Assignee: Nihon Kogyo KK
•
Filing: 1978-11-28
•
Granted: 1981-01-06
•
Expires: 1998-11-28
Abstract
Abstract A double-metal-coated metal sulfide powder comprises particles of a metal sulfide, a layer of a platinum group metal coating formed thereon, and an outer coating layer of a metal or alloy which contains at least one of iron, copper, nickel, and cobalt. The powder is obtained by forming a platinum group metal layer on metal sulfide particles by thermal decomposition of a plating composition which includes at least one platinum-metal compound containing a radical selected from the class consisting of NO, NO2, NO3, and NOCl and then forming a layer of at least one metal selected from the group consisting of iron, copper, nickel, and cobalt by the cementation reaction.
Inventors
- 👤 Haruki Sato
- 👤 Yoshio Kawasumi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 23:26
CPC Classifications
F; F16; F16C; F16C33/00; F16C33/02; F16C33/04; F16C33/06; F16C33/10; F16C33/1095; B; B22; B22F; B22F1/00; B22F1/14; B22F1/145; B22F1/18; Y; Y10; Y10T; Y10T428/00; Y10T428/12; Y10T428/12181; Y10T428/29; Y10T428/2982; Y10T428/2991
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
157 words
A process of producing a double-metal-coated metal sulfide powder, which comprises the steps of forming a platinum group metal layer on metal sulfide particles by thermal decomposition of a plating composition which includes at least one platinum group metal compound containing a radical selected from the class consisting of NO, NO 2 , NO 3 , and NOCl; and forming an outer layer of at least one metal or alloy selected from the group consisting of iron, copper, nickel and cobalt or an alloy thereof on said metal sulfide particles coated with the platinum group metal layer by adding and mixing the powder of a metal or alloy, less noble than said selected metal or alloy and further adding an acidic solution containing the ions of said selected metal(s) to the mixture obtained in the preceding step while stirring to thereby coat said platinum group metal layer with said selected metal(s) that results from a cementation reaction.
Claim 2
Dependent Claim
157 words
A process of producing a double-metal-coated metal sulfide powder, which comprises the steps of forming a platinum group metal layer on metal sulfide particles by thermal decomposition of a plating composition which includes at least one platinum group metal compound containing a radical selected from the class consisting of NO, NO 2 , NO 3 , and NOCl; and forming an outer layer of at least one metal or alloy selected from the group consisting of iron, copper, nickel and cobalt or an alloy thereof on said metal sulfide particles coated with the platinum group metal layer by adding and mixing the powder of a metal or alloy, less noble than said selected metal or alloy and further adding an acidic solution containing the ions of said selected metal(s) to the mixture obtained in the preceding step while stirring to thereby coat said platinum group metal layer with said selected metal(s) that results from a cementation reaction.
Claim 3
Dependent Claim
23 words
A process according to claim 1 wherein the metal sulfide powder is selected from a group of molybdenum disulfide and tungsten disulfide powders.
Claim 4
Dependent Claim
22 words
A process according to claim 1 wherein the metal sulfide powder has a particle size between about -100 mesh and +400 mesh.
Claim 5
Dependent Claim
34 words
A process according to claim 1 wherein when the starting metal sulfide powder is too fine or coarse and contains a large proportion of flat particles, it is subjected to preliminary granulation and/or sizing.
Claim 6
Dependent Claim
34 words
A process according to claim 4 wherein the metal sulfide powder is ground and granulated by a grinding-granulating mixer using a binder prepared by diluting a resol and/or novolak type phenol resin with alcohol.
Claim 7
Dependent Claim
93 words
A process according to claim 1 wherein said compound of platinum group metals is at least one selected from the group consisting of Ru(NO)(OH) 3 , OsO(NO)OH, Pt(NH 3 ) 2 (NO 2 ) 2 , (NH 4 ) 3 Rh(NO 2 ) 6 , Rh(NO 3 ) 2 .2H 2 O, (NH 4 ) 3 Ir(NO 2 ) 6 , Pd(NH 3 ) 2 (NO 2 ) 2 , Pd(NO 3 ) 2 , Pd(NH 3 ) 4 (NO 3 ) 4 (NO 3 ) 2 , Pd(NO 3 ) 2 .
Claim 8
Dependent Claim
58 words
A process according to claim 6 wherein in case palladium plating is effected, either of Pd(NH 3 ) 2 (NO 2 ) 2 , Pd(NH 3 ) 4 (NO 3 ) 2 or Pd(NO 3 ) 2 is employed in an amount of not less than 0.001 g/l and not more than 35 g/l in terms of palladium.
Claim 9
Dependent Claim
82 words
A process according to claim 6 wherein in case ruthenium, osmium, platinum, rhodium or iridium plating is effected, corresponding one of Ru(NO)(OH) 3 , OsO(NO)OH, Pt(NH 3 ) 2 (NO 2 ) 2 , (NH 4 ) 3 Rh(NO 2 ) 6 or Rh(NO 3 ) 2 .2H 2 O, or (NH 4 ) 3 Ir(NO 2 ) 6 is employed in an amount of not less than 0.01 g/l and not more than 28 g/l in terms of a platinum metal.
Claim 10
Dependent Claim
25 words
A process according to claim 1 wherein the plating composition further contains NH 4 OH, NH 4 NO 3 or NH 4 NO 2 .
Claim 11
Dependent Claim
19 words
A process according to claim 1 wherein the thermal decomposition is carried out at about 250° to 400° C.
Claim 12
Dependent Claim
30 words
A process according to claim 1 wherein the metal and/or alloy powder added is selected from a group of powders of zinc, iron, aluminum, magnesium, calcium or an alloy thereof.
Claim 13
Dependent Claim
23 words
A process according to claim 1 wherein the metal and/or alloy powder added has a particle size range from -100 to +400 mesh.
Claim 14
Dependent Claim
37 words
A process according to claim 1 wherein the metal and/or alloy powcer added is in a amount slightly more than the stoichiometric equivalent of the intended amount of the metal or alloy formed as the outer layer.
Claim 15
Dependent Claim
26 words
A process according to claim 1 wherein the source of the selected metal(s) is selected from the salts of sulfuric, hydrochloric, nitric, and organic acids thereof.
Claim 16
Dependent Claim
29 words
A process according to claim 1 wherein the acid to be employed is selected from a group of sulfuric acid, hydrochloric acid, nitric acid, acetic acid and oxalic acid.
Claim 17
Dependent Claim
42 words
A process according to claim 1 wherein the addition of the acidic solution is so effected that the funicular [II] region is reached in about 20 seconds to 10 minutes and then the slurry region is reached in 5 to 10 seconds.
Claim 18
Dependent Claim
13 words
A double-metal-coated metal sulfide powder made according to the process of claim 1.
References Cited (Backward Citations)
GB1517609A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-01-06 | 1984-07-07 | 1985-01-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-01-06 | 1988-07-07 | 1989-01-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-01-06 | 1992-07-07 | 1993-01-06 | $7700.00 | Window Closed / Lapsed |