Method for manufacturing a resin-reinforced carbon fiber product
Assignee: Individual
•
Filing: 1978-06-27
•
Granted: 1981-01-13
•
Expires: 1998-06-27
Abstract
Abstract A method for manufacturing a resin-reinforced carbon fiber bar product in which thermal setting resin-impregnated carbon fibers are heated to a temperature sufficient to set the resin to semi-solid state, the heated carbon fibers are passed through resilient constriction means to form a bar-like intermediate product, the bar-like intermediate product is cooled, a tape of water-containing cellophane is wound about the intermediate bar-like product in a spiral manner to compress the carbon fibers together, the intermediate bar-like product is pulled in the longitudinal direction while being heated, the thus treated intermediate bar-like product is cooled and the cellophane tape is removed from the intermediate bar-like product to thereby form a complete resin-reinforced bar product.
Inventors
- 👤 Tomotoshi Tokuno
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 17:57
CPC Classifications
B; B29; B29C; B29C70/00; B29C70/04; B29C70/06; B29C70/10; B29C70/16; B29C70/20; B29C70/28; B29C70/40; B29C70/50; B29C70/52; B29K; B29K2307/00
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
138 words
A method for manufacturing a resin-reinforced carbon fabric bar product which comprises the steps of heating a thermal setting resin-impregnated carbon fabric bundle to a temperature sufficient to set said thermal setting resin to a semi-solid state, drawing said carbon fabric bundle through resilient constriction means to compress the carbon fibers in said carbon fabric bundle together to form an intermediate bar product, cooling said intermediate bar product to room temperature, winding a tape of water-containing cellophane about said intermediate bar product in a spiral manner to further tighten said carbon fibers in the carbon fiber bundle together, tensioning said carbon fiber bundle in the longitudinal direction of the bundle while heating the carbon fiber bundle until the resin impregnated in the carbon fabric bundle is completely set and removing said cellophane tape from said carbon fabric bundle.
Claim 2
Independent Claim
138 words
A method for manufacturing a resin-reinforced carbon fabric bar product which comprises the steps of heating a thermal setting resin-impregnated carbon fabric bundle to a temperature sufficient to set said thermal setting resin to a semi-solid state, drawing said carbon fabric bundle through resilient constriction means to compress the carbon fibers in said carbon fabric bundle together to form an intermediate bar product, cooling said intermediate bar product to room temperature, winding a tape of water-containing cellophane about said intermediate bar product in a spiral manner to further tighten said carbon fibers in the carbon fiber bundle together, tensioning said carbon fiber bundle in the longitudinal direction of the bundle while heating the carbon fiber bundle until the resin impregnated in the carbon fabric bundle is completely set and removing said cellophane tape from said carbon fabric bundle.
Claim 3
Dependent Claim
31 words
The method as set forth in claim 1, in which said heating of the thermo-setting resin to a semi-solid state is carried out at a temperature within the range 40°-200° C.
Claim 4
Dependent Claim
16 words
The method as set forth in claim 1, in which said thermo-setting resin is epoxy resin.
Claim 5
Dependent Claim
16 words
The method as set forth in claim 1, in which said thermo-setting resin is polyester resin.
Claim 6
Dependent Claim
48 words
The method as set forth in claim 1, in which said resilient constriction means comprises a pair of upper and lower silicone rubber sheets disposed in parallel and horizontal orientation and having aligned holes the diameter of which is smaller than the diameter of said intermediate bar product.
Claim 7
Dependent Claim
23 words
The method as set forth in claim 1, in which said cooling of the intermediate bar product is carried out to room temperature.
Claim 8
Dependent Claim
19 words
The method as set forth in claim 1, in which said room temperature is within the range 15°-35° C.
Claim 9
Dependent Claim
33 words
The method as set forth in claim 1, in which said final heating of the resin impregnated in the intermediate carbon fabric product is performed at a temperature within the range 120°-180° C.
Claim 10
Dependent Claim
57 words
The method as set forth in claim 1, in which said heating of the carbon fiber bundle to set the resin impregnated in the carbon fibers of the carbon fiber bundle to a semi-solid state is carried out while the carbon fiber bundle is moving at a rate within the range 2 to 10 cm per second.
Claim 11
Dependent Claim
49 words
The method as set forth in claim 1, in which said stretching of the carbon fiber bundle is carried out by attachning holders to the opposite ends of the carbon fiber bundle, securing one of said holders to a support means and attaching a weight to the other holder.
Claim 12
Dependent Claim
40 words
The method as set forth in claim 1, in which said stretching of the carbon fiber bundle is carried out by attaching holders to the opposite ends of the carbon fiber bundle and pulling said holders away from each other.
References Cited (Backward Citations)
US2596162A
Cited
US2526945A
Cited
US2721820A
Cited
US2625498A
Cited
US3608052A
Cited
JPS4833270A
Cited
US3881977A
Cited
JPS5030965A
Cited
US4003773A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-01-13 | 1984-07-14 | 1985-01-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-01-13 | 1988-07-14 | 1989-01-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-01-13 | 1992-07-14 | 1993-01-13 | $7700.00 | Window Closed / Lapsed |