Exhaust electrode process for exhaust gas oxygen sensor
Assignee: Motors Liquidation Co
•
Filing: 1979-10-29
•
Granted: 1981-01-13
•
Expires: 1999-10-29
Abstract
Abstract A method of sputtering a platinum exhaust gas electrode onto a vitrified zirconia thimble for an electrochemical-type exhaust gas oxygen sensor. Porous high surface area platinum films are deposited that have more consistent properties. A platinum target is spaced about 3.0-4.5 cm from the thimble and more than 6 cm from the sputtering anode. A pressure of about 10-20 millitorr is used during sputtering at a DC power of about 13-22 watts/cm 2 of target area.
Inventors
- 👤 Terry J. Gold
- 👤 Frederick L. Kennard, III
- 👤 Paul C. Kikuchi
- 👤 Ralph V. Wilhelm, Jr.
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 22:50
CPC Classifications
G; G01; G01N; G01N27/00; G01N27/26; G01N27/403; G01N27/406; G01N27/407; G01N27/4075; C; C03; C03C; C03C17/00; C03C17/06; C03C17/09; C23; C23C; C23C14/00; C23C14/06; C23C14/14; C23C14/18; C23C14/185; H; H01; H01M; H01M4/00; H01M4/86; H01M4/90; H01M4/9041; H01M4/905; H01M4/9058; Y; Y02; Y02E; Y02E60/00; Y02E60/30; Y02E60/50
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
96 words
In a method of sputtering a platinum exhaust gas electrode onto a vitrified zirconia solid electrolyte body for an electrochemical-type exhaust gas oxygen sensor, the improvement wherein a platinum target spaced at least 3.0 cm from the body is used in the sputtering, the platinum is sputtered at a pressure of about 10-20 millitorr, and a sputtering power of about 13-22 watts/cm 2 of target area is used, whereby the platinum electrode is porous as deposited and has an apparent surface area at least double the geometric area of the zirconia surface on which it lies.
Claim 2
Dependent Claim
96 words
In a method of sputtering a platinum exhaust gas electrode onto a vitrified zirconia solid electrolyte body for an electrochemical-type exhaust gas oxygen sensor, the improvement wherein a platinum target spaced at least 3.0 cm from the body is used in the sputtering, the platinum is sputtered at a pressure of about 10-20 millitorr, and a sputtering power of about 13-22 watts/cm 2 of target area is used, whereby the platinum electrode is porous as deposited and has an apparent surface area at least double the geometric area of the zirconia surface on which it lies.
Claim 3
Dependent Claim
105 words
In a method of sputtering a platinum exhuast gas electrode onto a vitrified zirconia thimble for an electrochemical-type exhaust gas oxygen sensor, the improvement wherein a generally planar platinum target is oriented normal to the axis of the zirconia thimble and spaced about 3.0-4.5 cm from a closed end on the thimble, the platinum is sputtered using an atmosphere having a pressure of approximately 10-20 millitorr and a DC power of about 13-22 watts/cm 2 of target area, whereby the platinum electrode is consistently and reproducibly porous as deposited and has an apparent surface area as deposited at least four times its geometric surface area.
Claim 4
Dependent Claim
105 words
In a method of sputtering a platinum exhuast gas electrode onto a vitrified zirconia thimble for an electrochemical-type exhaust gas oxygen sensor, the improvement wherein a generally planar platinum target is oriented normal to the axis of the zirconia thimble and spaced about 3.0-4.5 cm from a closed end on the thimble, the platinum is sputtered using an atmosphere having a pressure of approximately 10-20 millitorr and a DC power of about 13-22 watts/cm 2 of target area, whereby the platinum electrode is consistently and reproducibly porous as deposited and has an apparent surface area as deposited at least four times its geometric surface area.
Claim 5
Dependent Claim
131 words
In a method of sputtering a platinum exhaust gas electrode onto a vitrified zirconia thimble for an electrochemical-type exhaust gas oxygen sensor, the improvement wherein the thimble is about 3-5 cm long, a generally planar platinum target is oriented normal to the thimble and spaced about 3.5-4.0 cm from a closed end on the thimble, the platinum is DC magnetron sputtered using an atmosphere having a pressure of approximately 10-20 millitorr and a DC power of about 13-22 watts/cm 2 of target area and for a duration to produce an electrode thickness of more than about 0.65 micrometer on said end and about 0.3-0.5 micrometer on thimble side walls, whereby the platinum electrode is deposited and has an apparent surface area as deposited at least four times its geometric surface area.
Claim 6
Dependent Claim
131 words
In a method of sputtering a platinum exhaust gas electrode onto a vitrified zirconia thimble for an electrochemical-type exhaust gas oxygen sensor, the improvement wherein the thimble is about 3-5 cm long, a generally planar platinum target is oriented normal to the thimble and spaced about 3.5-4.0 cm from a closed end on the thimble, the platinum is DC magnetron sputtered using an atmosphere having a pressure of approximately 10-20 millitorr and a DC power of about 13-22 watts/cm 2 of target area and for a duration to produce an electrode thickness of more than about 0.65 micrometer on said end and about 0.3-0.5 micrometer on thimble side walls, whereby the platinum electrode is deposited and has an apparent surface area as deposited at least four times its geometric surface area.
References Cited (Backward Citations)
US3978006A
Cited
US4021326A
Cited
US3844920A
Cited
US4116883A
Cited
US4129848A
Cited
US4136000A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-01-13 | 1984-07-14 | 1985-01-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-01-13 | 1988-07-14 | 1989-01-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-01-13 | 1992-07-14 | 1993-01-13 | $7700.00 | Window Closed / Lapsed |