Preparation of latex from solvent dispersed polymer composition

Claim 2

In the formation of the latex from a solvent dispersed polymer composition, by a process which comprises (1) providing a dispersion of the polymer composition in essentially water-immiscible volatile solvent which itself or as an azeotrope with water has a boiling point lower than that of water at atmospheric pressure, (2) adding water and emulsifier to said dispersion in proportions to form an emulsion having water as its continuum and emulsifying the same so that the discontinuous phase thereof is in particles of precursor latex size, (3) stripping the solvent from the emulsion to form an essentially solvent free latex, and (4) recovering the latex product, the improvement which consists in the combination in the process of the further steps of (5) providing a moving flow of gas comprising steam as an initial continuous phase, (6) dispersing the emulsion formed in step (2) into said flow of gas as the initial continuous phase while subjecting the phases to a decrease of pressure and maintaining the temperature thereof below the limiting temperature for stability of the emulsion, thereby vaporizing solvent from the dispersed droplets and forming essentially solvent free droplets of latex and vapor, (7) establishing a separating zone maintained at a pressure below the decreased pressure attained in step (6), (8) establishing a flow of latex of the selected high polymer other than the flow of steps (5) and (6) through said separating zone, (9) introducing into said separating zone the droplets of latex and vapor produced by step (6) and impinging said droplets upon the flow of latex therein, (10) withdrawing vapor from said separating zone, (11) withdrawing the combined latex from said separating zone, and (12) during step (6) and prior to the practice of step (9), (a) essentially avoiding impacting of the dispersed droplets on solid surfaces at high velocities capable of effecting agglomeration of polymer of the droplets, and (b) maintaining on the flowing dispersion, until the solvent vaporization from the dispersed droplets is essentially complete, a pressure gradient which is not so large as to destabilize the latex being formed.

Claim 3

A process as claimed in claim 1, futher comprising the steps of (13) delivering a part of the combined latex withdrawn in step (11) to a concentrating zone, (14) subjecting the combined latex in said concentrating zone to heating and reduction of pressure while maintaining the latex at temperatures within the limiting range for stability of the latex, thus to produce concentrated latex and vapor therefrom, and (15) introducing said concentrated latex and vapor into said separating zone to form the flow of latex therein.

Claim 4

A process as claimed in claim 2, in which step (14) is practiced by (16) heating the latex while maintaining it under a sufficient pressure to prevent boiling thereof, and (17) then subjecting the heated latex, essentially without further heating thereof, to a progressive reduction of pressure to cause concentration of the latex and generation of vapor therefrom by said pressure reduction while essentially preventing foaming thereof.

Claim 5

A process as claimed in claim 3, in which step (17) is conducted under conditions of turbulent flow sufficient to essentially prevent foaming.

Claim 6

A process as claimed in claim 3, in which during step (17) the latex and vapor generated therefrom are kept moving at a suffieient velocity to essentially prevent foaming.

Claim 7

A process as claimed in claim 3, in which in step (17) additional latex is impinged on the latex from which vapor is being generated for essentially preventing foaming thereof.

Claim 8

A process as claimed in claim 3, in which the heating in step (16) is conducted under conditions of turbulent flow.

Claim 9

A process as claimed in claim 2, further comprising the steps of: (16) establishing a second separating zone separate from said first separating zone, (17) delivering another part of the combined latex withdrawn in step (11) to a second concentrating zone, (18) subjecting the latex in said second concentrating zone to heating and reduction of pressure while maintaining the latex at temperatures within the limiting range for stability of the latex, thus to produce a further concentrated latex and vapor therefrom, (19) introducing said further concentrated latex and vapor into said second separating zone, and (20) withdrawing the further concentrated latex from said second separating zone.

Claim 10

A process as claimed in claim 8, in which at least one of steps (14) and (18) is practiced by (21) heating the latex while maintaining it under a sufficient pressure to prevent boiling thereof, and (22) then subjecting the heated latex, essentially without further heating thereof, to a progressive reduction of pressure to cause concentration of the latex and generation of vapor therefrom by said pressure reduction while essentially preventing foaming thereof.

Claim 11

A process as claimed in claim 9, in which step (22) is conducted under conditions of turbulent flow sufficient to essentially prevent foaming.

Claim 12

A process as claimed in claim 9, in which during step (22) the latex and vapor generated therefrom are kept moving at a sufficient velocity to essentially prevent foaming.

Claim 13

A process as claimed in claim 9, in which in step (22) additional latex is impinged on the latex from which vapor is being generated for essentially preventing foaming thereof.

Claim 14

A process as claimed in claim 9, in which the heating in step (21) is conducted under conditions of turbulent flow.

Claim 15

A process as claimed in claim 8, in which both of steps (14) and (18) are practiced by (21) heating the latex while maintaining it under a sufficient pressure to prevent boiling thereof, and (22) then subjecting the heated latex, essentially without further heating thereof, to a progressive reduction of pressure to cause concentration of the latex and generation of vapor therefrom by said pressure reduction while essentially preventing foaming thereof.

Claim 16

A process as claimed in claim 14, in which the heating in step (21) is conducted under conditions of turbulent flow in each of steps (14) and (18).

Claim 17

A process as claimed in claim 1, in which in step (12) the avoidance of impact is effected by maintaining the dispersion in essentially linear non-turbulent flow until the vaporization of solvent from the dispersed droplets is essentially complete by the pressure reduction effected by said pressure gradient.

Claim 18

A process as claimed in claim 1 in which in step (12) (a) the dispersion is maintained in essentially linear flow through a path comprising a first extended portion of relatively large cross-section, and a second portion of relatively restricted cross-section downstream thereof restricting the pressure drop in said first section, and in which (b) substantially all of the vaporization of solvent from the dispersed droplets is effected in said first portion under the restricted pressure gradient so maintained.

Claim 19

An improved process as claimed in claim 1, in which in the practice of step (6) the emulsion formed in step (2) is admixed with latex which has been subjected to step (11), and in such admixture is dipersed into said flow of gas.

Claim 20

An improved process as claimed in claim 2, in which in the practice of step (6) the emulsion formed in step (2) is admixed with latex which has been subjected to step (14), and in such admixture is dispersed into said flow of gas.

Claim 21

An improved process as claimed in claim 8, in which in the practice of step (6) the emulsion formed in step (2) is admixed with latex which has been subjected to step (2), and in such admixture is dispersed into said flow of gas.

Claim 22

An improved process including the steps of claim 1, which further comrpises (13) conveying the combined latex withdrawn in step (11) to a point of delivery, and (14) treating at least a portion of the latex being conveyed in step (13) to reduce its viscosity.

Claim 23

An improved process as claimed in claim 21, wherein (15) in step (14) the latex is treated to increase its particle size.

Claim 24

An improved process as claimed in claim 22, wherein (16) in step (14) the latex is treated to reduce the quantity of emulsifier in its aqueous phase.

Claim 25

An improved process as claimed in claim 1, wherein (15) in step (14) the latex is treated to reduce the quantity of emulsifier in its aqueous phase.

Claim 26

An improved process as claimed in claim 24, wherein (16) in step (15) the latex is diluted to reduce its solids content and reconcentrated by centrifugation.

Claim 27

An improved process including the steps of claim 8, which further comprises (21) conveying the further concentrated latex withdrawn in step (20) to a point of delivery, and (22) treating at least a portion of the latex being conveyed in step (21) to reduce its viscosity.

Claim 28

An improved process as claimed in claim 24, wherein (23) in step (22) the latex is treated to increase its particle size.

Claim 29

An improved process as claimed in claim 27, wherein (24) in step (22) the latex is treated to reduce the quantity of emulsifier in its aqueous phase.

Claim 30

An improved process as claimed in claim 26, wherein (23) in step (22) the latex is treated to reduce the quantity of emulsifier in its aqueous phase.

Claim 31

An improved process as claimed in claim 29, wherein (24) in step (23) the latex is diluted to reduce its solids content and reconcentrated by centrifugation.

Claim 32

An improved process as claimed in claim 30, wherein (25) in step (24) the latex is diluted with latex withdrawn in step (11).

Claim 33

An improved process as claimed in claim 26, wherein (24) in step (22) the latex is first treated to increase its particle size, and subsequently treated to reduce the quantity of emulsifier in its aqueous phase.

Claim 34

In the formation of a latex from an organic solvent dispersion of a composition of an organic solvent soluble or dispersible polymer, by a process of the type which comprises: (1) providing a dispersion of the polymer composition in essentially water-immiscible volatile solvent which itself or as an azeotrope with water has a boiling point lower than that of water at atmospheric pressure, (2) adding water and emulsifier to said dispersion in proportions to form an emulsion having water as its continuum and emulsifying the same so that the discontinuous phase thereof is in particles at least principally of precursor latex particle size, (3) stripping the solvent from the emulsion to form a latex, and (4) recovering the latex product, and which comprises the particular steps of: (5) providing a moving flow of gas comprising steam as an initial continuous phase, (6) dispersing the said emulsion into the flow of steam as the initial continuous phase while subjecting the phases to a decrease of pressure and maintaining the temperature thereof below the limiting temperature for stability of the emulsion, thereby vaporizing solvent from the dispersed droplets and forming latex and vapor, (7) establishing a reduced pressure zone and maintaining the same at a pressure lower than that attained in step (6), (8) establishing a flow of latex through said reduced pressure zone, (9) introducing into said reduced pressure zone the latex droplets and vapor produced by step (6) and impinging said droplets upon the flow of latex therein, (10) withdrawing vapor from said reduced pressure zone, and (11) withdrawing the combined latices from said reduced pressure zone, the improvement which consists in the combination in the process of the further steps of: (12) delivering the latex withdrawn in step (11) to a circulation and passing said circulation of latex in contact with a surface heated in the range of 212° to 260° F. for a sufficient time to destabilize and coagulate from the latex particles of greater than colloidal size, wich may be present in said circulation, without substantially coagulating the latex particles of colloidal size, and (13) separating from the latex any coagulum formed.

Claim 35

In the formation of a latex from an organic solvent dispersion of a composition of an organic solvent soluble or dispersible polymer, by a process of the type which comprises: (1) providing a dispersion of the polymer composition in essentially water-immiscible volatile solvent which itself or as an azeotrope with water has a boiling point lower than that of water at atmospheric pressure, (2) adding water and emulsifier to said dispersion in proportions to form an emulsion having water as its continuum and emulsifying the same so that the discontinuous phase thereof is in particles at least principally of precursor latex particle size, (3) stripping the solvent from the emulsion to form a latex, and (4) recovering the latex product, and which comprises the particular steps of: (5) providing a moving flow of gas comprising steam as an initial continuous phase, (6) dispersing the said emulsion into the flow of steam as the initial continuous phase while subjecting the phases to a decrease of pressure and maintaining the temperature thereof below the limiting temperature for stability of the emulsion, thereby vaporizing solvent from the dispersed droplets and forming latex and vapor, (7) establishing a reduced pressure zone and maintaining the same at a pressure lower than that attained in step (6), (8) establishing a flow of latex through said reduced pressure zone, (9) introducing into said reduced pressure zone the latex droplets and vapor produced by step (6) and impinging said droplets upon the flow of latex therein, (10) withdrawing vapor from said reduced pressure zone, and (11) withdrawing the combined latices from said reduced pressure zone, the improvement which consists in the combination in the process of the further steps of: (12) delivering the latex withdrawn in step (11) to a circulation and passing said circulation of latex in contact with a surface heated in the range of 212° to 260° F. for a sufficient time to destabilize and coagulate from the latex particles of greater than colloidal size, wich may be present in said circulation, without substantially coagulating the latex particles of colloidal size, and (13) separating from the latex any coagulum formed.

Claim 36

A process as claimed in claim 33, in which: (14) in step (12) the circulation is established as a concentrating zone in which the latex which has been passed in contact with the heated surface is subjected to reduction of pressure thus producing concentrated latex and vapor therefrom.