Sulfur containing refractory for resisting reactive molten metals
Assignee: RTX Corp
•
Filing: 1979-04-23
•
Granted: 1981-01-13
•
Expires: 1999-04-23
Abstract
Abstract Improved refractories for resisting attack of molten titanium aluminum and similar metals are provided by the inclusion of sulfur. Metal, oxygen, and sulfur combinations, wherein sulfur is present at from 10 to 60 atomic percent, are particularly useful. Disclosed is a material having the atomic formula M a S b O c where O is oxygen, S is sulfur, and M is at least one metal selected from the scandium subgroup of the periodic table transition metals (scandium, yttrium and the rare earths) and aluminum. In an alternate material, M is comprised of at least two elements, the first selected as above and the second selected from the alkaline earth metal group. A preferred material is formed by mixing and firing CaS and Y 2 O 3 in proportions which results in (Ca+Y) 0 .43 S 0 .14 O 0 .43.
Inventors
- 👤 Martin J. Blackburn
- 👤 Steven Z. Hayden
- 👤 Michael P. Smith
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 14:56
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/515; C04B35/547; B; B22; B22C; B22C9/00; C04B35/50; C04B35/505; C04B35/51
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
75 words
A sintered material for resisting the attack of reactive molten metals having the atomic formula: M.sub.a S.sub.b O.sub.c where O is oxygen and S is sulfur and where M is one element selected from the scandium sub-group of periodic table transition metals (scandium, yttrium and the rare earths) and aluminum or mixtures thereof and where a ranges from about 0.4 to 0.45, b from about 0.1 to 0.6, and c from about 0.2 to 0.6.
Claim 2
Dependent Claim
75 words
A sintered material for resisting the attack of reactive molten metals having the atomic formula: M.sub.a S.sub.b O.sub.c where O is oxygen and S is sulfur and where M is one element selected from the scandium sub-group of periodic table transition metals (scandium, yttrium and the rare earths) and aluminum or mixtures thereof and where a ranges from about 0.4 to 0.45, b from about 0.1 to 0.6, and c from about 0.2 to 0.6.
Claim 3
Dependent Claim
22 words
The material of claim 1 where a ranges from 0.41 to 0.45, b from 0.02 to 0.24, c from 0.31 to 0.57.
Claim 4
Dependent Claim
97 words
A sintered material for resisting the attack of molten reactive metal having the formula: M.sub.a S.sub.b O.sub.c where M consists of two elements, M' and M", and wherein M' is a metal selected from the scandium sub-group of transition metals (scandium, yttrium, and the rare earth lanthanides actinides) and aluminum or mixtures thereof and M" is a metal selected from the alkaline earth metal group (beryllium, magnesium, strontium, barium and radium) mixtures thereof and wherein a ranges from about 0.41 to 0.45, b ranges from about 0.02 to 0.24 and c ranges from about 0.34 to 0.57.
Claim 5
Dependent Claim
97 words
A sintered material for resisting the attack of molten reactive metal having the formula: M.sub.a S.sub.b O.sub.c where M consists of two elements, M' and M", and wherein M' is a metal selected from the scandium sub-group of transition metals (scandium, yttrium, and the rare earth lanthanides actinides) and aluminum or mixtures thereof and M" is a metal selected from the alkaline earth metal group (beryllium, magnesium, strontium, barium and radium) mixtures thereof and wherein a ranges from about 0.41 to 0.45, b ranges from about 0.02 to 0.24 and c ranges from about 0.34 to 0.57.
Claim 6
Dependent Claim
9 words
The material of claim 3 wherein M' is yttrium.
Claim 7
Dependent Claim
9 words
The material of claim 4 wherein M" is calcium.
Claim 8
Dependent Claim
21 words
The materials of claims 1 or 3 wherein a is about 0.43, b is about 0.14 and c is about 0.43.
Claim 9
Dependent Claim
58 words
A material for resisting the attack of reactive molten metal consisting of a mixture of an oxide of a metal selected from the group consisting of the scandium sub-group and aluminum or mixtures thereof, and a sulfide of a metal selected from the alkaline earth group, wherein the sulfide comprises 10 to 70 molar percent of the mixture.
Claim 10
Dependent Claim
58 words
A material for resisting the attack of reactive molten metal consisting of a mixture of an oxide of a metal selected from the group consisting of the scandium sub-group and aluminum or mixtures thereof, and a sulfide of a metal selected from the alkaline earth group, wherein the sulfide comprises 10 to 70 molar percent of the mixture.
Claim 11
Dependent Claim
49 words
A material for resisting the attack of titanium aluminum and like reactive alloys comprising a fine particulate intermixture of yttria and calcium sulfide, wherein calcium sulfide comprises 10 to 70 molar percent of the mixture and wherein the mixture is fired at 1250° C. or higher prior to use.
Claim 12
Dependent Claim
49 words
A material for resisting the attack of titanium aluminum and like reactive alloys comprising a fine particulate intermixture of yttria and calcium sulfide, wherein calcium sulfide comprises 10 to 70 molar percent of the mixture and wherein the mixture is fired at 1250° C. or higher prior to use.
Claim 13
Independent Claim
24 words
The method of improving the resistance of metal oxide refractories to reactive molten metals which comprises incorporating from 10 to 60 atomic percent sulfur.
Claim 14
Independent Claim
24 words
The method of improving the resistance of metal oxide refractories to reactive molten metals which comprises incorporating from 10 to 60 atomic percent sulfur.
Claim 15
Independent Claim
38 words
The method of improving the resistance to molten metal attack of yttrium and aluminum oxide base materials which comprises adding a metal sulfur compound in a quantity which produces up to 60 atomic percent sulfur in the material.
Claim 16
Independent Claim
38 words
The method of improving the resistance to molten metal attack of yttrium and aluminum oxide base materials which comprises adding a metal sulfur compound in a quantity which produces up to 60 atomic percent sulfur in the material.
Claim 17
Independent Claim
66 words
The method of improving the resistance to interaction of a vessel for receiving molten reactive metal which comprises providing molten metal contacting surfaces having a composition containing a metal chosen from the group consisting of the scandium sub-group and aluminum or mixtures thereof, in an amount ranging from about 40 to 45 atomic percent, and sulfur in an amount ranging from 10 to 60 atomic percent.
Claim 18
Independent Claim
66 words
The method of improving the resistance to interaction of a vessel for receiving molten reactive metal which comprises providing molten metal contacting surfaces having a composition containing a metal chosen from the group consisting of the scandium sub-group and aluminum or mixtures thereof, in an amount ranging from about 40 to 45 atomic percent, and sulfur in an amount ranging from 10 to 60 atomic percent.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-01-13 | 1984-07-14 | 1985-01-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-01-13 | 1988-07-14 | 1989-01-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-01-13 | 1992-07-14 | 1993-01-13 | $7700.00 | Window Closed / Lapsed |