Abstract
Abstract A slurry comprised of particulated glass-forming substances, with or without particulated relatively clear or light-colored metal oxides, dispersed in a photolacquer is applied as a uniform layer on a surface of a color image screen. Such layer is then developed via conventional photoforming techniques to produce sites or windows for phosphor dots and the resultant window-containing layer is heated, prior or subsequent to application of phosphor dots in such windows, at a temperature in the range of about 350° to 500° C. In instances where metal oxide particles are present in the slurry, the resultant layer becomes opaque or dark upon tempering and in cases where only pure glass-forming substance particles are in the slurry, the resultant layer becomes opaque or dark upon tempering in a reducing atmosphere. Electrical conductivity may be imparted to the light-absorbing coating by addition of selective conductive materials to the initial slurry.
Inventors
- 👤 Manfred Kobale
- 👤 Hans-Peter Lorenz
- 👤 Rolf Wengert
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 20:19
CPC Classifications
H; H01; H01J; H01J29/00; H01J29/02; H01J29/10; H01J29/18; H01J29/30; H01J29/32; H01J29/327; H01J9/00; H01J9/20; H01J9/22; H01J9/227; H01J9/2278
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
115 words
A method of producing light-absorbing edging of select conductivity on colour image screens, comprising the steps of: (a) applying a substantially uniform photo-formable coating onto an entire surface area of a glass screen substrate, said coating being formed from a slurry composed of glass-forming substances dispersed in a photolacquer; (b) developing the so-applied photo-formable coating via photoform techniques to that windows are formed in such coating at areas thereof corresponding to desired locations of color phosphors to be later applied; and (c) tempering the so-developed coating in a reducing atmosphere at a temperature in the range of 350° to 500° C. so as to attain a light-absorbing edging having windows therein for receiving color phosphors.
Claim 2
Independent Claim
115 words
A method of producing light-absorbing edging of select conductivity on colour image screens, comprising the steps of: (a) applying a substantially uniform photo-formable coating onto an entire surface area of a glass screen substrate, said coating being formed from a slurry composed of glass-forming substances dispersed in a photolacquer; (b) developing the so-applied photo-formable coating via photoform techniques to that windows are formed in such coating at areas thereof corresponding to desired locations of color phosphors to be later applied; and (c) tempering the so-developed coating in a reducing atmosphere at a temperature in the range of 350° to 500° C. so as to attain a light-absorbing edging having windows therein for receiving color phosphors.
Claim 3
Independent Claim
120 words
A method of producing light-absorbing edging of select conductivity on colour image screens, comprising the steps of: (a) applying a substantially uniform photo-formable coating onto an entire surface area of a glass screen substrate, said coating being formed of a slurry composed of glass-forming substances and metal oxides having a relatively low light-absorption characteristic dispersed in a photolacquer; (b) developing the so-applied coating via photoform techniques so that windows are formed in such coating at areas thereof corresponding to desired locations of color phosphors to be later applied; and (c) tempering the so-developed coating at a temperature in the range of about 350° to 500° C. so as to attain a light-absorbing edging having windows therein for receiving color phosphors.
Claim 4
Independent Claim
120 words
A method of producing light-absorbing edging of select conductivity on colour image screens, comprising the steps of: (a) applying a substantially uniform photo-formable coating onto an entire surface area of a glass screen substrate, said coating being formed of a slurry composed of glass-forming substances and metal oxides having a relatively low light-absorption characteristic dispersed in a photolacquer; (b) developing the so-applied coating via photoform techniques so that windows are formed in such coating at areas thereof corresponding to desired locations of color phosphors to be later applied; and (c) tempering the so-developed coating at a temperature in the range of about 350° to 500° C. so as to attain a light-absorbing edging having windows therein for receiving color phosphors.
Claim 5
Dependent Claim
28 words
A method as defined in claim 2, wherein said slurry contains a material selected from the group consisting of metal oxides, metal resinates, silicon esters and mixtures thereof.
Claim 6
Dependent Claim
27 words
A method as defined in claim 3, wherein said metal oxides are selected from the group consisting of chromium oxide, cobalt oxide, nickel oxide and mixtures thereof.
Claim 7
Dependent Claim
16 words
A method as defined in claim 2, wherein said slurry contains organo-metallic compounds and silicon esters.
Claim 8
Dependent Claim
32 words
A method as defined in claim 5, wherein said organo-metallic compounds are selected from a group consisting of sulfur resinates, mercaptanes and carboxylates of Ni, Co, Pb, Pt, Au and mixtures thereof.
Claim 9
Dependent Claim
29 words
A method as defined in claim 2, wherein said glass-forming substances are selected from the group consisting of lead oxide, silicon oxide, boron oxide, aluminum oxide and mixtures thereof.
Claim 10
Dependent Claim
55 words
A method as defined in claim 7, wherein said glass-forming substances are produced by melting such substances into a substantially uniform melt mass, cooling the resultant melt mass to obtain a solid mass and grinding such solid mass until a plurality of particles having an average maximum grain diameter of about 30 μm are attained.
Claim 11
Dependent Claim
58 words
A method as defined in claim 1, wherein a mask is used in step (b) in carrying out the photoform technique, said mask containing a raster identical to the base mask raster containing all raster points of colors on said image screen, said base mask being subsequently used to apply color phosphors onto the treated glass screen substrate.
Claim 12
Dependent Claim
33 words
A method as defined in claim 9 wherein step (a) occurs via spraying said slurry which contains powdered glass-forming substances until said coating attains a layer thickness of about 15 to 30 μm.
Claim 13
Dependent Claim
32 words
A method as defined in claim 9 wherein step (a) occurs via spraying said slurry which contains organo-metallic compounds until said coating attains a layer thickness of about 0.5 to 2 μm.
Claim 14
Dependent Claim
58 words
A method as defined in claim 1, wherein the light-absorbing edging and free glass surface areas between adjacent areas of said edging are provided with a conductive transparent layer comprised of a material selected from the group consisting of doped indium oxide and doped tin oxide prior to application of color phosphors onto the so-treated glass screen substrate.
Claim 15
Dependent Claim
23 words
A method as defined in claim 12, wherein the dopant in said material is selected from the group consisting of antimony and indium.
Claim 16
Dependent Claim
22 words
A method as defined in claim 12, wherein said conductive transparent layer has a maximum layer thickness of about 1 μm .
References Cited (Backward Citations)
DE2127845A1
Cited
US3654505A
Cited
US3858083A
Cited
US4019905A
Cited
DE2526882C3
Cited
US4020191A
Cited
DE2540132C3
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-01-06 | 1984-07-07 | 1985-01-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-01-06 | 1988-07-07 | 1989-01-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-01-06 | 1992-07-07 | 1993-01-06 | $7700.00 | Window Closed / Lapsed |