Easily disposable non-woven products having high wet strength at acid pH and low wet strength at base pH
Assignee: Dow Chemical Co
•
Filing: 1979-06-25
•
Granted: 1980-12-30
•
Expires: 1999-06-25
Abstract
Abstract A non-woven flexible web having enhanced wet strength and easy disposability is prepared by adhering the fibrous elements of the web with a polymer of an unsaturated acid and an unsaturated water-insoluble monomer in a ratio wherein the polymer is insoluble at lower pH values and soluble at higher pH values.
Inventors
- 👤 Syamalarao Evani
- 👤 William A. Foster
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 12:57
CPC Classifications
A; A47; A47K; A47K10/00; A47K10/16; D; D06; D06M; D06M15/00; D06M15/19; D06M15/21; D06M15/263; D21; D21H; D21H17/00; D21H17/20; D21H17/33; D21H17/34; D21H17/41; D21H17/42; D21H17/43; Y; Y10; Y10S; Y10S428/00; Y10S428/913; Y10T; Y10T428/00; Y10T428/31504; Y10T428/31725; Y10T428/31739; Y10T428/31743; Y10T428/3175; Y10T428/31786; Y10T428/31797; Y10T428/31855; Y10T428/3188; Y10T428/31895; Y10T428/31906; Y10T428/31909; Y10T428/31928; Y10T442/00; Y10T442/20; Y10T442/2484; Y10T442/2492
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
86 words
A non-woven flexible web having enhanced wet strength and easy disposability, said web comprising a mat of non-woven fibers impregnated with the acid form of a terpolymer formed by the reaction of an unsaturated monomer controlling the hydrophobicity of the terpolymer an unsaturated carboxylic acid and an alkyl capped polyoxyethylene moiety having an ethylenically unsaturated terminal group and at least about 10 oxyethylene units, the monomers having been reacted in a ratio that said polymer is insoluble below pH 6 and soluble at higher pH values.
Claim 2
Dependent Claim
86 words
A non-woven flexible web having enhanced wet strength and easy disposability, said web comprising a mat of non-woven fibers impregnated with the acid form of a terpolymer formed by the reaction of an unsaturated monomer controlling the hydrophobicity of the terpolymer an unsaturated carboxylic acid and an alkyl capped polyoxyethylene moiety having an ethylenically unsaturated terminal group and at least about 10 oxyethylene units, the monomers having been reacted in a ratio that said polymer is insoluble below pH 6 and soluble at higher pH values.
Claim 3
Dependent Claim
10 words
The web of claim 1 wherein said fibers are cellulosic.
Claim 4
Dependent Claim
10 words
The web of claim 2 wherein said mat is paper.
Claim 5
Dependent Claim
28 words
The web of claim 1 wherein said polymer is present in an amount of from about 1.5 to about 5 weight percent of the weight of said fibers.
Claim 6
Independent Claim
108 words
A method for treating a non-woven flexible web to enhance its wet strength and disposability wherein said web (1) while in a swollen state is impregnated with an ammonium hydroxide solution or dispersion of a linear terpolymer formed by the reaction of an unsaturated monomer controlling the hydrophobicity of the terpolymer, an ethylenically unsaturated carboxylic acid, and an alkyl capped polyoxyethylene moiety having an ethylenically unsaturated terminal group and at least about 10 oxyethylene units, the monomers being in a ratio that said polymer is water insoluble below pH 6 and soluble above pH 6, (2) is dried and (3) said polymer is converted to its acid form.
Claim 7
Independent Claim
108 words
A method for treating a non-woven flexible web to enhance its wet strength and disposability wherein said web (1) while in a swollen state is impregnated with an ammonium hydroxide solution or dispersion of a linear terpolymer formed by the reaction of an unsaturated monomer controlling the hydrophobicity of the terpolymer, an ethylenically unsaturated carboxylic acid, and an alkyl capped polyoxyethylene moiety having an ethylenically unsaturated terminal group and at least about 10 oxyethylene units, the monomers being in a ratio that said polymer is water insoluble below pH 6 and soluble above pH 6, (2) is dried and (3) said polymer is converted to its acid form.
Claim 8
Dependent Claim
49 words
The method claimed in claim 5 wherein said web is impregnated with an ammonium hydroxide solution of said polymer, the impregnated web dried and subsequently treated with an aqueous solution of an acid stronger than the carboxylic acid of said polymer to generate the acid form of said polymer.
Claim 9
Dependent Claim
18 words
The method claimed in claim 6 wherein the treated web is dried prior to exposure to the acid.
Claim 10
Dependent Claim
29 words
The method claimed in claim 5 wherein said polymer is a terpolymer of styrene, maleic anhydride and a vinylbenzyl ether of an alkylene oxide adduct of an alkyl phenol.
Claim 11
Dependent Claim
29 words
The method claimed in claim 8 wherein said terpolymer is composed of styrene, maleic anhydride and a vinylbenzyl ether of a forty mole ethylene oxide adduct of nonyl phenol.
References Cited (Backward Citations)
US4035540A
Cited
US4117187A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-12-30 | 1984-06-30 | 1984-12-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-12-30 | 1988-06-30 | 1988-12-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-12-30 | 1992-06-30 | 1992-12-30 | $7700.00 | Window Closed / Lapsed |