Metallic supported catalytic system and a method of making it
Assignee: Ford Motor Co
•
Filing: 1979-03-26
•
Granted: 1981-01-27
•
Expires: 1999-03-26
Abstract
Abstract A method of making and using a metallic supported catalytic system for automotive emission control is disclosed. A plain carbon steel foil is formed into a matrix having a plurality of aligned micropassages; forming is preferably carried out by corrugating one strip of foil and winding said corrugated strip along with one or more noncorrugated foil strips to create a honeycomb matrix. The formed matrix is then immersed in a hot lead bath containing alloying ingredients which displace iron atoms in said foil to provide diffusion alloying substantially throughout the entire thickness of said foil. The contact points between said foil strips are diffusion bonded to lock the entire matrix. The alloyed matrix is then heated to form an oxide film from at least one of the alloying ingredients. The bonded matrix is then coated with a refractory wash and with a catalytic ingredient. The entire coated and heat treated matrix is then placed in a suitable housing through which hot automotive emissions are directed with a predetermined pressure, flow pattern and chemical content for effecting fusion of the coatings and emission cleanup.
Inventors
- 👤 Richard G. Davies
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 23:00
CPC Classifications
B; B01; B01D; B01D53/00; B01D53/34; B01D53/74; B01D53/86; B01J; B01J37/00; B01J37/02; B01J37/024
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
232 words
The method of making a catalyst system, comprising: (a) preparing a plain carbon steel foil having a thickness of 0.002 inches or less, the steel having a carbon content of 0.08% or less, said preparation being carried out with cold rolling and substantially reduced annealing; (b) forming said steel foil into a matrix defining a plurality of aligned passages; (c) immersing said steel foil matrix in a high heat transfer medium containing chromium and aluminum for a period of 2-4 hours at a temperature of about 1100° C., said chromium and aluminum atoms migrating and diffusing into the steel foil surface in exchange for iron atoms, said diffusion penetrating to the core of the foil; (d) subjecting said matrix to heated flowing air in the temperature range of about 1100° C. for a period of about 1-5 hours, whereby a thin alumina film is heat grown from the aluminum atoms within said metal substrate and oxygen in said flowing air; (e) coating the surfaces of the heat treated matrix with a refractory wash which is then dried to form a porous film on said surfaces; (f) depositing a catalytic ingredient onto the coating of said heat treated matrix for impregnation and coating thereof; (g) placing said coated and heat treated matrix in a suitable housing through which automotive exhaust gas emissions are passed, said gases having a temperature of about 600°-1000° C.
Claim 2
Independent Claim
232 words
The method of making a catalyst system, comprising: (a) preparing a plain carbon steel foil having a thickness of 0.002 inches or less, the steel having a carbon content of 0.08% or less, said preparation being carried out with cold rolling and substantially reduced annealing; (b) forming said steel foil into a matrix defining a plurality of aligned passages; (c) immersing said steel foil matrix in a high heat transfer medium containing chromium and aluminum for a period of 2-4 hours at a temperature of about 1100° C., said chromium and aluminum atoms migrating and diffusing into the steel foil surface in exchange for iron atoms, said diffusion penetrating to the core of the foil; (d) subjecting said matrix to heated flowing air in the temperature range of about 1100° C. for a period of about 1-5 hours, whereby a thin alumina film is heat grown from the aluminum atoms within said metal substrate and oxygen in said flowing air; (e) coating the surfaces of the heat treated matrix with a refractory wash which is then dried to form a porous film on said surfaces; (f) depositing a catalytic ingredient onto the coating of said heat treated matrix for impregnation and coating thereof; (g) placing said coated and heat treated matrix in a suitable housing through which automotive exhaust gas emissions are passed, said gases having a temperature of about 600°-1000° C.
Claim 3
Dependent Claim
30 words
The method as in claim 1, in which said step (c) is carried out with successive immersion of said matrix in separate baths, one containing chromium and the other aluminum.
Claim 4
Dependent Claim
62 words
The method as in claim 1, in which said chromium and aluminum diffusion creates a chromium and aluminum gradient, the chromium gradient being constituted with at least 15% at the core of said foil and about 35% at the surface thereof, the aluminum gradient being constituted with about 4% at the core of said foil and about 12% at the surface thereof.
Claim 5
Dependent Claim
62 words
The method as in claim 1, in which in step (b) said matrix is formed by pleating a first sheet of said steel foil, winding said pleated sheet sandwiched by one or more uncorrugated sheets of steel foil to form a honeycomb matrix, the diffusion alloying serving to bond said sheets together at contact points by a bridge of diffused alloying ingredients.
Claim 6
Dependent Claim
29 words
The method as in claim 1, in which in step (e) the catalytic ingredient is platinum and is coated thereon by dipping said matrix in a platinum salt solution.
Claim 7
Dependent Claim
167 words
A catalytic system for automotive use, comprising: (a) a foraminous matrix defining a plurality of aligned micropassages each having a general cross sectional area less than 0.005 in 2 , said matrix walls being constituted of an iron based chromium-aluminum foil having a thickness lless than 0.003 inch, at least two plys of said foil engaging at separated contact points to define said micropassages; (b) a chemically converted alumina coating along and on the surface of said matrix, which alumina is formed from aluminum atoms derived from said matrix metal upon exposure to flowing oxygen at high temperature; (c) means on said chemically converted alumina coating forming a highly porous refractory coating promoting increased surface area; and (d) a catalytic ingredient coated and impregnated onto said porous refractory coating, said system being particularly characterized by the existence of a diffused alloy bond between all contact points of said matrix and by the existence of an alloying gradient between the surface and core of said thin matrix walls.
Claim 8
Dependent Claim
167 words
A catalytic system for automotive use, comprising: (a) a foraminous matrix defining a plurality of aligned micropassages each having a general cross sectional area less than 0.005 in 2 , said matrix walls being constituted of an iron based chromium-aluminum foil having a thickness lless than 0.003 inch, at least two plys of said foil engaging at separated contact points to define said micropassages; (b) a chemically converted alumina coating along and on the surface of said matrix, which alumina is formed from aluminum atoms derived from said matrix metal upon exposure to flowing oxygen at high temperature; (c) means on said chemically converted alumina coating forming a highly porous refractory coating promoting increased surface area; and (d) a catalytic ingredient coated and impregnated onto said porous refractory coating, said system being particularly characterized by the existence of a diffused alloy bond between all contact points of said matrix and by the existence of an alloying gradient between the surface and core of said thin matrix walls.
Claim 9
Dependent Claim
27 words
A catalytic system as in claim 6, in which said porous refractory coating is comprised of alumina deposited as a wash in the thickness range of 0.00025-0.003".
Claim 10
Independent Claim
103 words
A method of making a catalyst system, comprising: (a) forming a plain carbon steel foil into a matrix defining a plurality of passages; (b) immersing said matrix in a high heat transfer medium containing one or more alloying elements for a period sufficient to permit diffusion of the alloying elements throughout the thickness of said foil; (c) removing said matrix from said medium and then heating to a temperature to oxidize at least one of the alloying elements to form an oxide coating on the surface of said matrix; and (d) coating said matrix with a porous refractory film containing a catalytic ingredient.
Claim 11
Independent Claim
103 words
A method of making a catalyst system, comprising: (a) forming a plain carbon steel foil into a matrix defining a plurality of passages; (b) immersing said matrix in a high heat transfer medium containing one or more alloying elements for a period sufficient to permit diffusion of the alloying elements throughout the thickness of said foil; (c) removing said matrix from said medium and then heating to a temperature to oxidize at least one of the alloying elements to form an oxide coating on the surface of said matrix; and (d) coating said matrix with a porous refractory film containing a catalytic ingredient.
Claim 12
Dependent Claim
24 words
The method as in claim 8, which additionally comprises heating the coated matrix resulting from step (d) to fuse said coatings and matrix together.
Claim 13
Dependent Claim
29 words
The method as in claim 9, in which said last heating is carried out in service on an automobile by use of heated exhaust gases from the automobile engine.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-01-27 | 1984-07-28 | 1985-01-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-01-27 | 1988-07-28 | 1989-01-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-01-27 | 1992-07-28 | 1993-01-27 | $7700.00 | Window Closed / Lapsed |