-02-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-02-03 | 1992-08-04 | 1993-02-03 | $7700.00 | Window Closed / Lapsed |