Method of polymerizing vinyl chloride in seeded microsuspension
Assignee: Rhone Poulenc Industries SA
•
Filing: 1978-06-12
•
Granted: 1981-01-13
•
Expires: 1998-06-12
Abstract
Abstract A method for preparing polymers of vinyl chloride in which polymerization of the corresponding monomer or monomers is carried out in microsuspension in the presence of a seeding product in the form of a dispersion of particles of a vinyl polymer previously prepared by polymerization in microsuspension, the particles of which contain at least one organic soluble initiator, without any complementary addition of initiator and in the presence of one or more other seeding products in the form of dispersion of vinyl polymer, the sizes of which differ from one another and from the particles of the first seeding product.
Inventors
- 👤 Thomas Kemp
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 22:17
CPC Classifications
C; C08; C08F; C08F259/00; C08F259/02; C08F259/04; Y; Y10; Y10S; Y10S526/00; Y10S526/909
Claims Analysis
Total Claims: 20
Claim 1
Independent Claim
201 words
A method of preparing polymers of vinyl chloride, comprising: preparing an aqueous dispersion of polymers of vinyl chloride containing at least two populations of particles with different average diameters of less than 5 μm, with a polymer concentration of up to 75%, by polymerizing the corresponding monomer or monomers in microsuspension, without any complementary addition of initiator, with or without an emulsifier, in the presence of a first seeding product in the form of an aqueous dispersion of particles of a vinyl polymer, previously prepared by polymerization in microsuspension, the particles of which contain at least one initiator soluble in organic material, and one or more other seeding products in the form of aqueous dispersions of particles of vinyl polymer, the average diameters of which differ from one another and from the particles diameter of the first seeding product, at least one of these seeding products has particles substantially free of initiator and an average diameter less than the average diameter of the particles of the first seeding product, in which the particles of the first seeding product with initiator has an average diameter within the range of 0.05-1.5 μm; separating the polymer of vinyl chloride from the obtained aqueous dispersion.
Claim 2
Independent Claim
201 words
A method of preparing polymers of vinyl chloride, comprising: preparing an aqueous dispersion of polymers of vinyl chloride containing at least two populations of particles with different average diameters of less than 5 μm, with a polymer concentration of up to 75%, by polymerizing the corresponding monomer or monomers in microsuspension, without any complementary addition of initiator, with or without an emulsifier, in the presence of a first seeding product in the form of an aqueous dispersion of particles of a vinyl polymer, previously prepared by polymerization in microsuspension, the particles of which contain at least one initiator soluble in organic material, and one or more other seeding products in the form of aqueous dispersions of particles of vinyl polymer, the average diameters of which differ from one another and from the particles diameter of the first seeding product, at least one of these seeding products has particles substantially free of initiator and an average diameter less than the average diameter of the particles of the first seeding product, in which the particles of the first seeding product with initiator has an average diameter within the range of 0.05-1.5 μm; separating the polymer of vinyl chloride from the obtained aqueous dispersion.
Claim 3
Dependent Claim
34 words
The method as claimed in claim 1, in which the vinyl chloride polymer is polyvinyl chloride or a copolymer containing at least 50% by weight of vinyl chloride and at least one copolymerizable monomer.
Claim 4
Dependent Claim
41 words
The method as claimed in claim 1, in which the vinyl polymer is selected from the group consisting of homopolymers of vinyl chloride, copolymers of vinyl chloride with copolymerizable monomers, homopolymers of copolymerizable monomers and copolymers of said copolymerizable monomers together.
Claim 5
Independent Claim
250 words
A method of preparing polymers of vinyl chloride, comprising: preparing an aqueous dispersion of polymers of vinyl chloride containing at least two populations of particles with different average diameters of less than 5 μm, with a polymer concentration of up to 75%, by polymerizing the corresponding monomer or monomers in microsuspension, without any complementary addition of initiator, with or without an emulsifier, in the presence of a first seeding product in the form of an aqueous dispersion of particles of a vinyl polymer, previously prepared by polymerization in microsuspension, the particles of which contain at least one initiator soluble in organic material and one or more other seeding products in the form of aqueous dispersions of particles of vinyl polymer, the average diameters of which differ from one another and from the particles diameter of the first seeding product, at least one of these seeding products has particles substantially free of initiator and an average diameter less than the average diameter of the particles of the first seeding product; separating the polymer of vinyl chloride from the obtained aqueous dispersion, in which the formed dispersion contains three populations of particles with respective average diameters of from 0.4 to 2.5 μm, from 0.15 to 1 μm and from 0.05 to 0.4 μm, the diameter ratios of large particles/medium particles and medium particles/fine particles similar or different ranging from 1 to 20/1, and in weight ratios of large particles/medium particles and medium particles/fine particles, similar or different, ranging from 0.1 to 20/1.
Claim 6
Independent Claim
250 words
A method of preparing polymers of vinyl chloride, comprising: preparing an aqueous dispersion of polymers of vinyl chloride containing at least two populations of particles with different average diameters of less than 5 μm, with a polymer concentration of up to 75%, by polymerizing the corresponding monomer or monomers in microsuspension, without any complementary addition of initiator, with or without an emulsifier, in the presence of a first seeding product in the form of an aqueous dispersion of particles of a vinyl polymer, previously prepared by polymerization in microsuspension, the particles of which contain at least one initiator soluble in organic material and one or more other seeding products in the form of aqueous dispersions of particles of vinyl polymer, the average diameters of which differ from one another and from the particles diameter of the first seeding product, at least one of these seeding products has particles substantially free of initiator and an average diameter less than the average diameter of the particles of the first seeding product; separating the polymer of vinyl chloride from the obtained aqueous dispersion, in which the formed dispersion contains three populations of particles with respective average diameters of from 0.4 to 2.5 μm, from 0.15 to 1 μm and from 0.05 to 0.4 μm, the diameter ratios of large particles/medium particles and medium particles/fine particles similar or different ranging from 1 to 20/1, and in weight ratios of large particles/medium particles and medium particles/fine particles, similar or different, ranging from 0.1 to 20/1.
Claim 7
Dependent Claim
49 words
The method as claimed in claim 1, in which the average diameter of the polymer particles of the first seeding product with initiator is from 0.05 to 1.5 μm, and in which the average diameter of the polymer particles of the seeding product without initiator is from 0.02-1.5 μm.
Claim 8
Dependent Claim
32 words
The method as claimed in claim 1, in which the average diameter of the polymer particles of the seeding product or products other than the first is from 0.02 to 0.8 μm.
Claim 9
Dependent Claim
34 words
The method as claimed in claim 1, in which the seeding product or products other than the first are prepared by polymerization in microsuspension, in the presence of an initiator soluble in organic material.
Claim 10
Dependent Claim
31 words
The method as claimed in claim 1, in which the seeding product or products other than the first are prepared by polymerization in emulsion, in the presence of a water-soluble initiator.
Claim 11
Dependent Claim
53 words
The method as claimed in claim 1, in which the total quantity of seeding products to be used is such that the quantity of polymers contained therein represents 1 to 50% by weight of the sum of vinyl chloride or mixture of vinyl chloride and copolymerizable monomer to be polymerized plus seeding polymers.
Claim 12
Dependent Claim
26 words
The method as claimed in claim 1, in which the ratio of the first seeding polymer to the other seeding polymers is from 95/5 to 5/95.
Claim 13
Dependent Claim
46 words
The method as claimed in claim 1, in which the concentration of seeding polymers plus the vinyl chloride or mixture of vinyl chloride and copolymerizable monomer is from 20 to 80% by weight of the reaction mixture, allowing for the water content of the seeding products.
Claim 14
Independent Claim
321 words
A method of preparing polymers of vinyl chloride, comprising: preparing an aqueous dispersion of polymers of vinyl chloride containing at least two populations of particles with different average diameters of less than 5 μm, with a polymer concentration of up to 75%, by polymerizing the corresponding monomer or monomers in microsuspension, without any complementary addition of initiator, with or without an emulsifier, in the presence of a first seeding product in the form of an aqueous dispersion of particles of a vinyl polymer, previously prepared by polymerization in microsuspension, the particles of which contain at least one initiator soluble in organic material, and one or more other seeding products in the form of aqueous dispersions of particles of vinyl polymer, the average diameters of which differ from one another and from the particles diameter of the first seeding product, at least one of these seeding products has particles substantially free of initiator and an average diameter less than the average diameter of the particles of the first seeding product; separating the polymer of vinyl chloride from the obtained aqueous dispersion, in which an aqueous dispersion of polymers of vinyl chloride containing two populations of particles with respective average diameters from 0.4 to 2.5 μm and from 0.08 to 1 μm, in a diameter ratio from 1 to 20/1 and a weight ratio from 0.1 to 10/1 is prepared by polymerizing the corresponding monomer or monomers in microsuspension in the presence of a first seeding product in the form of an aqueous dispersion of particles of a vinyl polymer with an average diameter of from 0.05 to 1.5 μm, the particles of which contain at least one initiator soluble in organic material and one other seeding product in the form of an aqueous dispersion of particles of a vinyl polymer the average diameter of which differs from the particle diameter of the first seeding product and is from 0.02 to 1.5 μm.
Claim 15
Independent Claim
321 words
A method of preparing polymers of vinyl chloride, comprising: preparing an aqueous dispersion of polymers of vinyl chloride containing at least two populations of particles with different average diameters of less than 5 μm, with a polymer concentration of up to 75%, by polymerizing the corresponding monomer or monomers in microsuspension, without any complementary addition of initiator, with or without an emulsifier, in the presence of a first seeding product in the form of an aqueous dispersion of particles of a vinyl polymer, previously prepared by polymerization in microsuspension, the particles of which contain at least one initiator soluble in organic material, and one or more other seeding products in the form of aqueous dispersions of particles of vinyl polymer, the average diameters of which differ from one another and from the particles diameter of the first seeding product, at least one of these seeding products has particles substantially free of initiator and an average diameter less than the average diameter of the particles of the first seeding product; separating the polymer of vinyl chloride from the obtained aqueous dispersion, in which an aqueous dispersion of polymers of vinyl chloride containing two populations of particles with respective average diameters from 0.4 to 2.5 μm and from 0.08 to 1 μm, in a diameter ratio from 1 to 20/1 and a weight ratio from 0.1 to 10/1 is prepared by polymerizing the corresponding monomer or monomers in microsuspension in the presence of a first seeding product in the form of an aqueous dispersion of particles of a vinyl polymer with an average diameter of from 0.05 to 1.5 μm, the particles of which contain at least one initiator soluble in organic material and one other seeding product in the form of an aqueous dispersion of particles of a vinyl polymer the average diameter of which differs from the particle diameter of the first seeding product and is from 0.02 to 1.5 μm.
Claim 16
Independent Claim
353 words
A method of preparing polymers of vinyl chloride, comprising: preparing an aqueous dispersion of polymers of vinyl chloride containing at least two populations of particles with different average diameters of less than 5 μm, with a polymer concentration of up to 75%, by polymerizing the corresponding monomer or monomers in microsuspension, without any complementary addition of initiator, with or without an emulsifier, in the presence of a first seeding product in the form of an aqueous dispersion of particles of a vinyl polymer, previously prepared by polymerization in microsuspension, the particles of which contain at least one initiator soluble in organic material, and one or more other seeding products in the form of aqueous dispersions of particles of vinyl polymer, the average diameters of which differ from one another and from the particles diameter of the first seeding product, at least one of these seeding products has particles substantially free of initiator and an average diameter less than the average diameter of the particles of the first seeding product; separating the polymer of vinyl chloride from the obtained aqueous dispersion, in which an aqueous dispersion of polymers of vinyl chloride containing three populations of particles with respective average diameters of from 0.4 to 2.5 μm, from 0.15 to 1 μm and from 0.05 to 0.4 μm, the diameter ratios of large particles/medium particles and medium particles/fine particles similar or different, ranging from 0.1 to 20/1, and in weight ratios of large particles/medium particles and medium particles/fine particles, similar or different, ranging from 0.1 to 20/1 is prepared by polymerizing the corresponding monomer or monomers in microsuspension in the presence of a first seeding product in the form of an aqueous dispersion of particles of a vinyl polymer with an average diameter of from 0.05 to 1.5 μm, the particles of which contain at least one inititator soluble in organic material and two other seeding products in the form of aqueous dispersions of particles of a vinyl polymer the average diameters of which differ from one another and from the particles diameter of the first seeding product and are from 0.02 to 1.5 μm.
Claim 17
Independent Claim
353 words
A method of preparing polymers of vinyl chloride, comprising: preparing an aqueous dispersion of polymers of vinyl chloride containing at least two populations of particles with different average diameters of less than 5 μm, with a polymer concentration of up to 75%, by polymerizing the corresponding monomer or monomers in microsuspension, without any complementary addition of initiator, with or without an emulsifier, in the presence of a first seeding product in the form of an aqueous dispersion of particles of a vinyl polymer, previously prepared by polymerization in microsuspension, the particles of which contain at least one initiator soluble in organic material, and one or more other seeding products in the form of aqueous dispersions of particles of vinyl polymer, the average diameters of which differ from one another and from the particles diameter of the first seeding product, at least one of these seeding products has particles substantially free of initiator and an average diameter less than the average diameter of the particles of the first seeding product; separating the polymer of vinyl chloride from the obtained aqueous dispersion, in which an aqueous dispersion of polymers of vinyl chloride containing three populations of particles with respective average diameters of from 0.4 to 2.5 μm, from 0.15 to 1 μm and from 0.05 to 0.4 μm, the diameter ratios of large particles/medium particles and medium particles/fine particles similar or different, ranging from 0.1 to 20/1, and in weight ratios of large particles/medium particles and medium particles/fine particles, similar or different, ranging from 0.1 to 20/1 is prepared by polymerizing the corresponding monomer or monomers in microsuspension in the presence of a first seeding product in the form of an aqueous dispersion of particles of a vinyl polymer with an average diameter of from 0.05 to 1.5 μm, the particles of which contain at least one inititator soluble in organic material and two other seeding products in the form of aqueous dispersions of particles of a vinyl polymer the average diameters of which differ from one another and from the particles diameter of the first seeding product and are from 0.02 to 1.5 μm.
Claim 18
Dependent Claim
39 words
The method as claimed in claim 1, in which the polymerization speed is accelerated by activation of the initiator contained in the particles of seeding products, by a metal complex, formed in situ, which is soluble in organic material.
Claim 19
Dependent Claim
20 words
The method as claimed in claim 1 characterized in that their polymer concentration is from 20 to 75% by weight.
Claim 20
Dependent Claim
45 words
The method as claimed in claim 1 in which the two populations of particles have respective average diameters from 0.4 to 2.5 μm and from 0.08 to 1 μm, in a diameter ratio from 1 to 20/1 and a weight ratio from 0.1 to 10/1.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-01-13 | 1984-07-14 | 1985-01-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-01-13 | 1988-07-14 | 1989-01-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-01-13 | 1992-07-14 | 1993-01-13 | $7700.00 | Window Closed / Lapsed |