Method of providing a polycarbonate article with a uniform and durable organopolysiloxane coating
Assignee: General Electric Co
•
Filing: 1979-04-18
•
Granted: 1980-12-30
•
Expires: 1999-04-18
Abstract
Abstract A process for providing a protective coating on a polycarbonate substrate comprising (i) applying onto said polycarbonate substrate a priming emulsion composition containing (a) a thermosettable acrylic polymer, (b) an ultraviolet light absorber selected from the benzylidene malonates and cyanoacrylates, (c) water, and (d) a hydroxy ether or a lower alkanol; (ii) curing the thermosettable acrylic polymer thereby forming a primer layer containing a thermoset acrylic and an ultraviolet light screener on said substrate; (iii) applying a top coat composition containing a further curable organopolysiloxane; and (iv) curing said further curable organopolysiloxane thereby obtaining a thermoset organopolysiloxane top coat.
Inventors
- 👤 John C. Goossens
- 👤 Daniel R. Olson
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 05:27
CPC Classifications
C; C08; C08J; C08J7/00; C08J7/04; C08J7/042; C08J7/043; C08J7/046; C08J2369/00; C08J2433/00; C08J2433/04; C08J2433/06; C08J2433/08; Y; Y10; Y10T; Y10T428/00; Y10T428/31504; Y10T428/31507; Y10T428/31652; Y10T428/31663
Claims Analysis
Total Claims: 30
Claim 1
Independent Claim
213 words
A method for producing a polycarbonate article having improved mar, abrasion, scratch and chemical solvent resistance and possessing enhanced ultraviolet light stability comprising: (i) applying onto a polycarbonate substrate a primer emulsion composition consisting essentially of (a) a thermosettable acrylic polymer, (b) at least one ultraviolet light screening compound selected from the class consisting of benzylidene malonates and cyanoacrylates, (c) from about 20 to about 40 weight percent of a hydroxy ether or an alkanol containing from 1 to 4 carbon atoms, and (d) water; (ii) evaporating off a substantial portion of said hydroxy ether or alkanol from said primer emulsion composition thereby forming a layer comprised of said thermosettable acrylic polymer and at least one of said ultraviolet light screening compounds; (iii) applying heat to said layer at a temperature and for a period of time effective to cure said thermosettable acrylic polymer; (iv) applying onto said cured primer layer a further-curable organopolysiloxane top coat composition containing the partial hydrolysis and condensation product of an alkyltrialkoxy silane; (v) evaporating off a substantial portion of the volatile solvents from said top coat composition thereby forming a layer comprised of the partial hydrolysis and condensation product of said alkyltrialkoxy silane; and, (vi) thermally curing said partial hydrolysis and condensation product of said alkyltrialkoxy silane.
Claim 2
Independent Claim
213 words
A method for producing a polycarbonate article having improved mar, abrasion, scratch and chemical solvent resistance and possessing enhanced ultraviolet light stability comprising: (i) applying onto a polycarbonate substrate a primer emulsion composition consisting essentially of (a) a thermosettable acrylic polymer, (b) at least one ultraviolet light screening compound selected from the class consisting of benzylidene malonates and cyanoacrylates, (c) from about 20 to about 40 weight percent of a hydroxy ether or an alkanol containing from 1 to 4 carbon atoms, and (d) water; (ii) evaporating off a substantial portion of said hydroxy ether or alkanol from said primer emulsion composition thereby forming a layer comprised of said thermosettable acrylic polymer and at least one of said ultraviolet light screening compounds; (iii) applying heat to said layer at a temperature and for a period of time effective to cure said thermosettable acrylic polymer; (iv) applying onto said cured primer layer a further-curable organopolysiloxane top coat composition containing the partial hydrolysis and condensation product of an alkyltrialkoxy silane; (v) evaporating off a substantial portion of the volatile solvents from said top coat composition thereby forming a layer comprised of the partial hydrolysis and condensation product of said alkyltrialkoxy silane; and, (vi) thermally curing said partial hydrolysis and condensation product of said alkyltrialkoxy silane.
Claim 3
Dependent Claim
73 words
The method of claim 1 wherein said hydroxy ether is represented by the general formula R.sup.1 --O--R.sup.2 --OH wherein R 1 is an alkyl or an alkoxy alkyl radical containing from 1 to about 6 carbon atoms, and R 2 is an alkylidene radical containing from 1 to about 6 carbon atoms, provided that the sum of the carbon atoms present in R 1 and R 2 is from 3 to about 10.
Claim 4
Dependent Claim
12 words
The method of claim 2 wherein said hydroxy ether is butoxy ethanol.
Claim 5
Dependent Claim
21 words
The method of claim 1 wherein said cured primer layer has a thickness of from about 0.01 to about 0.1 mil.
Claim 6
Dependent Claim
55 words
The method of claim 1 wherein said benzylidene malonates are represented by the general formula ##STR5## wherein X is selected from hydrogen, OH, halogen radicals, alkyl radicals, and alkoxy radicals; and R 3 and R 4 are independently selected from alkyl radicals, substituted alkyl radicals, aryl radicals, substituted aryl radicals, alkaryl radicals, and aralkyl radicals.
Claim 7
Dependent Claim
23 words
The method of claim 5 wherein X is an alkoxy radical and R 3 and R 4 are independently selected from alkyl radicals.
Claim 8
Dependent Claim
11 words
The method of claim 6 wherein X is a methoxy radical.
Claim 9
Dependent Claim
14 words
The method of claim 7 wherein said methoxy radical is in the para position.
Claim 10
Dependent Claim
15 words
The method of claim 8 wherein R 3 and R 4 are both ethyl radicals.
Claim 11
Dependent Claim
15 words
The method of claim 8 wherein R 3 and R 4 are both methyl radicals.
Claim 12
Dependent Claim
36 words
The method of claim 1 wherein said cyanoacrylates are represented by the general formula ##STR6## wherein R 5 is selected from alkyl radicals, substituted alkyl radicals, aryl radicals, substituted aryl radicals, alkaryl radicals and aralkyl radicals.
Claim 13
Dependent Claim
12 words
The method of claim 11 wherein R 5 is an alkyl radical.
Claim 14
Dependent Claim
11 words
The method of claim 12 wherein said alkyl radical is octyl.
Claim 15
Dependent Claim
11 words
The method of claim 12 wherein said alkyl radical is ethyl.
Claim 16
Independent Claim
244 words
A method for providing a uniform and durably adhered mar, scratch, abrasion and chemical solvent resistant organopolysiloxane coating on a polycarbonate article which comprises: (i) applying onto the surface of a polycarbonate substrate a primer emulsion composition consisting essentially of, in percent by weight, (a) from about 1 to about 10 percent of a thermosettable acrylic polymer, (b) from about 1 to about 10 percent of at least one ultraviolet light screening compound selected from the class consisting of benzylidene malonates and cyanoacrylates, (c) from about 20 to about 40 percent of a hydroxy ether or an alkanol containing from 1 to 4 carbon atoms, and (d) from about 40 to about 78 percent water; (ii) evaporating off a substantial portion of said hydroxy ether or alkanol from said primer emulsion composition thereby forming a layer comprised of said thermosettable acrylic polymer and at least one of said ultraviolet light screening compounds; (iii) applying heat to said layer at a temperature and for a period of time effective to cure said thermosettable acrylic polymer; (iv) applying onto said cured primer layer a further-curable organopolysiloxane top coat composition comprised of the partial hydrolysis and condensation product of an alkyltrialkoxy silane; (v) evaporating off a substantial portion of the volatile solvents from said top coat composition thereby forming a layer comprised of the partial hydrolysis and condensation product of said alkyltrialkoxy silane; and, (vi) thermally curing said partial hydrolysis and condensation product of said alkyltrialkoxy silane.
Claim 17
Independent Claim
244 words
A method for providing a uniform and durably adhered mar, scratch, abrasion and chemical solvent resistant organopolysiloxane coating on a polycarbonate article which comprises: (i) applying onto the surface of a polycarbonate substrate a primer emulsion composition consisting essentially of, in percent by weight, (a) from about 1 to about 10 percent of a thermosettable acrylic polymer, (b) from about 1 to about 10 percent of at least one ultraviolet light screening compound selected from the class consisting of benzylidene malonates and cyanoacrylates, (c) from about 20 to about 40 percent of a hydroxy ether or an alkanol containing from 1 to 4 carbon atoms, and (d) from about 40 to about 78 percent water; (ii) evaporating off a substantial portion of said hydroxy ether or alkanol from said primer emulsion composition thereby forming a layer comprised of said thermosettable acrylic polymer and at least one of said ultraviolet light screening compounds; (iii) applying heat to said layer at a temperature and for a period of time effective to cure said thermosettable acrylic polymer; (iv) applying onto said cured primer layer a further-curable organopolysiloxane top coat composition comprised of the partial hydrolysis and condensation product of an alkyltrialkoxy silane; (v) evaporating off a substantial portion of the volatile solvents from said top coat composition thereby forming a layer comprised of the partial hydrolysis and condensation product of said alkyltrialkoxy silane; and, (vi) thermally curing said partial hydrolysis and condensation product of said alkyltrialkoxy silane.
Claim 18
Dependent Claim
73 words
The method of claim 15 wherein said hydroxy ether is represented by the general formula R.sup.1 --O--R.sup.2 --OH wherein R 1 is an alkyl or an alkoxy alkyl radical containing from 1 to about 6 carbon atoms, and R 2 is an alkylidene radical containing from 1 to about 6 carbon atoms, provided that the sum of the carbon atoms present in R 1 and R 2 is from 3 to about 10.
Claim 19
Dependent Claim
12 words
The method of claim 16 wherein said hydroxy ether is butoxy ethanol.
Claim 20
Dependent Claim
21 words
The method of claim 15 wherein said cured primer layer has a thickness of from about 0.01 to about 0.1 mil.
Claim 21
Dependent Claim
55 words
The method of claim 15 wherein said benzylidene malonates are represented by the general formula ##STR7## wherein X is selected from hydrogen, OH, halogen radicals, alkyl radicals, and alkoxy radicals, and R 3 and R 4 are independently selected from alkyl radicals, substituted alkyl radicals, aryl radicals, substituted aryl radicals, alkaryl radicals, and aralkyl radicals.
Claim 22
Dependent Claim
23 words
The method of claim 19 wherein X is an alkoxy radical and R 3 and R 4 are independently selected from alkyl radicals.
Claim 23
Dependent Claim
11 words
The method of claim 20 wherein X is a methoxy radical.
Claim 24
Dependent Claim
14 words
The method of claim 21 wherein said methoxy radical is in the para position.
Claim 25
Dependent Claim
15 words
The method of claim 22 wherein R 3 and R 4 are both ethyl radicals.
Claim 26
Dependent Claim
15 words
The method of claim 22 wherein R 3 and R 4 are both methyl radicals.
Claim 27
Dependent Claim
36 words
The method of claim 15 wherein said cyanoacrylates are represented by the general formula ##STR8## wherein R 5 is selected from alkyl radicals, substituted alkyl radicals, aryl radicals, substituted aryl radicals, alkaryl radicals and aralkyl radicals.
Claim 28
Dependent Claim
12 words
The method of claim 25 wherein R 5 is an alkyl radical.
Claim 29
Dependent Claim
11 words
The method of claim 26 wherein said alkyl radical is octyl.
Claim 30
Dependent Claim
11 words
The method of claim 26 wherein said alkyl radical is ethyl.
References Cited (Backward Citations)
US3582398A
Cited
US3650808A
Cited
US4041120A
Cited
US3707397A
Cited
US3843390A
Cited
US4024306A
Cited
US3978178A
Cited
US3986997A
Cited
US4027073A
Cited
US4045602A
Cited
US4040882A
Cited
US4156046A
Cited
US4135007A
Cited
US4188451A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-12-30 | 1984-06-30 | 1984-12-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-12-30 | 1988-06-30 | 1988-12-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-12-30 | 1992-06-30 | 1992-12-30 | $7700.00 | Window Closed / Lapsed |