Process for preparing a silicone molding composition

Claim 2

A process for preparing and mixing a silicone molding composition comprising (a) mixing a silicone resin compound of R SiO 3/2 units and R 2 SiO units where R is a monovalent hydrocarbon radical and the R to Si ratio varies from 1.0 to 1.9 with an organic solvent selected from the class consisting of aliphatic alcohol solvents, ketone solvents, toluene, xylene, chlorinated hydrocarbon solvents and mixtures thereof to from a solution of 10 to 50% by weight solids; (b) adding to the solution in a kneading vessel various types of fillers, a silicone plasticizer, a pigment and a catalyst to form a paste of 75 to 95% by weight solids; (c) kneading the paste to thoroughly mix the ingredients; (d) removing at least most of the remaining solvent to leave behind a silicone molding composition in which the ingredients are thoroughly mixed and (e) reducing the silicone molding composition to particles of the appropriate size.

Claim 3

The process of claim 1 wherein steps (a), (b) and (c) are carried out at a temperature in the range of 25° to 50° C.

Claim 4

The process of claim 1 wherein the organic solvent is selected from the class consisting of acetone, n-hexane, methyl alcohol, isopropyl alcohol and mixtures thereof.

Claim 5

The process of claim 1 wherein from 5 to 75% by weight of the solvent is an aliphatic alcohol of from 1 to 8 carbon atoms which alcohol acts as a stabilizer.

Claim 6

The process of claim 1 wherein step (d) is carried out by heating the paste at 80°-90° C. for up to 15 seconds to remove the solvent and step (e) is carried out by grinding the residue.

Claim 7

The process of claim 1 wherein step (d) and (e) are carried out by spray drying the paste in spray drying equipment in which the paste is contacted during the spray drying with a superheated solvent so that the solvent is removed from the paste and is removed as a vapor and is recycled to be used to dissolve additional silicone molding ingredients in a continuous process.

Claim 8

The process of claim 6 wherein the particles obtained from the spray dryer are processed through a separator wherein the particles of the right size are passed to a storage bin wherein the over-sized particles are ground and passed back to the separator for reprocessing and wherein the fines are passed with a minor amount of solvent back to the kneading vessel in a continuous manner.

Claim 9

The process of claim 7 wherein the superheated solvent is passed to the spray dryer continuously as the solvent removed from the paste is recovered, purified by passing through dust collectors and then along with fresh solvent recycled to said kneading vessel and said spray dryer as needed in a continuous manner.

Claim 10

The process of claim 1 wherein the silicone resin contains from 4 to 8% hydroxy groups and 2 to 4% alkoxy groups.

Claim 11

The process of claim 1 wherein the various types of fillers are ground glass, glass fibers and fumed silica.

Claim 12

The process of claim 10 wherein the fumed silica is treated with an octamethylcyclotetrasiloxane.

Claim 13

The process of claim 1 wherein the catalyst is a mixture of lead compound and an acid selected from the class consisting of carboxylic acids and carboxylic anhydrides.

Claim 14

The process of claim 12 wherein the catalyst is a mixture of lead carbonate and benzoic anhydrides.

Claim 15

The process of claim 1 wherein the silicone plasticizer is a phenyl-containing dimethylpolysiloxane fluid of a viscosity varying from 100 to 10,000 centipoise at 25° C.

Claim 16

A continuous process for preparing and mixing a silicone molding composition comprising (a) mixing a silicone resin composed of R SiO 3/2 units and R 2 SiO units where R is a monovalent hydrocarbon radical and the R to Si ratio varies from 1.0 to 1.9 with a solvent selected from the class consisting of aliphatic alcohol solvents, ketone solvents, toluene, xylene, and chlorinated hydrocarbon solvents and mixtures thereof to form a slurry or a solution of 10 to 50% solids; (b) adding to the slurry or the solution in a kneading vessel various types of fillers, a silicone plasticizer, a pigment and a catalyst to form a paste of 85% to 95% by weight solids; (c) kneading the paste to thoroughly mix the ingredients wherein the above steps are carried out at a temperature in the range of 25° to 50° C.; (d) continuously passing the paste in contact with superheated solvent vapor in a spray dryer; (e) removing at least most of the solvent from said paste to form solid particles of said silicone molding composition and continuously removing said solvent as well as said superheated solvent from said sprayer dryer purifying said superheated solvent by passing it through dust collectors to remove solid particles therefrom and passing it along with fresh solvent as needed into said spray dryer and said kneading vessel; (f) transferring said solid particles to a separator wherein the particles of the appropriate size are separated continuously and transferred into a storage bin, wherein the over-sized particles are separated, reground and passed back into said separator for sizing; (g) transferring the fines and any solvent collected in said separator back into said kneading vessel continuously; and (h) collecting from said storage bin the appropriate size solid particles of a uniformly mixed silicone molding composition.

Claim 17

A continuous process for preparing and mixing a silicone molding composition comprising (a) mixing a silicone resin composed of R SiO 3/2 units and R 2 SiO units where R is a monovalent hydrocarbon radical and the R to Si ratio varies from 1.0 to 1.9 with a solvent selected from the class consisting of aliphatic alcohol solvents, ketone solvents, toluene, xylene, and chlorinated hydrocarbon solvents and mixtures thereof to form a slurry or a solution of 10 to 50% solids; (b) adding to the slurry or the solution in a kneading vessel various types of fillers, a silicone plasticizer, a pigment and a catalyst to form a paste of 85% to 95% by weight solids; (c) kneading the paste to thoroughly mix the ingredients wherein the above steps are carried out at a temperature in the range of 25° to 50° C.; (d) continuously passing the paste in contact with superheated solvent vapor in a spray dryer; (e) removing at least most of the solvent from said paste to form solid particles of said silicone molding composition and continuously removing said solvent as well as said superheated solvent from said sprayer dryer purifying said superheated solvent by passing it through dust collectors to remove solid particles therefrom and passing it along with fresh solvent as needed into said spray dryer and said kneading vessel; (f) transferring said solid particles to a separator wherein the particles of the appropriate size are separated continuously and transferred into a storage bin, wherein the over-sized particles are separated, reground and passed back into said separator for sizing; (g) transferring the fines and any solvent collected in said separator back into said kneading vessel continuously; and (h) collecting from said storage bin the appropriate size solid particles of a uniformly mixed silicone molding composition.