Integrated Ag-SnO alloy electrical contact materials

Claim 1

An electrical contact material of comparatively large dimensions, formed from a plurality of generally similarly shaped pieces of silver-base alloy, which are of such dimensions that they are substantially smaller than the material having said large dimensions, and are such that said pieces are readily and completely internally oxidizable without depleted zones, each of said pieces of silver-base alloy, prior to being formed into said contact material, having silver grain matrices with metal oxides dispersedly precipitated therein, and said matrices being defined by metal oxides concentratedly precipitated along silver grain boundaries arranged generally in a tortoise-shell pattern as the result of internal oxidation for a comparatively short period of time, and comprising 1.5 to 10% by weight of tin, 0.5 to 6% by weight of indium, and a trace amount of less than 0.5% by weight of iron family element metals, and said pieces of the alloy being metallurgically integrated with each other by pressure rolling or extrusion conducted at a temperature higher than 700° C., and at about the melting point of silver, thereby to eliminate said grain boundaries in said pieces by causing precipitated metal oxides to migrate from said boundaries into said grain matrices, and to cause said matrices to coalesce to each other to form said contact material with said metal oxides being distributed uniformly throughout said material.

Claim 4

A method of making a Ag-SnO alloy electric contact material of comparatively large dimensions, which comprises providing a desired number of pieces of silver-base alloy of such dimensions that they are internally oxidizable within a comparatively short period of time, each of said pieces comprising 1.5 to 10% by weight of tin, 0.5 to 6% by weight of indium, and a trace amount of less than 0.5% by weight of nickel or cobalt, and internally oxidizing said pieces to form throughout each piece silver grain matrices defined by boundaries created by concentrations of precipitated metal oxides, and metallurgically integrating said pieces to each other by simultaneously subjecting them to extreme pressure at a temperature higher than 700° C. and sufficient to induce at least partially the melting of said pieces of said alloy without decomposing or breaking down the metal oxides precipitated in said pieces, thereby to eliminate the concentrations of said metal oxides around the silver grain matrices in said metallurgically integrated pieces, and to disperse the formerly concentrated metal oxides uniformly throughout the silver matrices of the integrated pieces.

Claim 5

A method of making a Ag-SnO alloy electric contact material of comparatively large dimensions, which comprises providing a desired number of pieces of silver-base alloy of such dimensions that they are internally oxidizable within a comparatively short period of time, each of said pieces comprising 1.5 to 10% by weight of tin, 0.5 to 6% by weight of indium, and a trace amount of less than 0.5% by weight of nickel or cobalt, and internally oxidizing said pieces to form throughout each piece silver grain matrices defined by boundaries created by concentrations of precipitated metal oxides, and metallurgically integrating said pieces to each other by simultaneously subjecting them to extreme pressure at a temperature higher than 700° C. and sufficient to induce at least partially the melting of said pieces of said alloy without decomposing or breaking down the metal oxides precipitated in said pieces, thereby to eliminate the concentrations of said metal oxides around the silver grain matrices in said metallurgically integrated pieces, and to disperse the formerly concentrated metal oxides uniformly throughout the silver matrices of the integrated pieces.

Claim 7

The method of making an electrical contact comprising forming a plurality of pieces of an alloy containing 1.5-10% by weight of tin, 0.5-6% by weight of indium, and a trace amount of less than 0.5% by weight of nickel or cobalt, subjecting said pieces to a heat treatment for a brief interval of time to effect substantially complete internal oxidation thereof and consequent precipitation of metal oxides in silver grain matrices in said pieces, at least certain of said precipitated metal oxides being concentrated along silver grain boundaries which border said matrices in each of said pieces, and thereafter metallurgically integrating said internally oxidized pieces, under pressure and a temperature in excess of 700° C., into the configuration of the desired electrical contact without decomposing the metal oxides precipitated in said pieces, and by causing the metal oxides to migrate from the concentrated areas thereof evenly and freely into the integrated silver matrices of the pieces and thus to eliminate the silver grain boundaries in said metallurgically integrated pieces.

Claim 8

The method of making an electrical contact comprising forming a plurality of pieces of an alloy containing 1.5-10% by weight of tin, 0.5-6% by weight of indium, and a trace amount of less than 0.5% by weight of nickel or cobalt, subjecting said pieces to a heat treatment for a brief interval of time to effect substantially complete internal oxidation thereof and consequent precipitation of metal oxides in silver grain matrices in said pieces, at least certain of said precipitated metal oxides being concentrated along silver grain boundaries which border said matrices in each of said pieces, and thereafter metallurgically integrating said internally oxidized pieces, under pressure and a temperature in excess of 700° C., into the configuration of the desired electrical contact without decomposing the metal oxides precipitated in said pieces, and by causing the metal oxides to migrate from the concentrated areas thereof evenly and freely into the integrated silver matrices of the pieces and thus to eliminate the silver grain boundaries in said metallurgically integrated pieces.