Assignee: EIDP Inc
•
Filing: 1979-11-30
•
Granted: 1981-01-20
•
Expires: 1999-11-30
Abstract
Abstract A polyamine/epoxy ether graft copolymer having an acrylic polamine backbone with secondary amine and hydroxy functionality, part of which is terminal primary hydroxy groups, onto which is grafted an epoxy ether. The ether is an epoxy resin preferably reacted with nonylphenol resulting in a monoepoxide ether with one or less epoxy group per epoxy ether molecule. The ether is reacted with part of the secondary amine on the acrylic backbone. This system can be formulated to a nearly-neutral pH cathodic dispersion with good cure response at 150°-175° C. using conventional aminoplast crosslinkers.
Inventors
- 👤 Isidor Hazan
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 05:57
CPC Classifications
C; C09; C09D; C09D5/00; C09D5/44; C09D5/4407; C09D5/4411; C09D5/4419; C09D5/443; C09D5/4434; C09D5/4488
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
169 words
As a new composition of matter, a graft copolymer comprising a mono-epoxide portion grafted onto an acrylic-amine backbone portion, which portions consist essentially of, by weight based on the graft copolymer, about: (a) 25-60% of an acrylic-amine backbone copolymer contributing: 14.7-35% of secondary amine acrylate or methacrylate, giving 0.08 to 0.2 equivalent of tertiary amine per 100 grams of graft copolymer, 7-17% of hydroxy-functional acrylate or methacrylate, 3-7.3% ethyl acrylate or methyl methacrylate, and 0.3-0.7% mercaptoethanol, giving primary terminal hydroxy functionality, graft polymerized with (b) and (c): (b) 33-60% of an epoxy copolymer of a condensation polymer of equimolar proportions of epichlorohydrin and bisphenol-A and reacted with an entity selected from the group consisting of alkyl phenols, alkyl alcohols and alkyl hydroxy ethers, with 1-20 carbon atoms in the alkyl groups, hydroxyamines, fatty amines and mercaptans, in a mole ratio of epoxy resin to said entity in the range of 1/1.1-1.9, and (c) 7-15% of a glycidyl ester of a tertiary carboxylic acid containing 9 to 11 carbon atoms.
Claim 2
Dependent Claim
169 words
As a new composition of matter, a graft copolymer comprising a mono-epoxide portion grafted onto an acrylic-amine backbone portion, which portions consist essentially of, by weight based on the graft copolymer, about: (a) 25-60% of an acrylic-amine backbone copolymer contributing: 14.7-35% of secondary amine acrylate or methacrylate, giving 0.08 to 0.2 equivalent of tertiary amine per 100 grams of graft copolymer, 7-17% of hydroxy-functional acrylate or methacrylate, 3-7.3% ethyl acrylate or methyl methacrylate, and 0.3-0.7% mercaptoethanol, giving primary terminal hydroxy functionality, graft polymerized with (b) and (c): (b) 33-60% of an epoxy copolymer of a condensation polymer of equimolar proportions of epichlorohydrin and bisphenol-A and reacted with an entity selected from the group consisting of alkyl phenols, alkyl alcohols and alkyl hydroxy ethers, with 1-20 carbon atoms in the alkyl groups, hydroxyamines, fatty amines and mercaptans, in a mole ratio of epoxy resin to said entity in the range of 1/1.1-1.9, and (c) 7-15% of a glycidyl ester of a tertiary carboxylic acid containing 9 to 11 carbon atoms.
Claim 3
Dependent Claim
146 words
A graft copolymer of claim 1 comprising a mono-epoxide portion grafted onto an acrylic-amine backbone portion, which portions consist essentially of, by weight based on the graft copolymer, about: (a) 28-27% of an acrylic-amine backbone copolymer contributing: 16.5-21.8% of secondary amine acrylate or methacrylate, giving 0.08 to 0.2 equivalent of tertiary amine per 100 grams of graft copolymer, 7.8-10.4% of hydroxy-functional acrylate of methacrylate, 3,4-4.4% ethyl acrylate or methyl methacrylate, and 0.3-0.4% mercaptoethanol, giving primary terminal hydroxy functionality, graft polymerized with (b) and (c): (b) 54-62% of an epoxy copolymer of a condensation polymer of equimolar proportions of epichlorohydrin and bisphenol-A and reacted with an entity selected from the group consisting of nonylphenol and dodecyl mercaptan in a mole ratio of epoxy resin to said entity of 1/1.4-1.7, and (c) 1-25% of a glycidyl ester of a tertiary carboxylic acid containing 9 to 11 carbon atoms.
Claim 4
Dependent Claim
26 words
The graft copolymer of claim 1 wherein the secondary amine is a methacrylate obtained by polymerization with the other backbone ingredients of tertiary butyl aminoethyl methacrylate.
Claim 5
Dependent Claim
21 words
The graft copolymer of claim 3 wherein the selected entity in the epoxy copolymer is at least one selected from para-nonylphenol.
Claim 6
Dependent Claim
101 words
The graft copolymer of claim 4 consisting essentially of, by weight based on the graft copolymer, about: (a) 33% of an acrylic amine backbone copolymer contributing: 19.4% of tertiary butyl aminoethyl methacrylate, giving about 0.1 equivalent of tertiary amine per 100 grams of graft copolymer, 9.3% hydroxyethyl methacrylate, 4% ethyl acrylate, and 0.3% mercaptoethanol, graft polymerized with (b) and (c): (b) 55% of an epoxy copolymer of a condensation polymer of equimolar proportions of epichlorohydrin and bisphenol-A reacted with nonylphenol at a molar ratio of epoxy resin to nonylphenol of 1/1.7, and (c) 12% of the glycidyl ester of versatic acid.
Claim 7
Dependent Claim
95 words
The graft copolymer of claim 4 consisting essentially of, by weight based on the graft copolymer, about: (a) 25% of an acrylic-amine backbone copolymer contributing: 14.7% of tertiary butyl aminoethyl methacrylate, giving about 0.1 equivalent of tertiary amine per 100 grams of graft copolymer, 7.7% hydroxyethyl methacrylate, 3% ethyl acrylate, and 0.3% mercaptoethanol, graft polymerized with (b) and (c): (b) 70% of an epoxy copolymer of equimolar proportions of epichlorohydrin and bisphenol-A reacted with nonylphenol at molar ratio of epoxy resin to nonylphenol of 1/1.7, and (c) 5% of the glycidyl ester of versatic acid.
Claim 8
Dependent Claim
47 words
A coating composition comprising a. graft copolymer of claims 1, 2, 3, 4, 5 or 6 mixed with b. as an ionizing agent, organic acid volatile at the curing temperature, present in an amount to give a pH of 6.0 to 7.0, and c. a liquid carrier.
Claim 9
Dependent Claim
58 words
A coating composition comprising a. graft copolymer of claims 1, 2, 3, 4, 5 or 6 mixed with b. as an ionizing agent, organix acid volatile at temperatures used to crosslink the paint selected from lactic, acetic, succinic and citric acids, present in amounts to give a pH of 6.0 to 7.0, and c. an aqueous liquid carrier.
Claim 10
Dependent Claim
52 words
A coating composition comprising a. graft copolymer of claims 1, 2, 3, 4, 5 or 6 mixed with b. a nitrogen resin crosslinker, c. as an ionizing agent, organic acid volatile at the curing temperature, present in an amount to give a pH of 6.0 to 7.0, and d. a liquid carrier.
Claim 11
Dependent Claim
68 words
A coating composition comprising a. graft copolymer of claims 1, 2, 3, 4, 5 or 6 mixed with b. nitrogen resin crosslinker selected from benzoguanamine-formaldehyde and urea-formaldehyde resins, c. as an ionizing agent, organic acid volatile at temperatures used to crosslink the paint selected from lactic, acetic, succinic and citric acids, present in amounts to give a pH of 6.0 to 7.0, and d. an aqueous liquid carrier.
Claim 12
Dependent Claim
119 words
In a process for electrocoating with paint a cathodically-charged substrate immersed in a coating bath containing an aqueous dispersion of said paint, said bath having a cathode zone containing said substrate and an anode zone containing a charged anode, the charged electrodes being maintained in electrical contact with each other by means of said bath, wherein said bath comprises a cationic film-forming polymer, an acidic ionizing agent, the improvement which comprises: employing an organic acid which is volatile at temperatures used to crosslink the film-forming polymer as the acidic ionizing agent; employing as the cationic film-forming polymer a graft copolymer of claim 1, 2, 3, 4, 5 or 6, and subsequently curing the paint to crosslink the film-forming polymers.
Claim 13
Dependent Claim
156 words
In a process for electrocoating with paing a cathodically-charged substrate immersed in a coating bath containing an aqueous dispersion of said paint, said bath having a cathode zone containing said substrate and an anode zone containing a charged anode, the charged electrodes being maintained in electrical contact with each other by means of said bath, wherein said bath comprises a cationic film-forming polymer, an acidic ionizing agent, and a crosslinking agent, the improvement which comprises: employing an organic acid which is volatile at temperatures used to crosslink the film-forming polymer as the acidic ionizing agent; employing as the cationic film-forming polymer a graft copolymer of claim 1, 2, 3, 4, 5 or 6, and employing as the crosslinking agent a composition which is nonreactive in the bath but reactive with said film-forming polymer at elevated temperatures to crosslink the polymers to form a durable paint film, and subsequently curing the paint to crosslink the film-forming polymers.
Claim 14
Dependent Claim
176 words
In a process for electrocoating with paint a cathodically-charged substrate immersed in a coating bath containing an aqueous dispersion of said paint, said bath having a cathode zone containing said substrate and an anode zone containing a charged anode, the charged electrodes being maintained in electrical contact with each other by means of said bath, wherein said bath comprises a cationic film-forming polymer, an acidic ionizing agent, and a crosslinking agent, the improvement which comprises: employing an organic acid which is volatile at temperatures used to crosslink the film-forming polymer as the acidic ionizing agent; employing as the cationic film-forming polymer a graft copolymer of claim 1, 2, 3, 4, 5 or 6, and employing as the crosslinking agent a composition which is nonreactive in the bath but reactive with said film-forming polymer at elevated temperatures to crosslink the polymers to form a durable paint film, and subsequently curing the paint to crosslink the film-forming polymers by heating the coated substrate to a temperature of at least about 175° C. for at least about 30 minutes.
References Cited (Backward Citations)
US3366706A
Cited
US4167499A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-01-20 | 1984-07-21 | 1985-01-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-01-20 | 1988-07-21 | 1989-01-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-01-20 | 1992-07-21 | 1993-01-20 | $7700.00 | Window Closed / Lapsed |