US4241191A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Manufacture of styrene suspension polymers
Assignee: BASF SE
•
Filing: 1978-11-24
•
Granted: 1980-12-23
•
Expires: 1998-11-24
Abstract
Abstract Styrene polymers are prepared by suspension polymerization using, as suspension stabilizers, mixtures of (A) a sparingly soluble inorganic metal compound and (B) a fine polymer dispersion. The styrene polymers may be used, together with blowing agents, for the manufacture of foams.
Inventors
- 👤 Hans G. Keppler
- 👤 Erhard Stahnecker
- 👤 Rolf Moeller
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 10:07
CPC Classifications
C; C08; C08F; C08F12/00; C08F12/02; C08F12/04; C08F12/06; C08F12/08; Y; Y10; Y10S; Y10S526/00; Y10S526/91
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
196 words
A process for the manufacture of expandable beads of styrene polymer, consisting essentially of polymerizing styrene in aqueous suspension in the presence of a suspension stabilizer, wherein said suspension stabilizer is used in the amount of from 0.05 to 1% by weight, based on the suspension, said stabilizer being made up of: (A) from 99 to 50% by weight of particles having a particle size of from 0.01 to 100 μm of a sparingly water-soluble phosphate of a divalent or trivalent metal and (B) from 1 to 50% by weight of a finely-divided preformed water-insoluble polymer of (i) from 100 to 90 parts by weight of one or more of the monomers which form water-insoluble homopolymers selected from the group consisting of styrene, butadiene, vinyl chloride, vinylidene chloride, a vinyl ester or an acrylic or methacrylic ester and (ii) from 0 to 10 parts by weight of one or more monomers which form water-soluble homopolymers, said preformed polymer being employed in the form of an aqueous dispersion having particle sizes up to 10 μm; said process further including the addition of a blowing agent to the suspension before, during or after the polymerization of the styrene.
Claim 2
Dependent Claim
196 words
A process for the manufacture of expandable beads of styrene polymer, consisting essentially of polymerizing styrene in aqueous suspension in the presence of a suspension stabilizer, wherein said suspension stabilizer is used in the amount of from 0.05 to 1% by weight, based on the suspension, said stabilizer being made up of: (A) from 99 to 50% by weight of particles having a particle size of from 0.01 to 100 μm of a sparingly water-soluble phosphate of a divalent or trivalent metal and (B) from 1 to 50% by weight of a finely-divided preformed water-insoluble polymer of (i) from 100 to 90 parts by weight of one or more of the monomers which form water-insoluble homopolymers selected from the group consisting of styrene, butadiene, vinyl chloride, vinylidene chloride, a vinyl ester or an acrylic or methacrylic ester and (ii) from 0 to 10 parts by weight of one or more monomers which form water-soluble homopolymers, said preformed polymer being employed in the form of an aqueous dispersion having particle sizes up to 10 μm; said process further including the addition of a blowing agent to the suspension before, during or after the polymerization of the styrene.
Claim 3
Dependent Claim
43 words
The process of claim 1, wherein the sparingly soluble inorganic metal compound A is introduced into the aqueous phase of the suspension before starting the polymerization and the finely divided polymer B is metered into the suspension in the course of the polymerization.
Claim 4
Dependent Claim
23 words
The process of claim 1, wherein the finely divided polymer B is metered in when the monomer conversion is from 5 to 40%.
Claim 5
Dependent Claim
28 words
The process of claim 1, wherein the metal compound A and the polymer B are premixed and are metered conjointly into the suspension before or during the polymerization.
Claim 6
Dependent Claim
27 words
The process of claim 1, wherein the mixture of the suspension stabilizers A and B is metered in when the monomer conversion is from 5 to 40%.
Claim 7
Dependent Claim
18 words
The process of claim 1, wherein a mixture of different sparingly soluble inorganic metal compounds A is employed.
Claim 8
Dependent Claim
17 words
The process of claim 1, wherein the sparingly soluble inorganic metal compound A comprises a calcium phosphate.
Claim 9
Dependent Claim
17 words
The process of claim 1, wherein a polystyrene dispersion is used as the finely divided polymer B.
Claim 10
Dependent Claim
54 words
The process of claim 1, wherein said vinyl ester is a vinyl ester of a saturated monocarboxylic acid having 2 to 12 carbon atoms, and said ester of acrylic acid or methacrylic acid is an ester thereof with a straight chain, a branced chain or a cyclic alkanol having 1 to 18 carbon atoms.
Claim 11
Dependent Claim
29 words
The process of claim 1, wherein the monomers which form water-soluble homopolymers are α,β-olefinically unsaturated monocarboxylic or dicarboxylic acids having 3 to 5 carbon atoms, or the amides thereof.
Claim 12
Dependent Claim
29 words
The process of claim 1, wherein said particles are undissolved particles of a sparingly water-soluble inorganic metal carbonate, phosphate, silicate, oxide or hydroxide of a divalent or trivalent metal.
Claim 13
Dependent Claim
19 words
The process of claim 1, wherein the metals are calcium, barium, strontium, magnesium, aluminum, zinc, iron, cobalt and manganese.
Claim 14
Dependent Claim
19 words
The process of claim 1, wherein the polymerization is carried out at a temperature of 80° to 120° C.
References Cited (Backward Citations)
US2888410A
Cited
US3001954A
Cited
US3047534A
Cited
US3243419A
Cited
US3468820A
Cited
US3462380A
Cited
US3696172A
Cited
US3758425A
Cited
US3786115A
Cited
US3912794A
Cited
US3919355A
Cited
US4110413A
Cited
US4036794A
Cited
US4141932A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-12-23 | 1984-06-23 | 1984-12-23 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-12-23 | 1988-06-23 | 1988-12-23 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-12-23 | 1992-06-23 | 1992-12-23 | $7700.00 | Window Closed / Lapsed |