Wall covering comprising a web having an impregnation and a back coating
Assignee: Chelsea Industries Inc
•
Filing: 1979-01-23
•
Granted: 1981-01-20
•
Expires: 1999-01-23
Abstract
Abstract A wall covering composed of a base sheet of non-woven polyester material saturated to give it strength, fire retardancy, and opacity and further provides the material with a density that prevents the coating applied to the back from seaping through the sheet. The base sheet is coated on the back to give it greater opacity and make it fungus and mildew resistant. The back coating may also control the thickness as well as the softness or firmness of the sheet. The front surface of the sheet is then transfer printed with the particular design desired.
Inventors
- 👤 Samuel P. Hirst
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 16:49
CPC Classifications
D; D06; D06N; D06N7/00; D06N7/0002; D06N2209/00; D06N2209/08; D06N2209/0853; D06N2209/16; D06N2209/1671; Y; Y10; Y10S; Y10S428/00; Y10S428/907; Y10S428/914; Y10T; Y10T428/00; Y10T428/24; Y10T428/24802; Y10T428/24942; Y10T428/2495; Y10T428/24967; Y10T428/26; Y10T428/266; Y10T442/00; Y10T442/20; Y10T442/2525; Y10T442/2533; Y10T442/2631
Claims Analysis
Total Claims: 24
Claim 1
Independent Claim
81 words
A wall covering sheet comprising a base layer of thin non-woven polyester material impregnated with a saturant to provide strength, fire retardancy and fungus and mildew resistance to the sheet but having a fabric feel to at least the front surface thereof, a coating applied to the back of the sheet to provide opacity to the sheet and prevent adhesive applied to the back of the sheet from striking through it, and a pattern printed on the front of the sheet.
Claim 2
Dependent Claim
81 words
A wall covering sheet comprising a base layer of thin non-woven polyester material impregnated with a saturant to provide strength, fire retardancy and fungus and mildew resistance to the sheet but having a fabric feel to at least the front surface thereof, a coating applied to the back of the sheet to provide opacity to the sheet and prevent adhesive applied to the back of the sheet from striking through it, and a pattern printed on the front of the sheet.
Claim 3
Dependent Claim
30 words
A wall covering sheet as defined in claim 1 further characterized by said impregnated base layer being approximately 0.011 inches thick and said coated sheet being approximately 0.013 inches thick.
Claim 4
Dependent Claim
23 words
A wall covering sheet as defined in claim 1 further characterized by the impregnated base layer and the coating being the same color.
Claim 5
Dependent Claim
26 words
A wall covering sheet as defined in claim 1 wherein said saturant and coating are both of a compatible material including a heat reactive acrylic latex.
Claim 6
Dependent Claim
19 words
A wall covering sheet as defined in claim 4 wherein said saturant also comprises antimony oxide and titanium dioxide.
Claim 7
Dependent Claim
19 words
A wall covering sheet as defined in claim 4 wherein said coating also comprises calcium carbonate and titanium dioxide.
Claim 8
Dependent Claim
18 words
A wall covering sheet as defined in claim 6 wherein the major coating component weightwise is calcium carbonate.
Claim 9
Independent Claim
111 words
A method of making wall covering material comprising the steps of providing a continuous web of non-woven material, impregnating the non-woven web with a viscous liquid to increase its strength, fire retardancy and opacity, curing the impregnated web by passing it through a heating oven, next applying a viscous coating material to the back of the continuous non-woven web, which coating is compatible with and bonds to the impregnating material to further increase the opacity and thickness of the web and provide a screen to prevent adhesive applied to the back from striking through the non-woven web, and drying the coating material by passing the web through a second heating oven.
Claim 10
Independent Claim
111 words
A method of making wall covering material comprising the steps of providing a continuous web of non-woven material, impregnating the non-woven web with a viscous liquid to increase its strength, fire retardancy and opacity, curing the impregnated web by passing it through a heating oven, next applying a viscous coating material to the back of the continuous non-woven web, which coating is compatible with and bonds to the impregnating material to further increase the opacity and thickness of the web and provide a screen to prevent adhesive applied to the back from striking through the non-woven web, and drying the coating material by passing the web through a second heating oven.
Claim 11
Dependent Claim
23 words
A method as defined in claim 8 further characterized by transfer printing the upper surface of the non-woven web with the desired pattern.
Claim 12
Dependent Claim
27 words
A method as defined in claim 8 further characterized by said continuous web being a polyester and said impregnating and coating materials being of the same color.
Claim 13
Dependent Claim
34 words
A method as defined in claim 8 further characterized by said impregnating material including a heat reactive acrylic latex and leaving the filaments of the non-woven web sufficiently exposed to absorb transfer printing inks.
Claim 14
Independent Claim
67 words
A method of making a wall covering material comprising the steps of providing a thin web of material and impregnating the web with a saturant to increase its thickness, curing the impregnated web and thereafter applying a coating to the back of the web to form a barrier for adhesive to be applied to the back and to further increase the web thickness, and drying the coating.
Claim 15
Independent Claim
67 words
A method of making a wall covering material comprising the steps of providing a thin web of material and impregnating the web with a saturant to increase its thickness, curing the impregnated web and thereafter applying a coating to the back of the web to form a barrier for adhesive to be applied to the back and to further increase the web thickness, and drying the coating.
Claim 16
Dependent Claim
36 words
A method as defined in claim 12 further characterized by said web being a non-woven polyester material, and limiting the thickness of the impregnating material so that the front of the sheet has a fabric-like feel.
Claim 17
Dependent Claim
44 words
A method as defined in claim 13 further characterized by said web being in the order of approximately 0.009 inch in thickness, said saturant increasing the web thickness to approximately 0.011 inch, and said coating further increasing the web thickness to approximately 0.013 inch.
Claim 18
Dependent Claim
22 words
A method as defined in claim 8 wherein the impregnating is controlled to provide a predetermined amount of saturant in the web.
Claim 19
Dependent Claim
43 words
A method as defined in claim 8 wherein the step of curing occurs in two heat zones including curing at a temperature in the range of 200° F. to 250° F. followed by curing in the range of 250° F. to 300° F.
Claim 20
Dependent Claim
30 words
A method as defined in claim 8 wherein the step of curing occurs in two heat zones including curing at a first temperature followed by curing at a higher temperature.
Claim 21
Dependent Claim
18 words
A method as defined in claim 17 wherein the web is in the first oven for 45-60 seconds.
Claim 22
Dependent Claim
20 words
A method as defined in claim 16 wherein the drying occurs at a temperature on the order of 375° F.
Claim 23
Dependent Claim
21 words
A method as defined in claim 17 wherein the drying occurs at a temperature still greater than said higher curing temperature.
Claim 24
Dependent Claim
19 words
A method as defined in claim 19 further characterized by said coating material including a heat reactive acrylic latex.
References Cited (Backward Citations)
US388472A
Cited
US1026793A
Cited
US3160548A
Cited
US3212957A
Cited
US3314840A
Cited
US3294618A
Cited
US3616146A
Cited
US3795567A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-01-20 | 1984-07-21 | 1985-01-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-01-20 | 1988-07-21 | 1989-01-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-01-20 | 1992-07-21 | 1993-01-20 | $7700.00 | Window Closed / Lapsed |