Method for preparing a magnesia carbon brick
Assignee: KUROSAKI YOGOYO Co Ltd A CORP OF JAPAN
•
Filing: 1979-06-06
•
Granted: 1981-02-03
•
Expires: 1999-06-06
Abstract
Abstract A magnesia carbon brick comprising a mixture of magnesia clinker and carbon, novolak phenol resin and a hardening agent. A method for preparing the magnesia carbon brick comprising the steps of mixing magnesia clinker and carbon together, adding novolak phenol resin and a hardening agent to said mixture of magnesia clinker and carbon and mixing, molding and drying the resultant mixture.
Inventors
- 👤 Junji Yomota
- 👤 Fumiaki Kurashina
- 👤 Mareyasu Kamiide
- 👤 Ichiro Takita
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 06:42
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/01; C04B35/013
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
150 words
A method for preparing a magnesia carbon brick comprising the steps of molding into a brick a mixture of magnesia clinker containing at least 90 percent by weight of MgO based on the weight of said magnesia clinker, carbon, a phenolic novolak resin having an average molecular weight of 300 to 600 dissolved in at least one solvent and an amount of a curing agent therefor sufficient to convert the novolak to a thermoset condition, wherein the magnesia clinker and carbon are present in a weight ratio within the range of 70 to 95 parts and 5 to 30 parts, respectively, the phenolic novolak resin solution is at a concentration within the range of 40 to 80 percent by weight, and the amount of the phenolic novolak resin ranges from 2 to 6 percent based on the weight of the mixture of magnesia clinker and carbon, and drying the brick.
Claim 2
Independent Claim
150 words
A method for preparing a magnesia carbon brick comprising the steps of molding into a brick a mixture of magnesia clinker containing at least 90 percent by weight of MgO based on the weight of said magnesia clinker, carbon, a phenolic novolak resin having an average molecular weight of 300 to 600 dissolved in at least one solvent and an amount of a curing agent therefor sufficient to convert the novolak to a thermoset condition, wherein the magnesia clinker and carbon are present in a weight ratio within the range of 70 to 95 parts and 5 to 30 parts, respectively, the phenolic novolak resin solution is at a concentration within the range of 40 to 80 percent by weight, and the amount of the phenolic novolak resin ranges from 2 to 6 percent based on the weight of the mixture of magnesia clinker and carbon, and drying the brick.
Claim 3
Dependent Claim
51 words
The method as set forth in claim 1, in which the mixture of magnesia clinker, carbon, novolak resin dissolved in a solvent and curing agent for the novolak resin is produced by dissolving the novolak resin in the solvent and mixing the resulting solution with the other ingredients of the mixture.
Claim 4
Dependent Claim
34 words
The method as set forth in claim 2 in which said solvent is selected from the group consisting of ethylene glycol, propylene glycol, diethylene glycol, polyethylene glycol, mixtures of the foregoing glycols and glycerin.
Claim 5
Dependent Claim
29 words
The method as set forth in claim 3, in which said magnesia clinker is one selected from the group consisting of sea water magnesia clinker and fused magnesia clinker.
Claim 6
Dependent Claim
25 words
The method as set forth in claim 3, in which said carbon is one selected from the group consisting of scaling graphite and amorphous graphite.
Claim 7
Dependent Claim
27 words
The method as set forth in claim 2, in which said novolak phenol resin is dissolved in a solvent including at least one dihydric or trihydric alcohol.
Claim 8
Dependent Claim
27 words
The method as set forth in claim 1, in which said curing agent is a member selected from the group consisting of paraformaldehyde, dioxane, trioxane and hexamethylenetetraamine.
Claim 9
Dependent Claim
12 words
A magnesia carbon brick produced by the method claimed in claim 1.
Claim 10
Dependent Claim
37 words
The method as set forth in claim 1, including the further step of adding an anti-oxidant comprising at least one member selected from the group consisting of metal silicon, silicon carbide and silicon nitride to said mixture.
Claim 11
Dependent Claim
60 words
The method as set forth in claim 2, including the further step of adding a first antioxidant comprising at least one member selected from the group consisting of metal silicon, silicon carbide and silicon nitride and a second antioxidant comprising at least one member selected from the group consisting of sodium pyrophosphate, sodium hexametaphosphate and magnesium phosphate to said mixture.
Claim 12
Dependent Claim
33 words
The method as set forth in claim 10, in which at least one of said metal silicon, silicon carbide and silicon nitride powder has been previously dispersed in said novolak phenol resin solution.
Claim 13
Dependent Claim
25 words
The method as set forth in claim 11, in which said first and second antioxidants have been previously dispersed in said novolak phenol resin solution.
Claim 14
Dependent Claim
20 words
The method as set forth in claim 1, including the further step of covering said brick with a metal cover.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-02-03 | 1984-08-04 | 1985-02-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-02-03 | 1988-08-04 | 1989-02-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-02-03 | 1992-08-04 | 1993-02-03 | $7700.00 | Window Closed / Lapsed |